Abstract
The mechanical and thermal insulation properties of expanded vermiculite (EV)/forsterite composite materials before and after the modification of EV by in situ alumina gel were characterized by three-point bending test, compressive strength test, and the flat-plate method for the determination of the thermal conductivity. The estimation method for the determination of the thermal conductivity of modified EV/forsterite composite materials was put forward, and the thermal conductivity in case of a high content of modified EV (the substitution rate of modified EV is more than 50 wt.%) is forecasted in this paper. The results show that, the mechanical properties and thermal insulation properties of the composite materials were significantly improved by increasing the modified EV content. When the substitution rate of modified EV was 50 wt.%, the flexural and compressive strength were 11.55 and 22.80 MPa, improved by 23.8 and 44.9%, respectively, compared with the unmodified sample; and the thermal conductivity was 0.169 W/m/K (at 1073 K), improved by 30.5%. The estimated thermal conductivities of modified EV/forsterite composite materials show good agreement with that of experiments, and the thermal conductivity of modified EV/forsterite composite materials was 0.157 W/m/K (at 1073 K) in case the substitution rate of modified EV was 100 wt.% through estimation.
Similar content being viewed by others
References
F. Koksal, O. Gencel, W. Brostow, and H.E. Hagg Lobland, Effect of High Temperature on Mechanical and Physical Properties of Lightweight Cement Based Refractory Including Expanded Vermiculite, Mater. Res., 2012, 16(1), p 7–13
K. Okada, S. Matsui, T. Isobe, Y. Kameshima, and A. Nakajima, Water-Retention Properties of Porous Ceramics Prepared from Mixtures of Allophane and Vermiculite for Materials to Counteract Heat Island Effects, Ceram. Int., 2008, 34(2), p 345–350
V.E. Peletskii and B.A. Shur, Experimental Study of the Thermal Conductivity of Heat Insulation Materials Based on Expanded Vermiculite, Refract. Ind. Ceram, 2007, 48(5), p 356–358
S.A. Suvorov and V.V. Skurikhin, High Temperature Heat Insulating Materials Based on Vermiculite, Refract. Ind. Ceram., 2002, 43(11–12), p 383–389
S.A. Suvorov and V.V. Skurikhin, Vermiculite—A Promising Material for High Temperature Heat Insulators, Refract. Ind. Ceram, 2003, 44(3), p 186–193
G.S. Hu, Z.Y. Li, Y.P. Zhu, and W.G. Zhang, Preparation of Vermiculite Powder with High Expansion and High Quality—II. Thermal Expansion of Vermiculite, Chin. J. Chem. Eng., 2006, 6, p 763–767
J. Matins and R. Fernandes, Hydrophobic Expanded Vermiculite as a Cleaning Agent for Contaminated Waters, Water Sci. Technol., 1992, 26, p 2297–2299
C.X. Li, H.Z. Gu, X. Gao et al., Setting Factors of Phosphate Bond Forsterite-Vermiculite Composite Material, J. Wuhan Univ. Sci. Technol., 2010, 33(6B), p 559–602
F. Zhou, H.Z. Gu, and C.F. Wang, Preparation and Microstructure of In Situ Gel Modified Expanded Vermiculite, Ceram. Int., 2013, 39(4), p 4075–4079
M. Sutcu, Influence of Expanded Vermiculite on Physical Properties and Thermal Conductivity of Clay Brick, Ceram. Int., 2015, 41(2B), p 2819–2827
J.F. Wang, J.K. Carson, M.F. North, and D.J. Cleland, A New Structural Model of Effective Thermal Conductivity for Heterogeneous Materials with Co-continuous Phases, Int. J. Heat Mass Transf., 2008, 51(9–10), p 2389–2397
N.N. Grishin and O.A. Belogurova, A Thermostable Forsterite Refractory Developed on a Model of Heat Conduction and Thermal Failure of the Refractory Lining, Refract. Ind. Ceram, 2006, 47(3), p 168–170
D. Kunii, Thermal Conductivity of Porous Media by Radiation, J. Jpn. Soc. Mech. Eng., 1962, 65(525), p 1447–1453
D. Kunii and J.M. Smith, Heat Transfer Characteristics of Porous Rocks, J. Am. Inst. Chem. Eng., 1960, 6, p 71–77
H.W. Russell, Principles of Heat Flow in Porous Insulators, J. Am. Ceram. Soc., 1935, 18(1), p 1–5
T. Shimizu, K. Matsuura, H. Furue, and K. Matsuzak, Thermal Conductivity of High Porosity Alumina Refractory Bricks Made by a Slurry Gelation and Foaming Method, J. Eur. Ceram. Soc., 2013, 33(15–16), p 3429–3435
R. Kumar and B. Bhattcsharjee, Porosity, Pore Size Distribution and In Situ Strength of Concrete, Cem. Concr. Res., 2003, 33(1), p 155–164
Acknowledgment
The authors are grateful to the process No. 51204126 of the National Natural Science Foundation of China and No. 2012CB722702 of 973 plans of the National Basic Research Program of China.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, D., Gu, H., Huang, A. et al. Mechanical Strength and Thermal Conductivity of Modified Expanded Vermiculite/Forsterite Composite Materials. J. of Materi Eng and Perform 25, 15–19 (2016). https://doi.org/10.1007/s11665-015-1770-0
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-015-1770-0