, Volume 10, Issue 6, pp 525–530 | Cite as

Failure Analysis of a Crimping Mechanism

  • Federico Sciammarella
  • Sharmistha Sarangi
Technical Article---Peer-Reviewed
  • 110 Downloads

Abstract

This article details the failure analysis of an aluminum bronze bushing that is utilized in a crimping machine. The crimping mechanism has an indenter (made of tool steel) that is guided by the aluminum bronze bushing that began to fail after 50,000 cycles or approximately 2 weeks of production operation. Typical run times prior to these failures were on the order of months. These failures were causing users to conduct excessive maintenance (i.e., swapping out aluminum bronze bushings). Initial concerns with quality of material were raised; however, after a detailed analysis of the entire system it was clear that there were several issues at play that were not previously considered. As a result this study focused on identifying appropriate materials and design changes of the indenter and bushing to reduce the wear and thus increase life.

Keywords

Indenter Bushing Wear Tool steel AMPCO alloy 

References

  1. 1.
    Guide to Adhesive Wear. Peoton Industries LtdGoogle Scholar
  2. 2.
    Crucible Service Center Data Sheet. Crucible Service Center, www.crucibleservice.com
  3. 3.
    Rigor, cold work tool steel. Tool Steel Facts. Uddeholm CompanyGoogle Scholar
  4. 4.
    Ampco Alloy Brochure. Ampco Metal Inc. www.ampcometal.com
  5. 5.
    Burakowski, T., Wierzchoń, T.: Surface Engineering of Metals. CRC Press, Boca Raton (1999)Google Scholar
  6. 6.
    Shi, Z., Sun, Y., Bloyce, A., Bell, T.: Unlubricated rolling-sliding wear mechanisms of complex aluminium bronze against steel. Wear 193, 235–241 (1996)CrossRefGoogle Scholar
  7. 7.
    Sverker 21, cold work tool steel. Tool Steel Facts. Uddeholm CompanyGoogle Scholar
  8. 8.
    van der Heide, E., Stam, E.D., Giraud, H., Lovato, G., Akdut, N., Clarysse, F., Caenen, P., Heikillä, I.: Wear of aluminium bronze in sliding contact with lubricated stainless steel sheet material. Wear 261, 68–73 (2006)CrossRefGoogle Scholar
  9. 9.
    Yong, W., Cao, L., Xue, Q.: Friction and wear characteristics of ZDDP in the sliding of steel against aluminum alloy. Tribiol. Int. 30, 767–772 (1997)CrossRefGoogle Scholar
  10. 10.
    Poggie, R.A., Wert, J.J.: The influence of surface finish and strain hardening on near-surface residual stress and the friction and wear behavior of A2, D2 and CPM-10V tool steels. Wear 149, 209–220 (1991)CrossRefGoogle Scholar
  11. 11.
    George, E.T.: The Handbook of Lubrication an Tribology. Vol 1: Application and Maintenance, 2nd edn. CRC Press, Boca Raton (2006)Google Scholar
  12. 12.
    Sullivan, J.L., Wong, L.F.: Wear of aluminium bronze on steel under conditions of boundary lubrication. Tribol. Int. 18, 275–281 (1985)CrossRefGoogle Scholar
  13. 13.
    ASM Handbook. Volume 18: Friction, Lubrication, and Wear Technology, 10th edn. ASM, OH (1992)Google Scholar

Copyright information

© ASM International 2010

Authors and Affiliations

  1. 1.Mechanical EngineeringNorther Illinois UniversityDeKalbUSA

Personalised recommendations