Stability of three-dimensional printable foam concrete as function of surfactant characteristics

  • Research Article
  • Published:
Frontiers of Structural and Civil Engineering Aims and scope Submit manuscript

Abstract

Extrudability is one of the most critical factors when designing three-dimensional printable foam concrete. The extrusion process likely affects the foam stability which necessitates the investigation into surfactant properties particularly for concrete mixes with high foam contents. Although many studies have been conducted on traditional foam concrete in this context, studies on three-dimensional printed foam concrete are scarce. To address this research gap, the effects of surfactant characteristics on the stability, extrudability, and buildability of three-dimensional printed foam concrete mixes with two design densities (1000 and 1300 kg/m3) using two different surfactants and stabilizers (synthetic-based sodium lauryl sulfate stabilized with carboxymethyl cellulose sodium salt, and natural-based hingot surfactant stabilized with xanthan gum) were investigated in this study. Fresh density tests were conducted before and after the extrusion to determine stability of the foam concrete. The results were then correlated with surfactant qualities, such as viscosity and surface tension, to understand the importance of key parameters in three-dimensional printing of foam concrete. Based on the experimental results, surfactant solu1tion with viscosity exceeding 5 m Pa·s and surface tension lower than 31 mN/m was recommended to yield stable three-dimensional printable foam concrete mixes. Nevertheless, the volume of foam in the mix significantly affected the printability characteristics. Unlike traditional foam concrete, the variation in the stabilizer concentration and density of concrete were found to have insignificant effect on the fresh-state-characteristics (slump, slump flow, and static yield stress) and air void microstructure of the stable mixes.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Dey D, Srinivas D, Panda B, Suraneni P, Sitharam T G. Use of industrial waste materials for 3D printing of sustainable concrete: A review. Journal of Cleaner Production, 2022, 340: 130749

    Article  Google Scholar 

  2. Tay Y W D, Panda B, Paul S C, Noor Mohamed N A, Tan M J, Leong K F. 3D printing trends in building and construction industry: A review. Virtual and Physical Prototyping, 2017, 12(3): 261–276

    Article  Google Scholar 

  3. Dey D, Srinivas D, Boddepalli U, Panda B, Gandhi I S R, Sitharam T G. 3D printability of ternary Portland cement mixes containing fly ash and limestone. Materials Today: Proceedings, 2022, 70: 195–200

    Google Scholar 

  4. Dey D, Panda B. An experimental study of thermal performance of 3D printed concrete slabs. Materials Letters, 2023, 330: 133273

    Article  Google Scholar 

  5. Bos F P, Menna C, Pradena M, Kreiger E, da Silva W R L, Rehman A U, Weger D, Wolfs R J M, Zhang Y, Ferrara L, Mechtcherine V. The realities of additively manufactured concrete structures in practice. Cement and Concrete Research, 2022, 156: 106746

    Article  Google Scholar 

  6. Boddepalli U, Panda B, Ranjani Gandhi I S. Rheology and printability of Portland cement based materials: A review. Journal of Sustainable Cement-based Materials, 2022, 12(7): 1–19

    Google Scholar 

  7. Markin V, Sahmenko G, Nerella V N, Näther M, Mechtcherine V. Investigations on the foam concrete production techniques suitable for 3D-printing with foam concrete. In: IOP Conference Series: Materials Science and Engineering. Bristol: IOP Publishing Ltd., 2019, 012039

    Google Scholar 

  8. Cho S, van Rooyen A, Kearsley E, van Zijl G. Foam stability of 3D printable foamed concrete. Journal of Building Engineering, 2022, 47: 103884

    Article  Google Scholar 

  9. Cho S, Kruger J, van Rooyen A, van Zijl G. Rheology and application of buoyant foam concrete for digital fabrication. Composites. Part B, Engineering, 2021, 215: 108800

    Article  Google Scholar 

  10. Markin V, Krause M, Otto J, Schröfl C, Mechtcherine V. 3D printing with foam concrete: From material design and testing to application and sustaintability. Journal of Building Engineering, 2021, 43: 102870

    Article  Google Scholar 

  11. Markin N, Nerella V N, Schröfl G, Guseynova G, Mechtcherine V. Material design and performance evaluation of foam concrete for digital fabrication. Materials (Basel), 2019, 12(15): 2433

    Article  Google Scholar 

  12. Markin V, Ivanova I, Fataei S, Reißig S, Mechtcherine V. Investigation on structural build-up of 3D printable foam concrete. In: Second RILEM International Conference on Concrete and Digital Fabrication: Digital Concrete 2020. Cham: Springer International Publishing, 2020, 301–311

    Google Scholar 

  13. Cho S, Kruger J, van Rooyen A, Zeranka S, van Zijl G. Rheology of 3D printable lightweight foam concrete incorporating nanosilica. In: Rheology and Processing of Construction Materials: RheoCon2 & SCC9. Cham: Springer International Publishing, 2020, 373–381

    Chapter  Google Scholar 

  14. Liu C, Wang X, Chen Y, Zhang C, Ma L, Deng Z, Chen C, Zhang Y, Pan J, Banthia N. Influence of hydroxypropyl methylcellulose and silica fume on stability, rheological properties, and printability of 3D printing foam concrete. Cement and Concrete Composites, 2021, 122: 104158

    Article  Google Scholar 

  15. Amran Y H M, Farzadnia N, Ali A A A. Properties and applications of foamed concrete: A review. Construction & Building Materials, 2015, 101: 990–1005

    Article  Google Scholar 

  16. Ramamurthy K, Kunhanandan Nambiar E K, Indu Siva Ranjani G. A classification of studies on properties of foam concrete. Cement and Concrete Composites, 2009, 31(6): 388–396

    Article  Google Scholar 

  17. Wagh C D, Indu Siva Ranjani G, Kamisetty A. Thermal properties of foamed concrete: A review. In: 3rd International Conference on Innovative Technologies for Clean and Sustainable Development: ITCSD 2020. Cham: Springer International Publishing, 2021, 29: 113–137

    Google Scholar 

  18. Siva M, Ramamurthy K, Dhamodharan R. Sodium salt admixtures for enhancing the foaming characteristics of sodium lauryl sulphate. Cement and Concrete Composites, 2015, 57: 133–141

    Article  Google Scholar 

  19. Sahu S S, Gandhi I S R, Khwairakpam S. State-of-the-art review on the characteristics of surfactants and foam from foam concrete perspective. Journal of the Institution of Engineers (India): Series A, 2018, 99(2): 391–405

    Google Scholar 

  20. Ranjani I S, Ramamurthy K. Relative assessment of density and stability of foam produced with four synthetic surfactants. Materials and Structures, 2010, 43(10): 1317–1325

    Article  Google Scholar 

  21. ASTM C796. Standard Test Method for Foaming Agents for Use in Producing Cellular Concrete Using Preformed Foam. West Conshohocken, PA: ASTM Int., 2019

    Google Scholar 

  22. Jones M R, Ozlutas K, Zheng L. Stability and instability of foamed concrete. Magazine of Concrete Research, 2016, 68(11): 542–549

    Article  Google Scholar 

  23. Sahu S S, Gandhi I S R. Studies on influence of characteristics of surfactant and foam on foam concrete behaviour. Journal of Building Engineering, 2021, 40: 102333

    Article  Google Scholar 

  24. Sahu S S, Ranjani Gandhi I S, Kumar A, Garg S. Evaluation of suitability of carboxymethyl cellulose in performance improvement of sodium lauryl sulfate foam and compressive strength of foam concrete. Advances in Civil Engineering Materials, 2021, 10(1): 20200083

    Article  Google Scholar 

  25. Raj S, Krishnan J M, Ramamurthy K. Influence of admixtures on the characteristics of aqueous foam produced using a synthetic surfactant. Colloids and Surfaces. A, Physicochemical and Engineering Aspects, 2022, 643: 128770

    Article  Google Scholar 

  26. Ranjani G I S, Ramamurthy K. Analysis of the foam generated using surfactant sodium lauryl sulfate. International Journal of Concrete Structures and Materials, 2010, 4(1): 55–62

    Article  Google Scholar 

  27. Hajimohammadi A, Ngo T, Mendis P. Enhancing the strength of pre-made foams for foam concrete applications. Cement and Concrete Composites, 2018, 87: 164–171

    Article  Google Scholar 

  28. Khwairakpam S, Ranjani Gandhi I S. Assessment of the potential of a naturally available foaming agent for use in the production of foam concrete. Materials Today: Proceedings, 2020, 32: 896–903

    Google Scholar 

  29. Selija K, Gandhi I S R. Comprehensive investigation into the effect of the newly developed natural foaming agents and water to solids ratio on foam concrete behaviour. Journal of Building Engineering, 2022, 58: 105042

    Article  Google Scholar 

  30. Panda B, Tran J. Innovation in Construction. Cham: Springer International Publishing, 2022, 301–320

    Book  Google Scholar 

  31. Dey D, Srinivas D, Panda B, Sitharam T G. Processing of cementitious materials for 3D concrete printing. In: Industry 4.0 and Advanced Manufacturing: Proceedings of I-4AM 2022. Singapore: Springer, 2023, 283–91

    Chapter  Google Scholar 

  32. ASTM C230. Standard Specification for Flow Table for Use in Tests of Hydraulic Cement 1. West Conshohocken, PA: ASTM Int., 2010

    Google Scholar 

  33. ASTM C1437. Standard Test Method for Flow of Hydraulic Cement Mortar. West Conshohocken, PA: ASTM Int., 2020

    Google Scholar 

  34. Dzuy N Q, Boger D V. Yield stress measurement for concentrated suspensions. Journal of Rheology, 1983, 27(4): 321–349

    Article  Google Scholar 

  35. ASTM C457. Standard Test Method for Microscopical Determination of Parameters of the Air-Void System in Hardened Concrete 1. West Conshohocken, PA: ASTM Int., 2013

    Google Scholar 

  36. Nambiar E K K, Ramamurthy K. Air-void characterisation of foam concrete. Cement and Concrete Research, 2007, 37(2): 221–230

    Article  Google Scholar 

  37. Zhu H, Chen L, Xu J, Han Q. Experimental study on performance improvement of anionic surfactant foaming agent by xanthan gum. Construction & Building Materials, 2020, 230: 116993

    Article  Google Scholar 

  38. Porter M. Handbook of Surfactants. Boston, MA: Springer, 2013

    Google Scholar 

  39. ASTM C869. Standard Specification for Foaming Agents Used in Making Preformed Foam for Cellular Concrete. West Conshohocken, PA: ASTM Int., 1999

    Google Scholar 

  40. Huang B, Nan X, Fu C, Guo T. Study of the bubble collapse mechanism and its influencing factors on stability under ultra-low surface tension. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2021, 618: 126440

    Article  Google Scholar 

  41. Tay Y W D, Qian Y, Tan M J. Printability region for 3D concrete printing using slump and slump flow test. Composites. Part B, Engineering, 2019, 174: 106968

    Article  Google Scholar 

  42. Le T T, Austin S A, Lim S, Buswell R A, Gibb A G F, Thorpe T. Mix design and fresh properties for high-performance printing concrete. Materials and Structures, 2012, 45(8): 1221–1232

    Article  Google Scholar 

Download references

Acknowledgements

The authors gratefully acknowledge the support from the Department of Civil and Mechanical Engineering, Indian Institute of Technology Guwahati, India.

Author information

Authors and Affiliations

  1. Department of Civil Engineering, Indian Institute of Technology, Guwahati, Assam, 781039, India

    Uday Boddepalli & Indu Siva Ranjani Gandhi

  2. Sustainable Resources for Additive Manufacturing (SReAM) Laboratory, Department of Mechanical Engineering, Indian Institute of Technology, Guwahati, Assam, 781039, India

    Biranchi Panda

Authors
  1. Uday Boddepalli
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Indu Siva Ranjani Gandhi
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Biranchi Panda
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Biranchi Panda.

Ethics declarations

The authors declare that they have no conflict of interest.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Boddepalli, U., Gandhi, I.S.R. & Panda, B. Stability of three-dimensional printable foam concrete as function of surfactant characteristics. Front. Struct. Civ. Eng. 17, 935–947 (2023). https://doi.org/10.1007/s11709-023-0964-z

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11709-023-0964-z

Keywords

Search

Navigation