Abstract
The cerium conversion film was applied to improving the corrosion resistance of Mg-Gd-Y-Zr magnesium alloy. The film was electrodeposited on the surface of the Mg-RE alloy in cerium nitrate solution. The compositions and morphologies were analyzed by X-ray diffraction(XRD), scanning election microscopy (SEM). The corrosion behaviors of the film were investigated electrochemical impedance spectroscopy (EIS), potentiodynamic polarization tests and immersion tests. The results show that the optimum parameters for electrochemical deposition are as follows: pH 10.0, time 30 min, 50 mmol/L Na2CO3 and temperature 25 °C by the designed experiments according to the orthogonal table L(9, 34). The corrosion protection efficiency is dependent on the deposition parameters. The cerium conversion film shows better corrosion protection behavior than chromate conversion film on Mg-Gd-Y-Zr magnesium alloy.
Similar content being viewed by others
References
WINSTON REVIE R, UHLIG H H. Corrosion and corrosion controll [M]. 4th ed. Hoboken: John Wiley & Sons Inc, 2008: 399.
XIAO Yang, ZHANG Xin-ming, CHEN Jian-mei, JIANG Hao. Microstructures and mechanical properties of Mg-15Gd-0.6Zr alloy [J]. The Chinese Journal of Nonferrous Metals, 2006, 16(4): 709–714. (in Chinese)
BEN-HAMU G, ELIEZER D, SHIN K S, COHEN S. The relation between microstructure and corrosion behavior of Mg-Y-RE-Zr alloys [J]. Alloys and Compounds, 2007, 431: 269–276.
GAO Yan, WANG Qu-dong, GU Jin-hai, ZHAO Yang, TONG Yan. Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540 °C [J]. Materials Science and Engineering A, 2007, A459: 117–123.
PINC W, GENG S, O’KEEFE M, FAHRENHOLTZ W, O’KEEFE T. Effects of acid and alkaline based surface preparation on spray deposited cerium based conversion coatings on Al2024-T3[J]. Applied Surface Science, 2009, 255: 4061–4065.
ZHAO M, WU S S, AN P, FUKUDA Y, NAKAE H. Growth of multi-elements complex coatings on AZ91D magnesium alloy through conversion treatment [J]. Alloys and Compounds, 2007, 427:310–315.
RUDD A L, BRESLIN C B, MANSFELD F. The corrosion protection afforded by rare earth conversion coatings applied to magnesium [J]. Corrosion Science, 2000, 42: 275–288.
DABALA M, BRUNELLI K, ENRICO N, MAURIZIO M. Cerium chemical conversion coatings on AZ63 magnesium alloy [J]. Surface Coating Technology, 2003, 172: 227–232.
YI Jian-long, ZHANG Xin-ming, CHEN Ming-an, GU Rui. Effect of Na2CO3 on corrosion resistance of cerium conversion film on Mg-Gd-Y-Zr magnesium alloys [J]. Scripta Materialia, 2008, 59: 955–958.
BONORA P L, ANDREI M, ELIEZER A, GUTMAN E M. Corrosion behaviour of stressed magnesium alloys [J]. Corrosion Science, 2002, 44: 729–749.
XUAN Lin, OKEEFE T J, STOFFER J O. An environmentally compliant cerium conversion coating for aluminum protection [D]. Rolla: University of Missouri-Rolla, 1998.
SONG G, ATRENS A, STJOHN D, NAIRN J, LI Y. The electrochemical corrosion of pure magnesium in 1 N NaCl [J]. Corrosion Science, 1997, 39(5): 855–875.
MONTEMOR M F, SIMOES A M, CARME M J. Characterization of rare-earth conversion film formed on the AZ31 magnesium alloy and its relation with corrosion protection [J]. Applied Surface Science, 2007, 253: 6922–6931.
ARDELEAN H, FIAUD C, MARCUS P. Enhanced corrosion resistance of magnesium and its alloys through the formation of cerium (and aluminium) oxide surface film [J]. Materials and Corrosion, 2001, 52: 889–895.
BRUNELLI K, DABALA M, CALLIARI I, MAGRINI M. Effect of HCl pre-treatment on corrosion resistance of cerium-based conversion coatings on magnesium and magnesium alloys [J]. Corrosion Science, 2005, 47: 989–1000.
Author information
Authors and Affiliations
Corresponding author
Additional information
Foundation item: Project (5133001E) supported by the Major State Basic Research and Development Program of China
Rights and permissions
About this article
Cite this article
Yi, Jl., Zhang, Xm., Chen, Ma. et al. Corrosion resistance of cerium conversion film electrodeposited on Mg-Gd-Y-Zr magnesium alloy. J. Cent. South Univ. Technol. 16, 38–42 (2009). https://doi.org/10.1007/s11771-009-0006-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11771-009-0006-6