, Volume 14, Issue 1, pp 68–75 | Cite as

Brittle Cracking of a Cylindrical Spiral Gear of Axle Gearbox

Technical Article---Peer-Reviewed
  • 216 Downloads

Abstract

A cylindrical spiral gear of locomotive axle gearbox failed after standing in site for 10 days. The failed gear had been assembled with the spiral gear-shaft. Inspection in site found that cracking occurred on the spoke plate between the shaft bore and the oil-pressed hole. The gear teeth are required to be carburized, but the surfaces of the shaft bore and the oil-pressed hole of gear are surface-coated to prevent carburizing. The crack initiated from the surface of oil-pressed hole and propagated along the radial of the oil-pressed hole. Metallurgical examination reveals that anti-carburizing measure was not conducted on the surface of oil-pressed hole as the specification. A simplified evaluation of the maximum hoop tensile on the wall of oil-pressed hole subjected to internal pressure for swelling bore is far insufficient to lead to brittle fracture. Delayed fracture of gear, the predominance of intergranular fracture micro-mechanism, and the presence of several secondary micro-cracks in the depth of case layer on the oil-pressed hole surface are a clear indication of hydrogen embrittlement. Hydrogen absorption occurred during gas carburizing process.

Keywords

Gear Intergranular brittle fracture Hydrogen embrittlement Carburizing 

References

  1. 1.
    Determination of Carburized Depth and Metallurgic Examination of Carburizing Structure (GB9450, China Standard, 1994) (in Chinese)Google Scholar
  2. 2.
    Metal Hand Book. Fractography and Atlas of Fractographs, 8th edn., vol. 9 (American Society for Metals, Metal Park, OH, 1974)Google Scholar
  3. 3.
    A.K. Jha, K. Sreekumar, Hydrogen-induced cracking (HIC) of hardened and tempered steel fastener used in space application. J. Fail. Anal. Prev. 9, 420–428 (2009)CrossRefGoogle Scholar
  4. 4.
    M.J. Hyder, M. Asif, Optimization of location and size of opening in pressure vessel cylinder using ANSYS. Eng. Fail. Anal. 15, 1–19 (2008)CrossRefGoogle Scholar
  5. 5.
    J. Purbolaksono, Y.W. Hong, S.S.M. Nor, H. Othman, B. Ahmad, Evaluation on reheater tube failure. Eng. Fail. Anal. 16, 533–537 (2009)CrossRefGoogle Scholar
  6. 6.
    Z.-Z. Hu, Steel and Heat Treatment Curves Handbook (National Defense Industry Press, Beijing, 1986) (in Chinese)Google Scholar
  7. 7.
    G. Krauss, Steel: Heat Treatment and Processing Principle (ASM International, Materials Park, 2000)Google Scholar
  8. 8.
    G. Straffelini, L. Versari, Brittle intergranular fracture of a thread: the role of a carburizing treatment. Eng. Fail. Anal. 16, 1448–1453 (2009)CrossRefGoogle Scholar
  9. 9.
    O. Asi, A.C. Can, J. Pineault, M. Belassel, The relationship between case depth of gas carburized SAM 8620 steel. Surf. Coat. Technol. 201, 5979–5987 (2007)CrossRefGoogle Scholar
  10. 10.
    G. Krauss, Steel: Heat Treatment and Processing Principles (ASM International, Materials Park, 2000)Google Scholar
  11. 11.
    G. Krauss, The microstructure and fracture of a carburized steel. Metall. Trans. 9A, 1527–1535 (1978)CrossRefGoogle Scholar
  12. 12.
    H. Streng, C. Razim, J. Grosh, Influence of hydrogen and tempering on the toughness of case-hardened structures. In Carburizing: Processing and Performance (Lakewood, 1989)Google Scholar

Copyright information

© ASM International 2013

Authors and Affiliations

  1. 1.Department of Material Science and EngineeringDalian Maritime UniversityDalianPeople’s Republic of China

Personalised recommendations