Cracking of AFNOR 7020 Aluminum Alloy Weld Joint of Water Tank for Satellite Launch Vehicle: A Metallurgical Investigation

Case History---Peer-Reviewed
  • 117 Downloads

Abstract

Aluminum alloys are frequently used as the preferred material for aerospace applications owing to their high-specific strength and ease of fabrication. In one such application, a torroidal-shaped water tank made of AFNOR 7020 (Al–4.5Zn–1.5Mg) alloy sheet and rings, stores water to provide for the initial run of a turbo pump and for the cooling of engine components. During the stage leak test, one of the water tanks leaked near the interconnecting ring welded to the shell. Detailed metallurgical investigations found that leakage was due to stress-assisted cracking, which was caused due to locked-in stresses introduced in the material during welding and to an inferior microstructure of the ring parent material. This article brings out the details of the investigations and recommends actions to avoid future failures.

Keywords

AFNOR 7020 aluminum alloy Liquated film Stress-assisted cracking 

Notes

Acknowledgments

The authors are indebted to Shri P.S. Veeraraghavan, Director, VSSC for permission to publish this work.

References

  1. 1.
    Jha, A.K., Sreekumar, K., Sinha, P.P.: Cracking of Al–Zn–Mg aluminium alloy nozzle weld of propellant storage tank—a metallurgical investigation. J. Fail. Anal. Prev. 9, 504–510 (2009)CrossRefGoogle Scholar
  2. 2.
    Jha, A.K., Narayanan, P.R., Sreekumar, K., Sinha, P.P.: Cracking of Al–4.5Zn–1.5Mg aluminium alloy propellant tank—a metallurgical investigation. Eng. Fail. Anal. 17, 562–570 (2010)CrossRefGoogle Scholar
  3. 3.
    Jha, A.K., Narayanan, P.R., Sreekumar, K.: Liquation cracking of Al–6.3Cu aluminium alloy propellant storage tank—a case study. Eng. Fail. Anal. 16, 1587–1596 (2009)CrossRefGoogle Scholar
  4. 4.
    Jha, A.K., Narayanan, P.R., Sreekumar, K., Arumugham, S.: Failure of AA 2014 aluminum alloy bracket. Pract. Metallogr. (Ger.) 29(10), 534–542 (1992)Google Scholar
  5. 5.
    Jha, A.K., Murty, S.V.S.N., Jacob, E.: Metallurgical analysis of cracks on an aluminum alloy ring used in a satellite separation system. Eng. Fail. Anal. 9, 709–719 (2002)CrossRefGoogle Scholar
  6. 6.
    Huang, C., Kou, S.: Liquation cracking in full penetration Al-Si weld. Weld. Res. 111S (2004)Google Scholar
  7. 7.
    Meletis, E.I.: Stress corrosion cracking properties of 2090 Al-Li alloy. In: Goel, V.S. (ed.) Corrosion Cracking, Conference Proceedings, p 315. American Society of Metals (1986)Google Scholar
  8. 8.
    Jha, A.K., Murty, S.V.S.N., Diwakar, V., Kumar, K.S.: Metallurgical analysis of cracking in weldment of propellant tank. Eng. Fail. Anal. 10(3), 265–273 (2003)CrossRefGoogle Scholar
  9. 9.
    Sreekumar, K., John, K.M., Natrajan, A., Lakshmanan, T.S.: Metallurgical aspects of stress assisted failure in high strength aluminium alloy. Pract. Metallogr. 31, 586–595 (1994)Google Scholar

Copyright information

© ASM International 2011

Authors and Affiliations

  1. 1.Materials Characterisation Division, Vikram Sarabhai Space CentreIndian Space Research OrganisationTrivandrumIndia
  2. 2.Materials and Metallurgy Group, Vikram Sarabhai Space CentreIndian Space Research OrganisationTrivandrumIndia
  3. 3.Materials and Mechanical Entity, Vikram Sarabhai Space CentreIndian Space Research OrganisationTrivandrumIndia

Personalised recommendations