Abstract
The silica fiber reinforced silica and boron nitride-based composites (SiO2f/SiO2-BN) were prepared firstly via the sol-gel method and then the urea route, and the effects of oxidation treatment on the component, structure, mechanical and dielectric properties of the composites were investigated. The results show that the oxidation treatment at 450 °C will not impair the structure of boron nitride, and carbon is the main impurity with the excessive urea. The density of SiO2f/SiO2-BN composites is 1.81 g/cm3, and the flexural strength and elastic modulus are 113.9 MPa and 36.5 GPa, respectively. After oxidation treatment, the density varies to 1.80 g/cm3, and the flexural strength and elastic modulus are decreased to 58.9 MPa and 9.4 GPa, respectively. The mechanical properties of the composites are severely damaged, but they still exhibit a good toughness. The composites show excellent dielectric properties with the dielectric constant and loss tangent being 3.22 and 0.003 9, respectively, which indicates that the oxidation treatment is ineffective to improve the dielectric properties of SiO2f/SiO2-BN composites.
Similar content being viewed by others
References
NEIL J T, BOWEN L J, MICHAUD B E. Fused silica radome: US, 4949095 [P]. 1990-08-14.
QI Gong-jin, ZHANG Chang-rui, HU Hai-feng. High strength three-dimensional silica fiber reinforced silicon nitride-based composites via polyhydridomethylsilazane pyrolysis [J]. Ceram Int, 2007, 33: 891–894.
BRAZEL J P, FENTON R. ADL-4D6: A silica/silica composite for hardened antenna windows [C]// Proceedings of the 13th symposium on electromagnetic windows. Atlanta, Georgia: Georgia Institute of Technology, 1976: 9–16.
MANOCHA L M, PANCHAL C N, MANOCHA S. Silica/silica composites through electrophoretic infiltration [J]. Ceram Eng Sci Proc, 2002, 23: 655–661.
LI Xiang-ming, YIN Xiao-wei, ZHANG Li-tong, CHENG Lai-fei, QI Yuan-chen. Mechanical and dielectric properties of porous Si3N4-SiO2 composite ceramics [J]. Mater Sci Eng A, 2009, 500: 63–69.
LI Bin, ZHANG Chang-rui, CAO Feng, WANG Si-qing, CAO Ying-bin, QI Gong-jin, JIANG Yong-gang. Effect of pyrolysis temperature on the properties of three-dimensional silica fiber reinforced nitride matrix composites [J]. J Mater Eng Perform, 2008, 17(1): 111–114.
LI Bin, ZHANG Chang-rui, CAO Feng, WANG Si-qing, LI Jun-sheng, CHEN Bang. Effects of curing atmospheric pressure on properties of silica fiber reinforced silicon-boron nitride matrix composites derived from precursor infiltration and pyrolysis [J]. Mater Technol, 2007, 22 (2): 81–84.
ECONOMY J, JUN C K, LIN R Y. Boron nitride-boron nitride composites: US, 4075276 [P]. 1978-02-21.
YUAN Bo, LIU Ji-xuan, ZHANG Guo-jun, KAN Yan-mei, WANG Pei-ling. Silicon nitride/boron nitride ceramic composites fabricated by reactive pressureless sintering [J]. Ceram Int, 2009, 35: 2155–2159.
LII Ding-fwu, HUANG Jow-lay, TSUI Li-jen, LEE Shaw-min. Formation of BN films on carbon fibers by dip-coating [J]. Surf Coat Technol, 2002, 150: 269–276.
GOMATHI A, RESHMA S, RAO C N R. A simple urea-based route to ternary metal oxynitride nanoparticles [J]. J Solid State Chem, 2009, 182: 72–76.
GOMATHI A, RAO C N R. Nanostructures of the binary nitrides, BN, TiN, and NbN prepared by the urea-route [J]. Mater Res Bull, 2006, 41: 941–947.
SUN J F, WANG M Z, ZhAO Y C, LI X P, LIANG B Y. Synthesis of titanium nitride powders by reactive ball milling of titanium and urea [J]. J Alloy Compd, 2009, 482: L29–L31.
WANG Xiang-dong, QIAO Guan-jun, JIN Zhi-hao. Preparation of SiC/BN nanocomposite powders by chemical processing [J]. Mater Lett, 2004, 58: 1419–1423.
LI Yong-li, ZHANG Jiu-xing, QIAO Guan-jun, JIN Zhi-hao. Fabrication and properties of machinable 3Y-ZrO2/BN nanocomposites [J]. Mater Sci Eng A, 2005, 397: 35–40.
LI Duan, ZHANG Chang-rui, LI Bin, CAO Feng, WANG Si-qing, CAO Ying-bin. Preparation and properties of SiO2f/SiO2-BN composites [J]. Acta Materiae Compositae Sinica, 2011, 28(3): 63–68. (in Chinese)
COFER C G, ECONOMY J, XU Y R, ZANGVIL A, CURZIO E L, FERBER M K, MORE K L. Characterization of fiber/matrix interfaces in composites with a boron nitride matrix [J]. Compos Sci Technol, 1996, 56: 967–975.
ZALDIVAR R J, RELLICK G S, YANG J M. Fiber strength utilization in carbon/carbon composites [J]. J Mater Res, 1993, 8: 501–511.
LI Shu-qin, PEI Yu-chen, YU Chang-qing, LI Jia-lu. Mechanical and dielectric properties of porous Si2N2O-Si3N4 in situ composites [J]. Ceram Int, 2009, 35: 1851–1854.
PAQUETTE D G. Method of making a radar transparent window material operable above 2000 °C: US, 5627542 [P]. 1997-05-06.
KINGERY W D, BOWEN H K, UHLMANN D R. Introduction to ceramics [M]. 2nd edition, New York: John Wiley & Sons, 1976.
LI Bin, ZHANG Chang-rui, WANG Si-qing, CAO Feng. Crystallization behaviors of carbon fiber reinforced BN-Si3N4 matrix composite [J]. Cryst Res Technol, 2007, 42(7): 648–651.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation item: Projects(50902150, 90916019) supported by the National Natural Science Foundation of China; Project (9140C8203040905) supported by the State Key Laboratory Foundation of China; Project(S100103) supported by the Graduate Innovation Foundation of National University of Defense Technology, China
Rights and permissions
About this article
Cite this article
Li, D., Zhang, Cr., Li, B. et al. Effects of oxidation treatment on properties of SiO2f/SiO2-BN composites. J. Cent. South Univ. Technol. 19, 30–35 (2012). https://doi.org/10.1007/s11771-012-0968-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-012-0968-7