Failure Investigation of Hydrotest Rupture on a Natural Gas Pipeline

  • V. S. A. Challa
  • I. V. S. Yashwanth
  • Kayna Lee Mendoza
  • Stephen Stafford
Technical Article---Peer-Reviewed
  • 140 Downloads

Abstract

A land-based natural gas pipeline, API 5L Grade B pipe with an electric resistance weld (ERW), failed during hydrotesting inspection along the ERW seam, which led to further investigation. Linear indications, indicative of surface cracks, were observed on the outer diameter of the pipe below the fracture surface, made visible by fluorescent light. Using transmission electron microscopy, it was evidenced that a crack may have initiated within the martensite/austenite islands and propagated through the ferrite bands seen beneath the fracture surface in the heat-affected zone. It was also evidenced by scanning electron microscopy (SEM) that the primary fracture mode consisted of high volume fractions of transgranular cleavage and low volume fractions of transgranular microvoid coalescence. Also evidenced in SEM, were regions of non-fracture evidence indicative of inadequate fusion within the ERW seam.

Keywords

Electric resistance weld Heat-affected zone Transmission electron microscopy Scanning electron microscopy Martensite/austenite islands Transgranular cleavage Transgranular microvoid coalescence 

Notes

Acknowledgments

The authors gratefully acknowledge the support from the Department of Metallurgical and Materials Engineering, University of Texas at El Paso. The authors acknowledge Paul Spencer for helping with NDE and Dr. Bradley for cleaning the fracture surface.

References

  1. 1.
    R. Datta, A. Deva, An investigation into the failure of API 5L X-46 grade ERW linepipes. Prat. Fract. Anal. 2(2), 59–62 (2002)Google Scholar
  2. 2.
    E. St. Pierre, Cold cracking of weld. Sodel Google Scholar

Copyright information

© ASM International 2016

Authors and Affiliations

  • V. S. A. Challa
    • 1
  • I. V. S. Yashwanth
    • 1
  • Kayna Lee Mendoza
    • 1
  • Stephen Stafford
    • 1
  1. 1.Department of Metallurgical and Materials EngineeringUniversity of Texas at El PasoEl PasoUSA

Personalised recommendations