Failure Analysis of Metallic Components of a Battery Fitted in a Naval System

Abstract

A battery based on Mg–AgCl with sea water as electrolyte was developed for propulsion of a naval system. In one occasion, the tie rod, conduit pipe and the copper bus rod each covered with polymer sleeve were found damaged. The copper bus rod was melted probably by amplified resistance and subsequent heating. Localized cross-sectional reduction (and thus increased resistance, R) seems to have aggravated heating by Joule heating (J = I2R) effect. Subsequently, it led to partial dissolution, embrittlement, softening and final fracture of the steel tie rod in the said sequence. There was no material deficiency. Chemical composition, microstructure and hardness values of the failed components indicate that the steel tie rod was made of the as-specified EN 24 type of low alloy steel in hardened and tempered condition, while copper bus rods were made of pure copper of 99.50% purity. Damage of the conduit tube was not related to the failure of steel tie rod and copper bus rod, although it indirectly offers clues that melting of copper happened and the molten copper reached many locations within the system.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16

References

  1. B. Joseph, M. Picat, F. Barbier, Liquid metal embrittlement: a state-of-the-art appraisal. Eur. Phys. J. Appl. Phys. 5(1), 19–31 (1999)

    Article  Google Scholar 

  2. W.F. Savage, E.F. Nippes, R.P. Stanton, Intergranular attack of steel by molten copper. Weld. Res. Suppl. 57, 9s–16s (1978)

    Google Scholar 

Download references

Acknowledgment

The authors would like to thank Dr. Vikas Kumar, Distinguished Scientist (DS) and the Director, DMRL for his constant encouragement to work on the present field. Also, funding from DRDO is gratefully acknowledged.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Mrityunjoy Hazra.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hazra, M., Singh, S. Failure Analysis of Metallic Components of a Battery Fitted in a Naval System. J Fail. Anal. and Preven. 19, 882–889 (2019). https://doi.org/10.1007/s11668-019-00689-9

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11668-019-00689-9

Keywords

  • Failure
  • Metallic component
  • Battery
  • Liquid metal embrittlement (LME)
  • En 24 steel
  • Copper bus rod