The Repair of Magnesium Rotorcraft Components by Cold Spray

Technical Article---Peer-Reviewed

Abstract

The U.S. Army and Navy have experienced significant corrosion problems with magnesium alloys that are used to fabricate aircraft components. The most severe of these are associated with large and expensive transmission and gearbox housings for rotorcraft, which have to be removed prematurely because of corrosion, adversely affecting fleet readiness and safety. Many of the parts cannot be reclaimed because there is not an existing technology that can restore them adequately for service. The replacement of these parts is very expensive ranging in the millions of dollars every year. One common repair technique, used for some of those parts that can be salvaged, involves the use of aluminum shims, which are adhesively bonded over areas where the corrosion has been ground down and dimensional restoration is required. The U.S. Army Research Laboratory (ARL) Center for Cold Spray has developed a cold spray process to reclaim magnesium components that shows significant improvement over existing methods and is in the process of qualification for use on rotorcraft. The cold spray repair has been shown to have superior performance in the tests conducted to date, is inexpensive, can be incorporated into production, and has been modified for field repair, making it a feasible alternative over competing technologies. The work presented in this chapter represents the first two years of a three-year effort, which will result in the establishment of a demonstration cold spray facility at the Naval Air Depot at Cherry Point, North Carolina (NADEP-CP) where the overhaul and repair of Navy rotorcraft is accomplished. The program involved the participation of all branches of the U.S. Department of Defense, major U.S. helicopter companies, academia and international participation.

Keywords

Cold spray Magnesium transmission housings Commercially-pure aluminum Galvanic corrosion 

References

  1. 1.
    Levy, M., Bombard, R., Huie, R.: Assessment of some corrosion protection schemes for magnesium alloy ZE41A-T5. In: Tri-Service Corrosion Conference, pp. 154–167Google Scholar
  2. 2.
    Yamauchi, M., Seki, J., Sakita, E., Miyata, Y., Arita, K.: Corrosion resistant composite layer on magnesium alloys. Adv. Compos. Mater. 1(1), 3–10 (1991)CrossRefGoogle Scholar
  3. 3.
    Gonzalez-Nunez, M.A., Nunez-Lopez, C.A., Skeldon, P., Thompson, G.E., Karimzadeh, H., Lyon, P., Wilks, T.E.: A non-chromate conversion coating for magnesium alloys and magnesium-based metal matrix composites. Corros. Sci. 37(11), 1763–1772 (1995)CrossRefGoogle Scholar
  4. 4.
    Gorman, W., Woolsey, E.: Selective anodization process for repair of magnesium helicopter components. In: Tri Service Corrosion Conference (2003)Google Scholar
  5. 5.
    Griffin, R., Zuniga, D.: Evaluation of coatings on Mg alloy ZE41A used in helicopter rotor gearboxes. In: Tri Service Corrosion Conference (2005)Google Scholar
  6. 6.
    Robinson, A.I.: Evaluation of various magnesium finishing systems. In: Proceedings of International Magnesium Association, 42nd World Conference, May 1985, NYGoogle Scholar
  7. 7.
    Johnson, A.: Helium recycle – a viable industrial option for cold spray. In: Cold Spray Conference. ASM International, Akron, OH (2004)Google Scholar
  8. 8.
    Vlcek, J., Gimeno, L., Huber, H., Lugscheider, E.: A systematic approach to material eligibility for the cold spray process. J. Therm. Spray Technol. 14, 125–133 (2005)CrossRefGoogle Scholar
  9. 9.
    ASM Handbook, Tenth Edition, Volume 2, “Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, p 49Google Scholar
  10. 10.
    Stoltenhoff, T., Kreye, H., Krommer, W., Richter, H.J.: Cold spraying-from thermal spraying to high kinetic energy spraying. In: Heinrich, P. (ed.) HVOF Colloquium 2000, pp. 29–38. Gemeinschaft Thermisches Spritzen e. V. (2000)Google Scholar
  11. 11.
    Stoltenhoff, T., Kreye, H., Richter, H.J., Assadi, H.: Optimization of the cold spray process. In: Berndt, C.C., Khor, K.A., Lugscheider, E.F. (eds.) ITSC 2001, pp. 409–416. ASM International, Materials Park (2001)Google Scholar
  12. 12.
    McCune, R.C., Donlon, W.T., Popoola, O.O., Cartwight, E.L.: Characterization of copper layers produced by cold gas-dynamic spraying. J. Therm. Spray Technol. 9(1), 73–82 (2000)CrossRefGoogle Scholar
  13. 13.
    Maev, R.Gr., Leshchynsky, V., Papyrin, A.: Structure formation of Ni-based composite coatings during low pressure gas dynamic spraying. In: Proceedings of the 2006 International Thermal Spray Conference, May 15–18, 2006, Seattle, Washington, USA, Sponsored by ASM InternationalGoogle Scholar
  14. 14.
    Graham, R.A., Thadhani, N.N.: Solid-state reactivity of shock-processed solids. In: Sawaoka, A.B. (ed.) Shock Waves in Materials Science, pp. 35–65. Springer, Berlin (1993)Google Scholar
  15. 15.
    Kreye, H.: The cold spray process and its potential for industrial applications. In: Presentation at Cold Spray 2004, September 27–28, 2004, Akron, OH. Sponsored by Thermal Spray Society of ASM InternationalGoogle Scholar
  16. 16.
    Zhang, D., Shipway, P.H., McCartney, D.G.: Cold gas dynamic spraying of aluminum: the role of substrate characteristics in deposit formation. J. Therm. Spray Technol. 14, 109–116 (2005)CrossRefGoogle Scholar
  17. 17.
    Papyrin, A.: Cold spray technology. Adv. Mater. Process. 159(9), 49–51 (2001)Google Scholar

Copyright information

© Society for Machinery Failure Prevention Technology 2007

Authors and Affiliations

  1. 1.US Army Research LaboratoryAberdeenUSA

Personalised recommendations