, Volume 11, Issue 6, pp 636–641 | Cite as

An Investigation on the Cracking of Air Tubes of Rotary Kilns in a Sponge Iron Plant

  • Goutam Mukhopadhyay
  • Sandip Bhattacharyya
Case History---Peer-Reviewed

Abstract

Cracking of an air tube used for supplying air in rotary kiln of a sponge iron plant is investigated in this paper. The material of the air tube is ASTM A297 HK 40, a member of the heat-resistant cast alloy family (H series) steels widely used for enhanced high-temperature properties. Microstructural degradation occurring at high temperature affects mechanical and corrosion-resistance properties of the component. The failure analysis consists of visual observation, chemical analysis, examination of microstructures using optical and scanning electron microscopes, and characterization with energy-dispersive spectroscopy (EDS). Microstructural characterization reveals (i) intergranular corrosion at the cross section of tube wall, (ii) formation of severe chromium carbide network at the grain boundary, (iii) formation of sigma phases along the grain boundary as well as within the matrix, and (iv) generation of crack at the grain boundary filled with oxides. Analyses of these results suggest that formation of carbide network and sigma phases at the elevated service temperature depletes the alloying elements from the surrounding matrix, enhancing intergranular corrosion, which leads to cracking of the air tube.

Keywords

Air tube HK 40 steel Carbide network Sigma phase Intergranular corrosion 

References

  1. 1.
    ASTM A 297: Standard Specification for Steel Castings, Iron–Chromium and Iron–Chromium–Nickel, Heat Resistant, for General Application. ASTM International, West Conshohocken, PA (2008)Google Scholar
  2. 2.
    Babakr, A.M., Al-Ahmari, A., Al-Jumayiah, K., Habiby, F.: Sigma phase formation and embrittlement of cast iron–chromium–nickel (Fe–Cr–Ni) alloys. J. Min. Mater. Charact. Eng. 7, 127–145 (2008)Google Scholar
  3. 3.
    Hau, J., Seijas, A.: Sigma phase embrittlement of stainless steel in FCC service. In: Corrosion NACExpo 2006, 61st Annu. Conf. Expos. Paper No. 06578 (2006)Google Scholar
  4. 4.
    David, S.A., Vitek, J.M., Alexander, D.J.: Embrittlement of austenitic stainless steel welds. J. Nondestruct. Eval. 15, 129–136 (1996)CrossRefGoogle Scholar
  5. 5.
    Tang, X.: Sigma phase characterization in AISI 316 stainless steel. Microsc. Microanal. 11, 78–79 (2005)CrossRefGoogle Scholar
  6. 6.
    Jackson, E.M.L.E.M., de Visser, P.E., Cornish, L.A.: Distinguishing between chi and sigma phases in duplex stainless steels using potentiostatic etching. Mater. Charact. 31, 185–190 (1993)CrossRefGoogle Scholar
  7. 7.
    Łabanowski, J.: Evaluation of reformer tubes degradation after long term operation. J. Achiev. Mater. Manuf. Eng. 43, 244–251 (2010)Google Scholar
  8. 8.
    Garin, J.L., Mannheim, R.L.: Sigma-phase precipitation upon industrial-like heating of cast heat-resistant steels. J. Mater. Process. Technol. 209, 3143–3148 (2009)CrossRefGoogle Scholar
  9. 9.
    Martins, M., Casteletti, L.C.: Sigma phase morphologies in cast and aged super duplex stainless steel. Mater. Charact. 60, 792–795 (2009)CrossRefGoogle Scholar
  10. 10.
    Babakr, A.M., Al-Ahmrai, A., Al-Jumayiah, K., Habiby, F.: Failure investigation of a furnace tube support. J. Fail. Anal. Preven. 9, 16–22 (2009)CrossRefGoogle Scholar
  11. 11.
    Tillack, D.J., Guthrie, J.E.: Wrought and Cast Heat Resistant Stainless Steel and Nickel Alloys for Refining and Petrochemical Industries. NiDI Technical Series No. 10071. Nickel Development Institute, Toronto (1992)Google Scholar
  12. 12.
    Gunn, R.N.: Duplex Stainless Steels–Microstructure, Properties and Applications, pp. 14–23. Abington Publishing, Cambridge (1997)CrossRefGoogle Scholar
  13. 13.
    Steinkush, W.: High-temperature failure of heat-resistant cast steels. Mater. Corros. 49, 69–87 (1998)CrossRefGoogle Scholar
  14. 14.
    Lopez, N., Cid, M., Puiggali, M.: Influence of sigma-phase on mechanical properties and corrosion resistance of duplex stainless steels. Corros. Sci. 41, 1615–1631 (1999)CrossRefGoogle Scholar
  15. 15.
    Coreno-Alonso, O., Duffus-Scott, A., Zánchez-Conejo, C., Coreno-Alonso, J., Sánchez-de Jesús, F., Bolarín-Miró, A.: On the effect of σ-phase formation during metal dusting. Mater. Chem. Phys. 84, 20–28 (2004)CrossRefGoogle Scholar
  16. 16.
    Sieurin, H., Sandstrom, R.: Sigma phase precipitation in duplex stainless steels. Mater. Sci. Eng. A 444, 271–276 (2004)Google Scholar
  17. 17.
    Kaya, A.A.: Microstructure of HK40 alloy after high-temperature service in oxidizing/carburizing environment. II. Carburization and carbide transformations. Mater. Charact. 49, 23–34 (2002)CrossRefGoogle Scholar
  18. 18.
    ASM International: Metallography and microstructures of heat-resistant alloys. In: ASM Handbook, Metallography and Microstructure, vol. 9, p. 837. ASM International, Materials Park, OH (2004)Google Scholar
  19. 19.
    Craig, B.D., Anderson, D.S. (eds.): Handbook of Corrosion Data, 2nd edn. ASM International, Materials Park, OH (1995)Google Scholar
  20. 20.
    ASM Specialty Hand Book. Stainless Steels, Metallurgy and Properties of Wrought Stainless Steels, pp. 48–52. ASM International, Materials Park, OH (1994)Google Scholar
  21. 21.
    Kaya, A.A., Krauklis, P., Young, D.J.: Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment. I. Oxidation phenomena and propagation of a crack. Mater. Charact. 49, 11–21 (2002)CrossRefGoogle Scholar

Copyright information

© ASM International 2011

Authors and Affiliations

  1. 1.Metallurgical Laboratories and QA GroupR&D and Scientific Services, Tata SteelJamshedpurIndia

Personalised recommendations