Abstract
For the process of dressing vitrified bonded grinding wheels with diamond tools it has been unknown how the wheel topography is generated. Moreover, the influence of the kinematical dressing parameters on the wheel wear behavior has not been quantified. In the course of this article the grinding wheel was dealt with as a porous ceramic composite. In FEM simulations common dressing forces and usual dressing tool geometries were applied. The results were verified by dressing tests and grinding wheel scratch tests which show the wheel wear mechanisms. The common practice of decreasing the grinding wheel surface roughness by a finishing dressing stroke has to be reconsidered, because previous dressing strokes with higher depths of cut can weaken the grinding wheel structure and lead to an unsteady phase with high grinding wheel wear after dressing.
Similar content being viewed by others
References
Marinescu ID, Rowe WB, Dimitrov B, Inasaki I (2004) Tribology of abrasive machining processes. William Andrew, ISBN 0-8155-1490-5
Wimmer J (1995) Konditionieren hochharter Schleifscheiben zum Schleifen von Hochleistungskeramik. Doctoral thesis, University of Kaiserslautern
Minke E (1988) Grundlagen der Verschleissausbildung an nicht-rotierenden Abrichtschneiden zum Einsatz an konventionellen Schleifwerkzeugen. Doctoral thesis, University of Bremen
Messer J (1983) Abrichten konventioneller Schleifscheiben mit stehenden Werkzeugen. Doctoral thesis, Aachen University
Moehlen H (1987) Verschleissverhalten von Diamantschleifscheiben bei der Bearbeitung hochfester Keramikwerkstoffe. Schleifen, Honen, Laeppen und Polieren, 54. Ausgabe, ISBN 3-8027-2675-8
Hessel D (2003) Punktcrushieren keramisch gebundener Diamantschleifscheiben. Doctoral thesis, University of Hannover
Çinar M (1995) Einsatzvorbereitung und Verschleissentwicklung keramisch gebundener CBN-Schleifscheiben. Doctoral thesis, University of Bremen
Stuff D (1996) Einsatzvorbereitung keramisch gebundener CBN-Schleifscheiben. Doctoral thesis, Aachen University
Moser M (1980) Microstructure of ceramics. Structure and properties of grinding tools, Akadémiai Kiadó, Budapest
Bot-Schulz R (2005) Untersuchung der Reaktionen an der Schnittstelle Korn/Bindung fuer Sol-Gel-Korund. Doctoral thesis, Aachen University
Linke B (2007) Wirkmechanismen beim Abrichten keramisch gebundener Schleifscheiben. Doctoral thesis, Aachen University
Klocke F, Nachmani Z, Telle R, Kuhl I Haftungskriterien an der Schnittstelle Korn/Bindung fuer Sol-Gel-Korund-Schleifwerkzeuge: final report, AiF-project 13 972 N, Laufzeit 01.02.04—31.01.06
Folkerts W (1993) Dynamische Prozesskennwerte des Schleifens und deren Einfluss auf das Prozessverhalten. Doctoral thesis, Aachen University
Kammler M (2006) Untersuchungen zur Bestimmung der Biegebruchfestigkeit gebundener Schleifmittel. Materwiss Werksttech 37(5):396–401
Deutsche Gesellschaft fuer Materialkunde e.V. (DGM) Bruchmechanik: Grundlagen, Pruefmethoden und Anwendungsbeispiele. Seminar 24.-26.09.2003 in Freiburg
Engelhorn R (2002) Verschleissmerkmale und Schleifeinsatzverhalten zweiphasig verstaerkter Sol-Gel-Korunde. Doctoral thesis, Aachen University
Peklenik J (1960) Untersuchungen der Haerte von Schleifkoerpern. Industrie-Anzeiger, Essen, pp 431–436
Merbecks T (2003) Entwicklung eines Charakterisierungsverfahrens fuer keramisch gebundene CBN-Schleifscheiben. Doctoral thesis, Aachen University
Malkin S (1989) Grinding technology—theory and applications of machining with abrasives. Ellis Horwood
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Klocke, F., Linke, B. Mechanisms in the generation of grinding wheel topography by dressing. Prod. Eng. Res. Devel. 2, 157–163 (2008). https://doi.org/10.1007/s11740-008-0101-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11740-008-0101-9