, Volume 18, Issue 2, pp 356–363 | Cite as

Maintenance Error Detection Procedure and A Case Study of Failure Analysis Locomotive Diesel Engine Bearings

  • Fatih Hayati Cakir
  • Abdullah Sert
  • Osman Nuri Celik
  • Nurten Dereoğlu
Technical Article---Peer-Reviewed
  • 132 Downloads

Abstract

This paper presents a maintenance error detection algorithm. Proposed algorithm is used to determine failure analysis of a locomotive diesel–electric engine. Although the inspected engines had been performing normally up to the maintenance sequence, the problem occurred after the maintenance and resulted in a complete stop of the engines with the high losses on-site. In failure cases, before focusing on technical problem narrowing down possibilities were required. After initial analysis, many possibilities were eliminated and the problem was determined with less effort on shorter time. Engine bearings were investigated to diagnose the problem. The origin of the problem was diagnosed and determined using SEM techniques and on-site inspections. The results show that the shot peening technique used in engine block cleaning operations caused the deterioration of the engine. Oil filters were damaged and could not hold shot peen particles. The oil filter and engine bearing have been examined with SEM and EDS analyses to determine the source of the particles. Some of the found ferrous particles had a spherical shape of 300–1000 µm. These particles and the high pressure created by the engine’s oil pump used to cool the system caused severe abrasive wear.

Keywords

Bearing failure Contamination Failure analysis Motors Pitting Shot peening Wear 

Notes

Acknowledgments

This work has been performed as a part of investigation of TULOMSAS engine plant division. This study was submitted under permission of TULOMSAS Company.

References

  1. 1.
    T.L.M. Morgado, C.M. Branco, V. Infante, A failure study of housing of the gearboxes of series 2600 locomotives of the Portuguese Railway Company. Eng. Fail. Anal. 15(1–2), 154–164 (2008)CrossRefGoogle Scholar
  2. 2.
    M. Baban, C.F. Baban, F.S. Blaga, Maintenance planning of cold plastic deformation tools using fuzzy logic. Eksploat. Niezawodn. 47(3), 21–26 (2010)Google Scholar
  3. 3.
    Y. Sun, L. Ma, Estimating interactive coefficients for analysing interactive failures. Eksploat. Niezawodn. 46(2), 67–72 (2010)Google Scholar
  4. 4.
    D. Koulocheris, A. Stathis, T. Costopoulos, D. Tsantiotis, Experimental study of the impact of grease particle contaminants on wear and fatigue life of ball bearings. Eng. Fail. Anal. 39, 164–180 (2014)CrossRefGoogle Scholar
  5. 5.
    M.M. Maru, R.S. Castillo, L.R. Padovese, Study of solid contamination in ball bearings through vibration and wear analyses. Tribol. Int. 40(3), 433–440 (2007)CrossRefGoogle Scholar
  6. 6.
    G.K. Nikas, A state-of-the-art review on the effects of particulate contamination and related topics in machine-element contacts. Proc. Inst. Mech. Eng. Part J J. Eng. Tribol. 224(5), 453–479 (2010)CrossRefGoogle Scholar
  7. 7.
    C.Q. Yuan, Z. Peng, X.C. Zhou, X.P. Yan, Effects of temperature on sliding wear process under contaminated lubricant test conditions. Wear 257(7–8), 812–822 (2004)CrossRefGoogle Scholar
  8. 8.
    A. Vencl, A. Rac, Diesel engine crankshaft journal bearings failures: case study. Eng. Fail. Anal. 44, 217–228 (2014)CrossRefGoogle Scholar
  9. 9.
    ISO 7146-1:2008, Plain bearings—appearance and characterization of damage to metallic hydrodynamic bearings—part 1: general (2008). https://www.iso.org/standard/36100.html
  10. 10.
    ISO 7146-2:2008, Plain bearings—appearance and characterization of damage to metallic hydrodynamic bearings—part 2: cavitation erosion and its countermeasures (2008). https://www.iso.org/standard/40940.html
  11. 11.
    SAE, Cast shot and grit size specifications for peening and cleaning, J444_201209 (2009). https://www.sae.org/standards/content/j444_201209/

Copyright information

© ASM International 2018

Authors and Affiliations

  1. 1.Eskişehir Vocational SchoolEskişehir Osmangazi UniversityEskisehirTurkey
  2. 2.Department of Mechanical EngineeringEskisehir Osmangazi UniversityBati Meselik, EskisehirTurkey
  3. 3.TULOMSAS Engine CompanyEskisehirTurkey

Personalised recommendations