Abstract
The long-term durability of ceramics coated glass with high performance should be appropriately evaluated prior to their applications. Fatigue properties of such materials should be clarified to ensure the long-term durability. In this work, a borosilicate glass was coated with single- and two-layered ceramic thin films by a sputtering method. Fatigue tests of coated glass were conducted under bending mode, and fatigue properties of coated glass were investigated. It was revealed that the fatigue life of glass coated with two-layered film became longer compared with those of glass substrate and glass coated single-layered film. Hardness as surface characteristics of coated films, and bending strength as bulk property of coated glass were correlated with the average fatigue life, though no good correlation was found between them. Fatigue resistance strength was proposed as another strength parameter. It was found that the average fatigue life was adequately expressed by a power function of fatigue resistance strength.
Similar content being viewed by others
References
K.H. Kim, K.C. Park, and D.Y. Ma, Structural, Electrical and Optical Properties of Aluminum Doped Zinc Oxide Films Prepared by Radio Frequency Magnetron Sputtering, J. Appl. Phys., 1997, 81, p 7764–7772
Y. Fukuma, H. Asada, N. Nishimura, and T. Koyanagi, Ferromagnetic Properties of IV-VI, Diluted Magnetic Semiconductor Ge1−xMnxTe Films Prepared by Radio Frequency Sputtering, J. Appl. Phys., 2003, 93, p 4034–4039
Y. Peng, C. Park, and D.E. Laughlin, Fe3O4 Thin Films Sputter Deposited from Iron Oxide Targets, J. Appl. Phys., 2003, 93, p 7657–7959
D.A. Chang, P. Lin, and T.Y. Tseng, Optical Properties of ZrTiO4 Films Grown by Radio-Frequency Magnetron Sputtering, J. Appl. Phys., 1995, 77, p 4445–4451
G.T. Kiehne, G.K.L. Wong, and J.B. Ketterson, Optical Second-Harmonic Generation in Sputter-Deposited AlN Films, J. Appl. Phys., 1998, 84, p 5922–5927
H. Mizoguchi, N. Kitamura, K. Fukumi, T. Mihara, J. Nishii, M. Nakamura, N. Kikuchi, H. Hosono, and H. Kawazoe, Optical Properties of SrMoO3 Thin Film, J. Appl. Phys., 2000, 87, p 4617–4619
S. Venkataraj, O. Kapperiz, H. Weis, R. Drese, R. Jayavel, and M. Wuttig, Structural and Optical Properties of Thin Zirconium Oxide Films Prepared by Reactive Direct Current Magnetron Sputtering, J. Appl. Phys., 2002, 92, p 3599–3607
T. Hoshide and M. Hirano, Evaluation of Strength of Borosilicate Glass Coated with Ceramic Materials by Sputtering, J. Mater. Eng. Perform., 2010, 19, p 562–567
T. Hoshide and T. Otomo, Mechanical Properties of Borosilicate Glass Coated with Two-layered Ceramics by Sputtering, J. Mater. Eng. Perform., 2008, 17, p 91–97
T. Hoshide, A. Nebu, and K. Hayashi, Bending Strength of Borosilicate Glass Coated with Alumina and Silicon Carbide by RF Magnetron Sputtering, JSME Int. J. Ser. A, 1998, 41, p 332–337
T. Hoshide, K. Hayashi, T. Saito, K. Katsuki, and T. Inoue, Mechanical Properties of Borosilicate Glass Coated with Alumina by Sputtering Process, Mater. Sci. Res. Int., 1996, 2, p 33–38
T. Hoshide and M. Tanaka, Fatigue Properties of Borosilicate Glass Coated with Ceramics and Effect of Proof testing on Life Distribution, Proc. Eng., 2011, 10, p 740–745
T. Hoshide, Strength Characteristics of Structural Ceramics, Mater. Sci. Res. Int., 1996, 2, p 220–228
P.J. Burnett and D.S. Rickerby, Assessment of Coating Hardness, Surf. Eng., 1987, 3, p 69–76
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hoshide, T., Tanaka, M. & Tsujiai, H. Fatigue Properties of Borosilicate Glass Coated with Two-Layered Ceramic Thin Films. J. of Materi Eng and Perform 22, 1079–1084 (2013). https://doi.org/10.1007/s11665-012-0351-8
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-012-0351-8