Failure Analysis of Nozzle Guide Vane of a Low Pressure Turbine in an Aero Gas Turbine Engine
- 289 Downloads
Failure of low pressure turbine nozzle guide vane (NGV) in an aero gas turbine engine is analyzed to determine its root cause. Forensic and metallurgical investigations are carried out on the NGV failed as well as the failed components of the downstream modules. Failure in the cooling system in the NGV due to crack in the sealing plate was found to be the cause of NGV getting burnt. This failure has caused extensive damages in low pressure turbine modules. Remedial measures are also suggested to prevent such failures.
KeywordsFailure analysis Cracks Forensic analysis Corrosion Oxidation
The authors are very grateful to the Executive Director, Engine Division, Hindustan Aeronautics Limited, General Manager, Foundry & Forge Division, Hindustan Aeronautics Limited and Chief Executive (Airworthiness), CEMILAC for their kind permission for publishing this paper.
- 3.S. Suresh, Fatigue of Materials, 2nd edn, (Cambridge University Press, Cambridge, 2003). pp. 256–257Google Scholar
- 4.J.A. Bannantine, J.J. Comer, J.L. Handrock, Fundamental of Metal Fatigue Analysis (Prentice Hall Inc, Englewood Cliffs, 1990), pp. 40–87Google Scholar
- 6.C.B. Meher-Homji, G. Gabriles, Gas turbine blade failures-causes, avoidance and trouble shooting. Proceedings of 27th Turbomachinery Symposium, 1995Google Scholar
- 7.H. Cohen, G.F.C. Rogers, H.I.H. Saravanamuttoo, Gas Turbine Theory, (Wiley, New York, 1996)Google Scholar
- 9.H.Arthur Lefebvre, GAS Turbine Combustion (CRC Press, Boca Raton, 1998)Google Scholar