, Volume 10, Issue 3, pp 240–244 | Cite as

Degradation Characterization of Ethylene-Propylene-Diene Monomer (EPDM) Rubber in Artificial Weathering Environment

  • Quanlin Zhao
  • Xiaogang Li
  • Jianwen Hu
  • Zhengfang Ye
Technical Article---Peer-Reviewed

Abstract

Ethylene-propylene-diene monomer containing 5-ethylidene-2-norbornene as diene was exposed to artificial weathering environment produced by a xenon lamp light exposure and weathering equipment for different periods of time. The changes of surface color and mechanical properties were monitored by spectrophotometer, computer-controlled tensile testing and hardness measurements. Crosslink density of ethylene-propylene-diene monomer specimens was measured by the solvent swell method. The results showed that the surface of ethylene-propylene-diene monomer became yellower due to the form of carbonyl group. The degradation process proceeded predominantly via cross-linking. With increase in crosslink density, the tensile strength increased and the elongation at fracture decreased.

Keywords

Degradation Ethylene-propylene-diene monomer Artificial weathering Crosslink density Mechanical properties 

Notes

Acknowledgments

The authors are grateful for the financial support of the National Natural Science Foundation of China, whose registered numbers are 50533060 and 50571013. The authors are also thankful for the financial support of the National R&D Infrastructure and Facility Development Program of China, whose registered number is 2005DKA10400.

References

  1. 1.
    Ehsani, M., Borsi, H., Gockenbach, E., Morshedian, J., Bakhshandeh, G.R.: An investigation of dynamic mechanical, thermal, and electrical properties of housing materials for outdoor polymer insulators. Eur. Polym. J. 40, 2495–2503 (2004)CrossRefGoogle Scholar
  2. 2.
    Huang, H., Yang, J., Liu, X., Zhang, Y.: Dynamically vulcanized ethylene propylene diene terpolymer/nylon thermoplastic elastomers. Eur. Polym. J. 38, 857–861 (2002)CrossRefGoogle Scholar
  3. 3.
    Meuleman, E.E.B., Willemsen, J.H.A., Mulder, M.H.V., Strathmann, H.: EPDM as a selective membrane material in pervaporation. J. Membr. Sci. 188, 235–249 (2001)CrossRefGoogle Scholar
  4. 4.
    Yu, L., Wang, W.J., Xiao, W.D.: The effect of decabromodiphenyl oxide and antimony trioxide on the flame retardation of ethylene–propylene–diene copolymer/ polypropylene blends. Polym. Degrad. Stab. 86, 69–73 (2004)CrossRefGoogle Scholar
  5. 5.
    Vieira, I., Severgnini, V.L.S., Mazera, D.J., Soldi, M.S., Pinheiro, E.A., Pires, A.T.N., Soldi, V.: Effects of maleated ethylene propylene diene rubber (EPDM) on the thermal stability of pure polyamides, and polyamide/EPDM and polyamide/poly (ethylene terephthalate) blends: kinetic parameters and reaction mechanism. Polym. Degrad. Stab. 74, 151–157 (2001)CrossRefGoogle Scholar
  6. 6.
    Tillier, D.L., Meuldijk, J., Hohne, G., Frederik, P.M., Regev, O., Koning, C.E.: About morphology in ethylene–propylene(-diene) copolymers-based latexes. Polymer 46, 7094–7108 (2005)CrossRefGoogle Scholar
  7. 7.
    Bhadane, P.A., Champagne, M.F., Huneault, M.A., Tofan, F., Favis, B.D.: Continuity development in polymer blends of very low interfacial tension. Polymer 47, 2760–2771 (2006)CrossRefGoogle Scholar
  8. 8.
    Gamlin, C.D., Dutta, N.K., Choudhury, N.R.: Mechanism and kinetics of the isothermal thermodegradation of ethylene-propylene-diene (EPDM) elastomers. Polym. Degrad. Stab. 80, 525–531 (2003)CrossRefGoogle Scholar
  9. 9.
    Rajeev, R.S., De, S.K., Bhowmick, A.K., John, B.: Studies on thermal degradation of short melamine fibre reinforced EPDM, maleated EPDM and nitrile rubber composites. Polym. Degrad. Stab. 79, 449–463 (2003)CrossRefGoogle Scholar
  10. 10.
    Kumar, A., Commereuc, S., Verney, V.: Aging of elastomers: a molecular approach based on rheological characterization. Polym. Degrad. Stab. 85, 751–757 (2004)CrossRefGoogle Scholar
  11. 11.
    Rivaton, A., Cambon, S., Gardette, J.L.: Radiochemical ageing of ethylene-propylene-diene elastomers. 4. Evaluation of some anti-oxidants. Polym. Degrad. Stab. 91, 136–143 (2006)CrossRefGoogle Scholar
  12. 12.
    Zaharescu, T., Giurginca, M., Jipa, S.: Radiochemical oxidation of ethylene-propylene elastomers in the presence of some phenolic antioxidants. Polym. Degrad. Stab. 63, 245–251 (1999)CrossRefGoogle Scholar
  13. 13.
    Rivaton, A., Cambon, S., Gardette, J.L.: Radiochemical ageing of ethylene-propylene-diene monomer elastomers. 1. Mechanism of degradation under inert atmosphere. J. Polym. Sci. Part A: Polym. Chem. 42, 1239–1248 (2004)CrossRefADSGoogle Scholar
  14. 14.
    Mitra, S., Ghanbari-Siahkali, A., Almdal, K.: A novel method for monitoring chemical degradation of crosslinked rubber by stress relaxation under tension. Polym. Degrad. Stab. 91, 2520–2526 (2006)CrossRefGoogle Scholar
  15. 15.
    Mitra, S., Ghanbari-Siahkali, A., Kingshott, P., Hvilsted, S., Almdal, K.: An investigation on changes in chemical properties of pure ethylene-propylene-diene rubber in aqueous acidic environments. Mater. Chem. Phys. 98, 248–255 (2006)CrossRefGoogle Scholar
  16. 16.
    Mitra, S., Ghanbari-Siahkali, A., Kingshott, P., Rehmeier, H.K., Abildgaard, H., Almdal, K.: Chemical degradation of crosslinked ethylene-propylene-diene rubber in an acidic environment. Part I. Effect on accelerated sulphur crosslinks. Polym. Degrad. Stab. 91, 69–80 (2006)CrossRefGoogle Scholar
  17. 17.
    Mitra, S., Ghanbari-Siahkali, A., Kingshott, P., Rehmeier, H.K., Abildgaard, H., Almdal, K.: Chemical degradation of crosslinked ethylene-propylene-diene rubber in an acidic environment. Part II. Effect of peroxide crosslinking in the presence of a coagent. Polym. Degrad. Stab. 91, 81–93 (2006)CrossRefGoogle Scholar
  18. 18.
    Hong, S.G., Liao, C.M.: The surface oxidation of a thermoplastic olefin elastomer under ozone exposure: ATR analysis. Polym. Degrad. Stab. 49, 437–447 (1995)CrossRefGoogle Scholar
  19. 19.
    Giurginca, M., Zaharescu, T., Meghea, A.: Degradation of ethylene-propylene elastomers in the presence of ozone. Polym. Degrad. Stab. 50, 45–48 (1995)CrossRefGoogle Scholar
  20. 20.
    Snijders, E.A., Boersma, A., Baarle, B., Noordermeer, J.: Effect of third monomer type and content on the UV stability of EPDM. Polym. Degrad. Stab. 89, 200–207 (2005)CrossRefGoogle Scholar
  21. 21.
    Aimura, Y., Wada, N.: Reference materials for weathering tests on rubber products. Polym. Test. 25, 166–175 (2006)CrossRefGoogle Scholar
  22. 22.
    Wang, W.Z., Qu, B.J.: Photo- and thermo-oxidative degradation of photocrosslinked ethylene-propylene-diene terpolymer. Polym. Degrad. Stab. 81, 531–537 (2003)CrossRefGoogle Scholar
  23. 23.
    Zhao, Q.L., Li, X.G., Gao, J.: Surface degradation of ethylene-propylene-diene monomer (EPDM) containing 5-ethylidene-2-norbornene (ENB) as diene in artificial weathering environment. Polym. Degrad. Stab. 93, 692–699 (2008)CrossRefGoogle Scholar

Copyright information

© ASM International 2010

Authors and Affiliations

  • Quanlin Zhao
    • 1
  • Xiaogang Li
    • 2
  • Jianwen Hu
    • 3
  • Zhengfang Ye
    • 1
  1. 1.Department of Environmental Engineering, The Key Laboratory of Water and Sediment Sciences, Ministry of EducationPeking UniversityBeijingPeople’s Republic of China
  2. 2.School of Materials Science and EngineeringUniversity of Science and Technology BeijingBeijingPeople’s Republic of China
  3. 3.Materials Science and Engineering SchoolHebei University of Science and TechnologyShijiazhuangPeople’s Republic of China

Personalised recommendations