Failure Investigation of Cooling Plates of a Blast Furnace

  • Pankhuri Sinha
  • Goutam Mukhopadhyay
  • Sandip Bhattacharyya
Case History—Peer-Reviewed
  • 181 Downloads

Abstract

Premature failure of cooling plates of a blast furnace in service has been investigated. The cooling plates are water-cooled copper channels shielded by refractory lining. Industrial cooling water (ICW) flows at 5 bar pressure through the cooling plates. The investigation consisted of visual inspection, chemical analysis, microstructural examination by optical microscopy, energy-dispersive spectroscopy (EDS), and hardness measurement. Visual inspection revealed that the refractory lining on the component was damaged, thereby exposing the cooling plates to elevated temperatures of the furnace atmosphere. This led to overheating of the cooling plates. Chemical analysis revealed that the component was essentially pure copper (~99.24% purity). Microstructural analysis showed grain size variation across the section of the component. Also, annealing twins were revealed on optical examination. A through-thickness pit was identified on the failed component during the optical examination. The examination also revealed branched cracks associated with scale in the component. Energy-dispersive spectroscopy (EDS) confirmed the scale to be oxides indicating high-temperature oxidation of the component resulting in pitting. Analysis suggested overheating due to damage of the refractory lining as the prime cause of failure of the component.

Keywords

Copper cooling plates Overheating Coarse grains 

References

  1. 1.
    IS 228: Part 20: 2003, Methods for Chemical Analysis of Steels—Part 20: Determination of Carbon and Sulphur by Infra Red Absorption Method. Bureau of Indian Standard, New Delhi (2003)Google Scholar
  2. 2.
    ASTM E112-10, Standard test method for determining average grain sizeGoogle Scholar
  3. 3.
    T. Notoya, Localized corrosion in copper tubes and the effect of anti-tarnishing pretreatment. J. Mater. Sci. Lett. 10, 389–391 (1991)CrossRefGoogle Scholar
  4. 4.
    D. Atlas, J. Coombs, O.T. Zajicek, The corrosion of copper by chlorinated drinking waters. Water Res. 16, 693–698 (1982)CrossRefGoogle Scholar
  5. 5.
    P.K.A. Hong, Y. Macauley, Corrosion and leaching of copper tubing exposed to chlorinated drinking water. Water Air Soil Pollut. 108, 457–471 (1998)CrossRefGoogle Scholar

Copyright information

© ASM International 2014

Authors and Affiliations

  • Pankhuri Sinha
    • 1
  • Goutam Mukhopadhyay
    • 1
  • Sandip Bhattacharyya
    • 1
  1. 1.Metallurgical Laboratories, Scientific Services, R&D and Scientific ServicesTata Steel Ltd.JamshedpurIndia

Personalised recommendations