Abstract
In this study, Mg-Al-Sn alloy was hot compressed at 523 K (250 °C) and annealed at 623 K (350 °C) for various times. The initial as-deformed microstructure was partially dynamic recrystallized with strain-induced precipitates on the recrystallized grain boundaries. After annealing at 623 K (350 °C), static recrystallization (SRX) of the bimodal microstructure took place where, at this temperature, no static precipitates formed. The goal of this work was to study the effect of dynamic precipitation on the texture evolution during the SRX process. Progressive texture evolution was studied during annealing by electron backscattered diffraction technique through a microstructure-tracking process. It was found that the grain-coarsening mechanism during the early stage of annealing is not totally controlled by the basal-oriented grains. Also, it was found that the dynamic precipitates may have significant influence in the early texture weakening during annealing of a bimodal structure.
Similar content being viewed by others
References
B. L. Mordike and T. Ebert: Materials Science and Engineering A, 2001, vol. 302, pp. 37-45.
S. R. Agnew, M. H. Yoo, and C. N. Tome: Acta Materialia, 2001, vol. 49, pp. 4277-4289.
L. W. F. Mackenzie and M. O. Pekguleryuz: Scripta Materialia, 2008, vol. 59, pp. 665-668.
F.J. Humphreys and M. Hatherly: Recrystallization and Related Annealing Phenomena, Elsevier, Oxford, UK. 2004.
E. A. Ball and P. B. Prangnell: Scripta Metallurgica, 1994, vol. 31, pp. 111-116.
L. W. F. Mackenzie, B. Davis, F. J. Humphreys, and G. W. Lorimer: Materials Science and Technology, 2007, vol. 23, pp. 1173-1180.
X. Huang, K. Suzuki, Y. Chino, and M. Mabuchi: Journal of Alloys and Compounds, 2011, vol. 509, pp. 7579-7584.
J. D. Robson, D. T. Henry, and B. Davis: Acta Materialia, 2009, vol. 57, pp. 2739-2747.
X. Y. Yang, Y. K. Zhu, H. Miura, and T. Sakai: Transactions of Nonferrous Metals Society of China, 2010, vol. 20, pp. 1269-1274.
M. R. Barnett: Materials Science Forum, 2003, vol. 419-422, pp. 503.
S. A. Farzadfar, É. Martin, M. Sanjari, E. Essadiqi, and S. Yue: Journal of Materials Science, 2012, vol. 47, pp. 5488-5500.
A. S. H. Kabir, M. Sanjari, J. Su, I.-H. Jung, and S. Yue: Materials Science and Engineering: A, 2014, vol. 616, pp. 252-259.
S. B. Yi, S. Zaefferer, and H. G. Brokmeier: Materials Science and Engineering: A, 2006, vol. 424, pp. 275-281.
A. S. H. Kabir, M. Sanjari, J. Su, I.-H. Jung, and S. Yue, Journal of Materials Science, 2015, 64, pp. 1-10.
M. T. Pérez-Prado and O. A. Ruano: Scripta Materialia, 2003, vol. 48, pp. 59-64.
S. Abdessameud, H. Azzeddine, B. Alili, and D. Bradai, Transactions of Nonferrous Metals Society of China, 2010, vol. 20, pp. 2215-2222.
Acknowledgments
The authors would like to thank General Motors and NSERC, Canada for the financial support.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted January 2, 2016.
Rights and permissions
About this article
Cite this article
Kabir, A.S.H., Su, J. & Yue, S. Texture Evaluation of a Bi-Modal Structure During Static Recrystallization of Hot-Deformed Mg-Al-Sn Alloy. Metall Mater Trans B 47, 3326–3332 (2016). https://doi.org/10.1007/s11663-016-0613-1
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-016-0613-1