Abstract
The embrittlement and softening behavior in simulated heat-affected zones (HAZ) of a newly designed dual-phase DP680 steel for wheel rim applications with different flash allowances were investigated to determine weldability, and offer valuable information for the steel design and its subsequent flash butt welding (FBW). The characterization of microstructure and mechanical performance for the simulated HAZ was conducted by means of optical microscopy, scanning electron microscopy, electron backscatter diffraction, hardness distribution, and Charpy V-notch (CVN) values at selected temperatures. The investigation demonstrates that the toughness of coarse-grained HAZ was kept at an average level of 25.3 J when the prior austenite grain size was controlled to 60.54 μm at a flash allowance of 14 mm (equivalent to heat input of 15.14 kJ/cm based on real welding process), which exhibits the worst toughness when the flash allowance was changed from 4 to 14 mm. Further, with a higher martensite fraction (> 30 pct) in base material (BM), the softening occurs in inter-critical HAZ (ICHAZ) instead of sub-critical HAZ since most of martensite in ICHAZ has decomposed, and the rest ferrite and newly formed bainite with remaining martensite reduce the hardness to a larger extent compared to SCHAZ, whose martensite has only partly decomposed. Even if the softening degree is up to 21.6 pct compared to the BM (average 233 HV0.5), the work hardening during a series of forming processes after FBW has alleviated the softening evidently (work hardening degree > 10 pct). However, the failure location is still in ICHAZ after forming extension which has been confirmed in practical applications of DP680 FBW and subsequent forming processes.
Similar content being viewed by others
References
H. Ashrafi, M. Shamanian, R. Emadi, and N. Saeidi: Mater. Sci. Eng. A, 2017, vol. 680, pp. 197–202.
L. Kascak, E. Spisak, and R. Kubik: MM Sci. J., 2016, vol. 5, pp. 1402–06.
J.F. Wang, L.J. Yang, M.S. Sun, T. Liu, and H. Li: Mater. Des., 2016, vol. 97, pp. 118–25.
J. Wang, Y. Lu, J. Han, J.J. Qi, L. Sun, Z.Y. Jiang, C. Ma, and V. Linton: Int. J. Adv. Manuf. Technol., 2022, vol. 122, pp. 639–58.
J.L. Shen, Z.J. Wei, X.R. Zhu, Y. Liang, Y.L. Liang, F.L. Jiang, and Z.X. Xiao: Mater. Sci. Eng. A, 2018, vol. 718, pp. 34–42.
Z.X. Zhu, J. Han, and H.J. Li: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 5467–75.
J. Wang, C. Ma, J. Han, Z.Y. Jiang, and V. Linton: Mater. Lett., 2021, vol. 303, p. 130511.
P. Lu, Z.X. Xu, K.Y. Jiang, F. Ma, and Y. Shu: J. Mater. Res., 2017, vol. 32, pp. 831–42.
D.C. Saha, E. Biro, A.P. Cerlich, and Y. Zhou: Mater. Lett., 2020, vol. 264, p. 127368.
G. Park, G. Bae, and C. Lee: Metall. Mater. Trans. A, 2019, vol. 50A, pp. 1294–1307.
E. Biro, J.R. McDermid, J.D. Embury, and Y. Zhou: Metall. Mater. Trans. A, 2010, vol. 41A, pp. 2348–56.
M.S. Xia, E. Biro, Z.L. Tian, and Y.N. Zhou: ISIJ Int., 2008, vol. 48, pp. 809–14.
G. Jha, S. Das, A. Lodh, and A. Haldar: Mater. Sci. Eng. A, 2012, vol. 552, pp. 457–63.
L. Ma, J. Han, J. Shen, and S. Hu: Acta Metall. Sin. Engl., 2014, vol. 27(3), pp. 407–15.
T. Taka, K. Kunishige, N. Yamauchi, and N. Nagao: ISIJ Int., 1989, vol. 29, pp. 503–10.
W.J. Chen, H.W. Song, L. Lazarescu, Y. Xu, S.H. Zhang, and D. Banabic: Int. J. Adv. Manuf. Technol., 2020, vol. 110, pp. 1563–73.
C.Y. Xi, D.Q. Sun, Z.Z. Xuan, J.G. Wang, and G.S. Song: Mater. Des., 2016, vol. 96, pp. 506–14.
Z.X. Zhu, J. Han, H.J. Li, and C. Lu: Mater. Lett., 2016, vol. 163, pp. 171–74.
Z.X. Zhu, J. Han, and H.J. Li: Mater. Des., 2015, vol. 88, pp. 1326–33.
Q. Sun, H.S. Di, J.C. Li, and X.N. Wang: Mater. Des., 2015, vol. 105, pp. 201–11.
R.P.S. Sisodia and M. Gaspar: J. Mater. Eng. Perform., 2021, vol. 30(3), pp. 1703–710.
N. Yurioka, M. Okumura, T. Kasuya, and H.J.U. Cotton: Met. Constr., 1987, vol. 19, pp. 217–23.
C.W. Li, W. Wang, T. Han, B. Han, and L.Y. Li: J. Mater. Sci., 2011, vol. 46, pp. 727–33.
D.P. Field: Mater. Sci. Eng. A, 1995, vol. 190, pp. 241–46.
Y.C. Cai, L.S. Zhu, Y. Cui, M.D. Shan, H.J. Li, Y. Xin, and J. Han: Appl. Surf. Sci., 2021, vol. 543, p. 148794.
S.T. Zhang, S. Romo, R.A. Giorjao, P.B.P. Leao, and A.J. Ramirez: Mater. Charact., 2022, vol. 193, p. 112293.
M.G. Jiang, C. Xu, H. Yan, G.H. Fan, T. Nakata, C.S. Lao, R.S. Chen, S. Kamado, E.H. Han, and B.H. Lu: Acta Mater., 2018, vol. 157, pp. 53–71.
E. Biro and A. Lee: Sheet Metal Welding Conference XII, AWS, Livonia, MI, 2006.
E. Biro and A. Lee: Sheet Metal Welding Conference XI, AWS, Sterling Heights, MI, 2006.
J.W. Christian: The Theory of Transformations in Metals and Alloys, Part I, Equilibrium and General Kinetic Theory, 2nd ed. Pergamon Press, Oxford, 1975, pp. 19–20.
P. Lu, Z.X. Xu, and K.Y. Jiang: J. Mater. Res., 2017, vol. 32, pp. 831–42.
R.A. Hardin and C. Beckermann: Metall. Mater. Trans. A, 2013, vol. 44A, p. 5316.
H. Cao, Z. Luo, C. Wang, J. Wang, T. Hu, L. Xiao, and J. Chen: Materials, 2020, vol. 13, p. 3019.
Y. Cai, Y. Cui, S.M. Manladan, L. Zhu, M. Shan, D. Sun, and J. Han: JOM, 2022, vol. 74, pp. 2860–70.
Acknowledgments
The authors would like to thank the support from UOW-HBIS Project (No. IRIS 200506001).
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Han, J., Zhu, L., Wang, J. et al. HAZ Effects in Hot-Rolled Dual-Phase Steel During Flash Butt Welding of Wheel Rims. Metall Mater Trans B 54, 3361–3376 (2023). https://doi.org/10.1007/s11663-023-02914-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-023-02914-1