Abstract
Redox equilibria, activities of cobalt, iron and their oxides in calcium ferrite and calcium ironsilicate slags, were measured through metal-slag-gas equilibrium experiments under controlled oxygen potentials (10−7 to 3 × 10−7 atm) at 1573 K. Results on the redox equilibria show that addition of CoO to calcium ferrite slag increases the equilibrium Fe3+/Fe2+ ratio in these melts. Measured activities of CoO and FeO showed positive deviations from ideal behavior, while that of Fe2O3 showed negative deviation. Partial substitution of CaO by SiO2, by up to 4 wt pct SiO2 in the calcium ferrite based melts, resulted in increases in the activity coefficients of CoO and Fe2O3. Phase equilibria studies on the cobalt containing CaO-FeO-Fe2O3-SiO2 slags were also carried out using the drop-quench technique. Good agreement between the activity data and the liquidus temperature with respect to magnetite solid solution containing CoO was observed.
Similar content being viewed by others
References
B. Clarke: in Co-Products and Minor Elements in Non-Ferrous Smelting, T. Lehner, ed., TMS-AIME, Warrendale, PA, 1995, pp. 97–107.
K.C. Teague, D.R. Swinbourne, and S. Jahanshahi: AusIMM Proc., 1998, No. 1, pp. 53–58.
M. Somerville, T. Norgate, P. Jefferies, A. Vecchio-Sadus, and S. Jahanshahi: Copper 99-Cobre 99 Int. Conf., TMS, Warrendale, PA, 1999, vol. IV, pp. 15–33.
A. Yazawa, Y. Takeda, and Y. Waseda: Can. Metall. Q., 1981, vol. 20 (2), pp. 129–34.
Y. Takeda, S. Ishiwata, and A. Yazawa: Trans. JIM, 1983, vol. 24 (7), pp. 518–28.
M. Nagamori, Y. Takeda, and A. Yazawa: Met. Rev. MMIJ, 1989, vol. 6 (1), pp. 6–21.
A. Katyal and J.H.E. Jeffes: 3rd Int. Conf. on Molten Slags and Fluxes, Glasgow, 1989, Institute of Metals, London, pp. 46–55.
L.S. Darken and R.W. Gurry: J. Am. Chem. Soc., 1945, vol. 67, pp. 1398–1412.
E.J. Grimsey and X. Liu: Metall. Mater. Trans. B, 1995, vol. 26B, pp. 229–34.
S.S. Wang, N.H. Santander, and J.M. Toguri: Metall. Trans., 1974, vol. 5, pp. 261–65.
R.S. Young: Chemical Analysis in Extractive Metallurgy, Charles Griffin and Company Limited, London, 1971, pp. 172–87.
M. Timucin and A.E. Morris: Trans. AIME, 1970, vol. 1, pp. 3193–3201.
R. Rait: Ph.D. Thesis, University of Melbourne, Melbourne, 1997.
B. Phillips and A. Muan: J. Am. Ceram. Soc., 1959, vol. 42, pp. 413–23.
O. Knacke, O. Kubaschewski, and K. Hesselmann: Thermochemical Properties of Inorganic Substances, Springer-Verlag, Berlin, 1991.
E.T. Turkdogan: Physical Chemistry of High Temperature Technology, Academic Press, Sydney, 1980, pp. 5–10.
G. Gudmundsson and J.R. Holloway: Am. Mineral., 1993, vol. 78 (1–2), pp. 178–86.
R.W. Taylor and A. Muan: Trans. AIME, 1962, vol. 224, pp. 500–02.
E.F. Heald: Trans. AIME, 1967, vol. 239 (9), pp. 1337–40.
K. Schwerdtfeger and A. Muan: ACTA Metallurgica, 1964, vol. 12, pp. 905–09.
J. Vrestal: Kovove Materially, 1976, vol. 14 (6), pp. 625–35.
L.S. Darken: Trans. AIME, 1967, vol. 239 (1), pp. 90–96.
T. Oishi, K. Ono, and J. Morijama: J. Jpn. Inst. Met., 1981, vol. 45, pp. 1126–31.
S. Wright: Report No. 92/11, unpublished; Report No. 756, CSIRO Minerals, Clayton South, Australia, 1993, pp. 27–28.
H. Larson and J. Chipman: Trans. AIME, 1953, vol. 197, pp. 1089–96.
C. Bodsworth: J. Iron Steel Inst., 1959, 193, pp. 13–24.
E.F. Osborn and A. Muan: Phase Equilibria amongst Oxides in Steel Making, Addison-Wesley Publishing Co. Inc., Reading, MA, 1965, pp. 113–14.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Teague, K.C., Swinbourne, D.R. & Jahanshahi, S. A thermodynamic study on cobalt containing calcium ferrite and calcium iron silicate slags at 1573 K. Metall Mater Trans B 32, 47–54 (2001). https://doi.org/10.1007/s11663-001-0007-9
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11663-001-0007-9