Abstract
This work examines the effect of grain refinement via accumulative roll bonding (ARB) on the homogeneity of microstructure and hardness through the thickness of commercially pure aluminum AA1100 sheets. The use of 7 cycles of ARB was shown to produce homogeneous ultrafine-grained microstructure, reducing the grain size to 0.46 and 1.03 µm in normal direction and rolling direction, respectively. Examination by electron backscattered diffraction indicates that continuous dynamic recrystallization was the main mechanism for the formation of submicron equiaxed grains bounded with high-angle grain boundaries (HAGBs). The fraction of HAGBs increased gradually reaching a maximum of 71.6% after 7 cycles. Through-thickness hardness measurements using Vickers and nanoindentation tests show an increase from 43.5 Hv (0.85 GPa) for as-received sample to 63 Hv (1.1 GPa) after 7 cycles. The heterogeneity in hardness through the thickness of the as-received material was shown to restrain the evolution of uniform hardness across the sheet thickness with increasing ARB cycles. Tensile tests showed that the tensile strength is increased to 250 MPa, which is about 2 times its initial value. Owing to the high stacking fault energy of AA1100, strong dynamic recovery occurred with increasing ARB strain which was balanced with the strain hardening property of the material. This resulted in plastic instability at small strains and thus early necking during the tensile test.
Similar content being viewed by others
References
Y. Saito, H. Utsunomiya, N. Tsuji, and T. Sakai, Novel Ultra-high Straining Process for Bulk Materials Development of the Accumulative Roll-Bonding (ARB) Process, Acta Mater., 1999, 47(2), p 579–583
J. Chang, G. Kim, and I. Moon, X-ray Diffraction Analysis of Pure Aluminum in the Cyclic Equal Channel Angular Pressing, Scr. Mater., 2001, 44, p 331–336
N. Tsuji, Y. Saito, S. Less, and Y. Minamino, ARB (Accumulative Roll-Bonding) and Other New Techniques to Produce Bulk Ultrafine Grained Materials, Adv. Eng. Mater., 2003, 5, p 338–344
H. Pirgazi, A. Akbarzadeha, R. Petrovb, and L. Kestensc, Microstructure Evolution and Mechanical Properties of AA1100 Aluminum Sheet Processed by Accumulative Roll Bonding, Mater. Sci. Eng. A, 2008, 497, p 132–138
M. Eizadjou, H.D. Manesh, and K. Janghorban, Microstructure and Mechanical Properties of Ultra-fine Grains (UFGs) Aluminum Strips Produced by ARB Process, J. Alloy. Compd., 2009, 474, p 406–415
X. Huang, N. Tsuji, N. Hansen, and Y. Minamino, Microstructural Evolution During Accumulative Roll-Bonding of Commercial Purity Aluminum, Mater. Sci. Eng. A, 2003, 340, p 265–271
H.-W. Kim, S.-B. Kang, N. Tsuji, and Y. Minamino, Elongation Increase in Ultra-fine Grained Al–Fe–Si Alloy Sheets, Acta Mater., 2005, 53, p 1737–1749
J. Scharnweber, W. Skrotzki, C.-G. Oertel, H.-G. Brokmeier, H.W. Höppel, I. Topic, and J. Jaschinski, Texture, Microstructure and Mechanical Properties of Ultrafine Grained Aluminum Produced by Accumulative Roll Bonding, Adv. Eng. Mater., 2010, 12, p 989–994
K. Wu, H. Chang, E. Maawad, W.M. Gan, H.G. Brokmeier, and M.Y. Zheng, Microstructure and Mechanical Properties of the Mg/Al Laminated Composite Fabricated by Accumulative Roll Bonding (ARB), Mater. Sci. Eng. A, 2010, 527, p 3073–3078
S.H. Lee, Y. Saito, T. Sakai, and H. Utsunomiya, Microstructures and Mechanical Properties of 6061 Aluminum Alloy Processed by Accumulative Roll-Bonding, Mater. Sci. Eng. A, 2002, 325, p 228–235
S.H. Lee, Y. Saito, N. Tsuji, H. Utsunomiya, and T. Sakai, Role of Shear Strain in Ultragrain Refinement by Accumulative Roll-Bonding (ARB) Process, Scr. Mater., 2002, 46, p 281–285
W.C. Oliver and G.M. Pharr, An Improved Technique for Determining Hardness and Elastic Modulus Using Load and Displacement Sensing Indentation Experiments, J. Mater. Res., 1992, 7, p 1564–1583
N. Tsuji, R. Ueji, Y. Ito, Y. Saito, In-situ Recrystallization of Ultra-fine Grains in Highly Strained Metallic Materials, Proceedings of the 21 st RISØ International Symposium on Materials Science, Denmark, 2000, pp 607–616
F.J. Humphreys and M. Hatherly, Recrystallization and Related Annealing Phenomena, 2nd ed., Elsevier, Kidlington, 2004
F.J. Humphreys, P.B. Prangnell, and R. Priestner, Fine-Grained Alloys by Thermomechanical Processing, Curr. Opin. Solid State Mater. Sci., 2001, 5, p 15–21
K. Huang and R.E. Logé, A Review of Dynamic Recrystallization Phenomena in Metallic Materials, Mater. Des., 2016, 111, p 548–574
M. Shaarbaf and M.R. Toroghinejad, Nano-grained Copper Strip Produced by Accumulative Roll Bonding Process, Mater. Sci. Eng. A, 2008, 473, p 28–33
S. Pasebani and M.R. Toroghinejad, Nano-grained 70/30 Brass Strip Produced by Accumulative Roll-Bonding (ARB) Process, Mater. Sci. Eng. A, 2010, 527, p 491–497
P. Chekhonin, B. Beausir, J. Scharnweber, C. Oertel, T. Hausol, H.W. Hoppel, and W. Skrotzki, Confined Recrystallization of High-Purity Aluminum During Accumulative Roll Bonding of Aluminum Laminates, Acta Mater., 2012, 60, p 4661–4671
H. Jazaeri, F.J. Humphreys, The Recrystallization of a Highly Deformed Al–Fe–Mn Alloy, Proceedings of first International Conference on Recrystallization and Grain Growth. Aachen, Germany, 2001, pp 27–31
K.D. Lau, “Development of Microstructure and Texture in Accumulative Roll Bonded Commercial Purity Aluminium,” Master’s thesis, University of New South Wales, Australia, 2011
B. Li, N. Tsuji, and N. Kamikawa, Microstructure Homogeneity in Various Metallic Materials Heavily Deformed by Accumulative Roll-Bonding, Mater. Sci. Eng. A, 2006, 423, p 331–342
C. Kwan, Z. Wang, and S.B. Kang, Mechanical Behavior and Microstructural Evolution Upon Annealing of the Accumulative Roll-Bonding (ARB) Processed Al Alloy 1100, Mater. Sci. Eng. A, 2008, 480, p 148–159
M. Raei, M.R. Toroghinejad, and R. Jamaati, Nano/Ultrafine Structured AA1100 by ARB Process, Mater. Manuf. Process., 2011, 26, p 1352–1356
R.W. Hertzberg, Deformation and Fracture Mechanics of Engineering Materials, 3rd ed., Wiley, Singapore, 1989, p 253–257
N. Tsuji, Y. Ito, Y. Saito, and Y. Minamino, Strength and Ductility of Ultrafine Grained Aluminum and Iron Produced by ARB and Annealing, Scr. Mater., 2002, 47, p 893–899
R. Manna, N.K. Mukhopadhyay, and G.V.S. Sastry, Effect of Equal Channel Angular Pressing on Microstructure and Mechanical Properties of Commercial Purity Aluminum, Metall. Mater. Trans. A, 2008, 39, p 1525–1534
L. Su, C. Lu, A.K. Tieu, G. Deng, and X. Sun, Ultrafine Grained AA1050/AA6061 Composite Produced by Accumulative Roll Bonding, Mater. Sci. Eng. A, 2013, 559, p 345–351
W.D. Nix and H. Gao, Indentation Size Effects in Crystalline Materials: A Law for Strain Gradient Plasticity, J. Mech. Phys. Solids, 1998, 46, p 411–425
E.O. Hall, The Deformation and Ageing of Mild Steel: III, Discussion of Results, Proc. Phys. Soc., 1951, 64, p 747–753
N.J. Petch, The Cleavage Strength of Polycrystals, J. Iron Steel Inst., 1953, 173, p 25–28
N. Kamikawa, X. Huang, N. Tsuji, and N. Hansen, Strengthening Mechanisms in Nanostructured High-Purity Aluminium Deformed to High Strain and Annealed, Acta Mater., 2009, 57, p 4198–4208
J.W. Wyrzykowski and M.W. Grabski, The Hall–Petch Relation in Aluminium and Its Dependence on the Grain Boundary Structure, Philos. Mag. A, 1986, 53, p 505–520
S. Thangaraju, M. Heilmaier, B.S. Murty, and S.S. Vadlamani, On the Estimation of True Hall–Petch Constants and Their Role on the Superposition Law Exponent in Al Alloys, Adv. Eng. Mater., 2010, https://doi.org/10.1002/adem.201200114
N. Hansen, Hall–Petch Relation and Boundary Strengthening, Scr. Mater., 2004, 51, p 801–806
K. Ma, H. Wen, T. Hu, T.D. Topping, D. Isheim, D.N. Seidman, E.J. Lavernia, and J.M. Schoenung, Mechanical Behavior and Strengthening Mechanisms in Ultrafine Grain Precipitation-Strengthened Aluminum Alloy, Acta Mater., 2014, 62, p 141–155
T. Huang, L. Shuai, A. Wakeel, G. Wu, N. Hansen, and X. Huang, Strengthening Mechanisms and Hall–Petch Stress of Ultrafine Grained Al–0.3%Cu, Acta Mater., 2018, 156, p 369–378
Y. Murata, I. Nakaya, and M. Morinaga, Assessment of Strain Energy by Measuring Dislocation Density in Copper and Aluminium Prepared by ECAP and ARB, Mater. Trans., 2008, 49, p 20–23
A. Rezaee-Bazzaz, S. Ahmadian, and H. Reihani, Modeling of Microstructure and Mechanical Behavior of Ultrafine Grained Aluminum Produced by Accumulative Roll Bonding, Mater. Des., 2011, 32, p 4580–4585
Acknowledgments
The authors would like to acknowledge the support provided by Kuwait University General Facility (Grant No. GE 01/07) for sample preparation and SEM and EBSD measurements.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Al-Fadhalah, K.J., Alyazidi, M.K. & Rafiq, M. Effect of Microstructure Refinement on Hardness Homogeneity of Aluminum Alloy 1100 Processed by Accumulative Roll Bonding. J. of Materi Eng and Perform 28, 4693–4706 (2019). https://doi.org/10.1007/s11665-019-04228-3
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-019-04228-3