Abstract
Al-Ti-B type master alloys have been widely used in the grain refinement of aluminum since 1940s. The introduction of Al3Ti and TiB2(AlB2) particles reduces the grain sizes down to about 200 micrometer level and makes aluminum alloys castable. However, the mechanism for the grain refinement is still not clear, though it is believed that TiB2 particles in the presence of Al3Ti nucleate α-Al grains during solidification. This paper presents our finding on the formation of (Ti,Al)B2 solid solution, which leads to a proposed theory on grain refinement by Al-Ti-B type master alloys that upon addition into aluminum melt stable TiB2 particles react with aluminum slowly and release titanium into the melt. The titanium thus released in combination with titanium in the melt through dissolution of Al3Ti particles maintains a dynamic titanium-rich layer on the surface of (Ti,Al)B2. This layer offers a low crystal mismatch with α-Al and promotes the nucleation of aluminum grains.
Similar content being viewed by others
References
A. Cibula: J. Inst. Metals, 1949-50, vol. 76, p. 321.
L1`. Arnberg, L. Bäckerud, H. Klang: Met. Technol., 1982, vol. 9, pp. 1.
M. Guzowski, G. Sigworth, D. Sentner: Metall. Trans. A, 1987, vol. 18, pp. 603.
G.P. Jones, J. Pearson: Metall. Trans. B, 1976, vol. 7, pp. 223.
D. McCartney: Int. Mater. Rev., 1989, vol. 34, pp. 247.
P. Schumacher, A. Greer, J. Worth, P.V. Evans, M.A. Kearns, P. Fisher, A.H. Green: Mater. Sci. Technol., 1998, vol. 14, pp. 394.
G.K. Sigworth: Metall Trans A, 1984, vol. 15, pp. 277.
M. Easton, D. Stjohn: Metall. Mater. Trans. A, 1999, vol. 30A, pp. 1625.
P. Mohanty, J. Gruzleski: Acta Metall Mater 1995, vol. 43, pp. 2001.
B.D. Cullity: ‘Elements of X-ray diffraction’ 2nd edn, 1978, Addison-Wesley Publishing Company. Reading.
J. Fjellstedt, A.E. Jarfors, L. Svendsen: J. Alloys Compd., 1999, vol. 283, pp. 192.
R.P. Pawlek: in Light Metals, p. 377, TMS, Warrendale, PA, 2010.
A. Cornish: Met. Sci., 1975, vol. 9, pp. 477.
J. Marcantonio, F. Mondolfo: Metall. Trans., 1971, vol. 2, pp. 465.
X. Wang, R. Brydson, A. Jha: in Inst. Phys. Conf. Ser. No. 161, p. 499, Sheffield, IOP Publishing Ltd., 1999.
N.J. Finch: Metall. Trans., 1972, vol. 3, pp. 2709.
A.L. Greer, A.M. Bunn, A. Tronche, P.V. Evans, D.J. Bristow: Acta Mater., 2000, Vol. 48, pp. 2823.
H. Xu, L.D. Xu, S.J. Zhang, Q. Han: Scripta Mater., 2006, vol. 54, pp. 2191.
Acknowledgment
The authors gratefully acknowledge financial support from the National Natural Science Foundation of China (Grant No. 51320105003).
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted September 9, 2014.
Rights and permissions
About this article
Cite this article
Wang, X., Liu, Z., Dai, W. et al. On the Understanding of Aluminum Grain Refinement by Al-Ti-B Type Master Alloys. Metall Mater Trans B 46, 1620–1625 (2015). https://doi.org/10.1007/s11663-014-0252-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-014-0252-3