Erosion–Corrosion Behavior of 20Cr Steel in Corrosive Solid–Liquid Two-Phase Flow Conditions

Technical Article---Peer-Reviewed

Abstract

An experimental study was conducted on erosion–corrosion (E–C) properties of 20Cr (Chinese steel grade) steel. Three corrosive solid–liquid two-phase aqueous solutions (distilled water, 3.5 wt.% NaCl aqueous solutions and saturated CO2 aqueous solutions, respectively, mixed with quartz grain) are used at three different experiments. The research confirmed that the E–C rate increased exponentially with the increase in flow velocity. The equation V e  = KV n can be used to express the relationship between E–C rate and flow velocity. Furthermore, a new regression approach called ‘segment fitting’ was proposed. It had better fitting precision to express the relationship between E–C rate and flow velocity. The analysis and SEM surface topography show that the material removal rate is controlled by electrochemical corrosion at lower flow velocity and may suffer from mechanically induced deterioration at higher flow velocity. The impact angle has complex effects on E–C rate. In the experiment condition, the E–C rate will reach highest at 45° impact angle.

Keywords

Low-alloy steel Erosion–corrosion Solid–liquid two-phase Erosion–corrosion rate 

Notes

Acknowledgments

Thanks are due to the National Natural Science Foundation Program of China (No. 51305348) and Youth Pearl River Nova Program of Shaanxi (2015KJXX-37).

References

  1. 1.
    J. Werer, Flow induced corrosion: 25 years of industrial research. Br. Corros. J. 27, 193–199 (1992)CrossRefGoogle Scholar
  2. 2.
    X. Jiang, Y.G. Zheng, W. Ke, Effect of flow velocity and entrained sand on inhibition performances of two inhibitors for CO2 corrosion of N80 steel in 3% NaCl solution. Corros. Sci. 47, 2636–2658 (2005)CrossRefGoogle Scholar
  3. 3.
    A. Neville, T. Hodgkiess, An assessment of the corrosion behaviour of high-grade alloys in seawater at elevated temperature and under a high velocity impinging flow. Corros. Sci. 38, 927–956 (1996)CrossRefGoogle Scholar
  4. 4.
    E.A.M. Hussain, M.J. Robinson, Erosion–corrosion of 2205 duplex stainless steel in flowing seawater containing sand particles. Corros. Sci. 49, 1737–1754 (2007)CrossRefGoogle Scholar
  5. 5.
    S.H. Shah, S. Jain et al., Coiled tubing erosion during hydraulic fracturing slurry flow, in SPE Conference, Houston, 2004Google Scholar
  6. 6.
    Y. Yang, Y.F. Cheng, Parametric effects on the erosion–corrosion rate and mechanism of carbon steel pipes in oil sands slurry. Wear 276–277, 141–148 (2012)CrossRefGoogle Scholar
  7. 7.
    K.S. Tan, J.A. Wharton, R.J.K. Wood, Solid particle erosion–corrosion behaviour of a novel HVOF nickel aluminum bronze coating for marine applications—correlation between mass loss and electrochemical measurements. Wear 258, 629–640 (2005)CrossRefGoogle Scholar
  8. 8.
    A. Neville, M. Reyes et al., Mechanisms of wear on a Co-base alloy in liquid–solid slurries. Wear 238, 138–150 (2000)CrossRefGoogle Scholar
  9. 9.
    B.T. Lu, L.C. Mao, J.L. Luo, Hydrodynamic effects on erosion-enhanced corrosion of stainless steel in aqueous slurries. Electrochim. Acta 56, 87–90 (2010)Google Scholar
  10. 10.
    API, API Specification 5CT, Specification for Casing and Tubing, 9th edn. (American Petroleum Institute, Washington, DC, 2011)Google Scholar
  11. 11.
    H-j Zhu, Y-h Lin, D-z Zeng, R-t Yan, Simulations of flow induced corrosion in API drillpipe connector. J. Hydrodyn. 23(6), 784–791 (2011)CrossRefGoogle Scholar
  12. 12.
    M.M. Salama, An alternative to API 14E erosional velocity limits for sand-laden fluids. J. Energy Resour. Technol. 122, 71–77 (2000)CrossRefGoogle Scholar
  13. 13.
    F. Mohammadi, J. Luo, Effects of particle angular velocity and friction force on erosion enhanced corrosion of 304 stainless steel. Corros. Sci. 52, 2994–3001 (2010)CrossRefGoogle Scholar
  14. 14.
    R.J.K. Wood, Erosion–corrosion interactions and their effect on marine and offshore materials. Wear 261, 1012–1023 (2006)CrossRefGoogle Scholar
  15. 15.
    S.S. Rajahram, T.J. Harvey, R.J.K. Wood, Evaluation of a semi-empirical model in predicting erosion–corrosion. Wear 267, 1883–1893 (2009)CrossRefGoogle Scholar
  16. 16.
    S. Nesic, Effects of multiphase flow on internal CO2 corrosion of mild steel pipelines. Energy Fuels 26, 4098–4111 (2012)CrossRefGoogle Scholar
  17. 17.
    A.V. Levy, P. Crook, The erosion properties of alloys for the chemical processing industries. Wear 151, 337–350 (1991)CrossRefGoogle Scholar
  18. 18.
    D. López et al., Effect of particle velocity and impact angle on the corrosion-erosion of AISI 304 and AISI 420 stainless steels. Wear 259, 118–124 (2005)CrossRefGoogle Scholar
  19. 19.
    M.A. Al-Bukhaiti et al., Effect of impingement angle on slurry erosion behaviour and mechanisms of 1017 steel and high-chromium white cast iron. Wear 262, 1187–1198 (2007)CrossRefGoogle Scholar
  20. 20.
    G.T. Burstein, K. Sasaki, Detecting electrochemical transients generated by erosion corrosion. Electrochim. Acta 46, 3675–3683 (2001)CrossRefGoogle Scholar
  21. 21.
    M. Matsumura, Y. Oka, H. Hiura, M. Yano, The role of passivating film in preventing slurry erosion corrosion of austenitic stainless steel. ISIJ Int. 31, 168–176 (1991)CrossRefGoogle Scholar
  22. 22.
    X. Tanga, L.Y. Xua, Y.F. Cheng, Electrochemical corrosion behavior of X-65 steel in the simulated oil sand slurry. II: synergism of erosion and corrosion. Corros. Sci. 50, 1469–1474 (2008)CrossRefGoogle Scholar
  23. 23.
    A.J. Smitha, M. Stratmann, A.W. Hassel, Investigation of the effect of impingement angle on tribocorrosion using single impacts. Electrochim. Acta 51, 6521–6526 (2006)CrossRefGoogle Scholar

Copyright information

© ASM International 2018

Authors and Affiliations

  1. 1.School of Mechanical EngineeringXi’an Shiyou UniversityXi’anChina

Personalised recommendations