A High Performance of ENi–P Coatings on Mechanical and Tribological Properties with Influence of Bath pH on AZ91 Magnesium Alloy

Technical Article---Peer-Reviewed

Abstract

Electroless nickel–phosphorus (ENi–P) coating was carried out on AZ91 magnesium alloy substrates by varying the bath solutions pH. The ENi–P coating process was carried out with sodium hydroxide as the pH adjuster. The effect of bath pH values on surface characteristics and wear resistance properties were investigated after deposition on AZ91 magnesium alloy substrates. Three suitable bath compositions with different pH were prepared for coating the substrates. Encouraging results for ENi–P deposit were obtained when the bath pH value was maintained at 6.5. A smooth and uniform microstructure was observed in the deposit obtained from bath B (6.5 pH). It also enhanced the microhardness and wettability, while the surface roughness of the ENi–P deposit reduced considerably, thereby resulting in better wear resistance and also preventing regular or early failures, and improving service life.

Keywords

Electroless Ni–P alloy coatings Microhardness pH (NaOH) solution Wear resistance 

References

  1. 1.
    W.X. Zhang, J.G. He, Z.H. Jiang, J.S. Lian, Electroless Ni–P layer with a chromium-free pretreatment on AZ91D magnesium alloy. Surf. Coat. Technol. 201, 4594–4600 (2007)CrossRefGoogle Scholar
  2. 2.
    M. Anik, E. Korpe, Effect of alloy microstructure on electroless NiP deposition behavior on alloy AZ91. Surf. Coat. Technol. 201, 4702–4710 (2007)CrossRefGoogle Scholar
  3. 3.
    N. El Mahallawy, A. Bakkar, M. Shoeib, H. Palkowski, V. Neubert, Electroless Ni–P coating of different magnesium alloys. Surf. Coat. Technol. 202, 5151–5157 (2008)CrossRefGoogle Scholar
  4. 4.
    W. Riedel, Electroless Nickel Plating (Finishing Publications Ltd., ASM International, Ohio, 1991)Google Scholar
  5. 5.
    D. Mukherjee, D. Rajagopal, Electrodeposition of amorphous nickel alloys. Met. Finish. 90, 15–19 (1992)Google Scholar
  6. 6.
    G.O. Mallory, J.B. Hajdu, The fundamental aspects of electroless nickel plating, in Electroless Plating: Fundamentals and Applications, AESF, Orlando (1990)Google Scholar
  7. 7.
    A. Froats, T.K. Aune, D. Hawke, W. Unsworth, J. Hillis, Corrosion of magnesium and magnesium alloys, 9th edn. (ASM, New York, 1987), p. 740Google Scholar
  8. 8.
    G.L. Makar, J. Kruger, Corrosion of magnesium. Int. Mater. Rev. 38, 138–145 (1993)CrossRefGoogle Scholar
  9. 9.
    D.S. Mehta, S.H. Masood, W.Q. Song, Investigation of wear properties of magnesium and aluminium alloys for automotive application. J. Mater. Proc. Technol. 155, 1526–1531 (2004)CrossRefGoogle Scholar
  10. 10.
    Z. Liu, W. Gao, The effect of substrate on the electroless nickel plating of Mg and Mg alloys. Surf. Coat. Technol. 200, 3553–3560 (2006)CrossRefGoogle Scholar
  11. 11.
    J. Sudagar, J. Lian, W. Sha, Electroless nickel, alloy, composite and nano coatings—a critical review. J. Alloys Compd. 571, 183–204 (2013)CrossRefGoogle Scholar
  12. 12.
    T.S.N. Sankara Narayanan, I. Baskaran, K. Krishnaveni, S. Parthiban, Deposition of electroless Ni–P graded coatings and evaluation of their corrosion resistance. Surf. Coat. Technol. 200, 3438–3445 (2006)CrossRefGoogle Scholar
  13. 13.
    L. Zeng, S. Yang, W. Zhang, Y. Guo, C. Yan, Preparation and characterization of a double-layer coating on magnesium alloy AZ91D. Electrochm. Acta. 55, 3376–3383 (2010)CrossRefGoogle Scholar
  14. 14.
    H. Liu, N. Li, S. Bi, D. Li, Z. Zou, Effect of organic additives on the corrosion resistance properties of electroless nickel deposits. Thin Solid Films 516, 1883–1889 (2008)CrossRefGoogle Scholar
  15. 15.
    M.H. Staia, E.J. Castillo, E.S. Puchi, B. Lewis, H.E. Hintermann, Wear performance and mechanism of electroless Ni-P coating. Surf. Coat. Technol. 86–87, 598–602 (1996)CrossRefGoogle Scholar
  16. 16.
    D.T. Gawne, U. Ma, Wear mechanisms in electroless nickel coatings. Wear 120, 125–149 (1987)CrossRefGoogle Scholar
  17. 17.
    D.T. Gawne, U. Ma, Structure and wear of electroless nickel coatings. Mater. Sci. Technol. 3, 228–238 (1987)CrossRefGoogle Scholar
  18. 18.
    J.K. Dennis, K.S. Sagoo, Wear behavior of engineering coatings and surface treatments. Met. Finish. 89, 111–122 (1991)Google Scholar
  19. 19.
    A.B.D. Cassie, S. Baxter, Wettability of porous surfaces. Trans. Faraday Soc. 40, 546–551 (1944)CrossRefGoogle Scholar
  20. 20.
    M. Miwa, A. Nakajima, A. Fujishima, K. Hashimoto, T. Watanabe, Effect of the surface roughness on sliding angles of water droplet on superhydrophobic surfaces. Langmuir 16, 5754–5760 (2000)CrossRefGoogle Scholar
  21. 21.
    T.J. Athauda, D.S. Decker, R.R. Ozer, Effect of surface metrology on the wettability of SiO2 nanoparticle coating. Mater. Lett. 67, 338–341 (2012)CrossRefGoogle Scholar
  22. 22.
    N.J. Shirtcliffe, G. McHale, S. Atherton, M.I. Newton, An introduction to superhydrophobicity. Adv. Colld. Interf. Sci. 161, 124–138 (2010)CrossRefGoogle Scholar

Copyright information

© ASM International 2016

Authors and Affiliations

  1. 1.Department of Mechanical Engineering, Defence Institute of Advanced Technology (DU)Ministry of DefencePuneIndia

Personalised recommendations