Effect of different stages of tensile deformation on micromagnetic parameters in high-strength, low-alloy steel

  • Published:
Metallurgical and Materials Transactions A Aims and scope Submit manuscript

Abstract

The influence of tensile deformation on the magnetic Barkhausen emissions (MBE) and hysteresis loop has been studied in a high-strength, low-alloy steel (HSLA) and its weldment. The magnetic measurements were made both in loaded and unloaded conditions for different stress levels. The rootmean-square (RMS) voltage of the MBE has been used for analysis. This study shows that the preyield and postyield deformation can be identified from the change in the the MBE profile. The initial elastic deformation showed a linear increase in the MBE level in the loaded condition, and the MBE level remained constant in the unloaded condition. The microplastic yielding, well below the macroyield stress, significantly reduces the MBE, indicating the operation of grain-boundary dislocation sources below the macroyield stress. This is indicated by the slow increase in the MBE level in the loaded condition and the decrease in the MBE level in the unloaded condition. The macroyielding resulted in a significant increase in the MBE level in the loaded condition and, more clearly, in the unloaded condition. The increase in the MBE level during macroyielding has been attributed to the grain rotation phenomenon, in order to maintain the boundary integrity between adjacent grains, which would preferentially align the magnetic domains along the stress direction. With progressive plastic deformation, the MBE level remains more or less constant in the loaded condition and decreases linearly with strain in the unloaded condition. This constant MBE behavior in the loaded condition is attributed to the opposing effect of applied tensile stress (which tends to align the domains along the stress direction) and the dislocation density (which reduces the domain-wall displacement). The decreasing MBE in the unloaded condition is attributed to the combined effect of compressive residual stress at the surface layers (which tends to align the domain wall perpendicular to the stress direction) and the dislocation density. This study shows that MBE during tensile deformation can be classified into four stages: (1) perfectly elastic, (2) microplastic yielding, (3) macroyielding, and (4) progressive plastic deformation. A multimagnetic parameter approach, combining the hysteresis loop and MBE, has been suggested to evaluate the residual stresses.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

We’re sorry, something doesn't seem to be working properly.

Please try refreshing the page. If that doesn't work, please contact support so we can address the problem.

References

  1. S. Tiitto: Acta Polytechnica Scandinavica, Appl. Phys. Ser., 1977, vol. 119, pp. 1–80.

    Google Scholar 

  2. D.J. Buttle, C.B. Scruby, J.P. Jakubovics, and G.A.D. Briggs: Phil. Mag. A, 1987, vol. 55A (6), pp. 717–34.

    Google Scholar 

  3. C. Gatelier-rothea, P. Fleischmann, J. Chicois, and R. Fougeres: Nondestr. Testing Eval., 1992, vols. 8–9, pp. 591–602.

    Google Scholar 

  4. J. Kameda and R. Ranjan: Acta Metall., 1987, vol. 35 (7), pp. 1515–26.

    Article  CAS  Google Scholar 

  5. V. Moorthy, S. Vaidyanathan, T. Jayakumar, and Baldev Raj: J. Magnetism Magnetic Mater., 1997, vol. 171, pp. 179–89.

    Article  CAS  Google Scholar 

  6. Baldev Raj, V. Moorthy, and S. Vaidyanathan: Mater. Eval., 1997, vol. 55 (1), pp. 81–84.

    CAS  Google Scholar 

  7. V. Moorthy, S. Vaidyanathan, T. Jayakumar, and Baldev Raj: Phil. Mag. A, 1998, vol. 77 (6), pp. 1499–1514.

    Article  CAS  Google Scholar 

  8. D.J. Buttle, C.B. Scruby, G.A.D. Briggs, and J. Jakubovics: Proc. R. Soc. London, 1987, vol. 414A, pp. 469–97.

    Google Scholar 

  9. R. Rautioaho, L.P. Karjalainen, and M. Moilanen: J. Magnetism Magnetic Mater., 1988, vol. 73, pp. 96–102.

    Article  CAS  Google Scholar 

  10. L.P. Karjalainen and M. Moilanen: NDT Int., 1979, vol. 12 (2), pp. 51–55.

    Article  CAS  Google Scholar 

  11. R. Langman: NDT Int., 1987, vol. 20 (2), pp. 93–99.

    Article  Google Scholar 

  12. A.K. Sengupta and W.A. Theiner: Mater. Eval., 1995, vol. 53 (5), pp. 554–61.

    CAS  Google Scholar 

  13. S.M. Thompson and B.K. Tanner: J. Magnetism Magnetic Mater., 1994, vol. 132, pp. 71–88.

    Article  CAS  Google Scholar 

  14. D.C. Jiles: J. Phys. D, 1988, vol. 21, pp. 1196–1204.

    Article  CAS  Google Scholar 

  15. T. Vreeland, D.S. Wood, and D.S. Clark: Acta Metall., 1953, vol. 1, pp. 414–21.

    Article  CAS  Google Scholar 

  16. V. Moorthy, S. Vaidyanathan, K. Laha, T. Jayakumar, K. Bhanu Sankara Rao, and Baldev Raj: Mater. Sci. Eng., 1997, vol. 231A, pp. 98–104.

    Google Scholar 

  17. B.D. Cullity: Introduction to Magnetic Material, 1st ed., Addison-Wesley, Reading, MA, 1972, pp. 320–25.

    Google Scholar 

  18. B.D. Cullity: J. Appl. Phys., 1964, vol. 35, pp. 1915–19.

    Article  Google Scholar 

  19. V. Moorthy, S. Vaidyanathan, T. Jayakumar, and Baldev Raj: Acta Mater., in press.

Download references

Author information

Authors and Affiliations

Authors

Rights and permissions

Reprints and permissions

About this article

Cite this article

Vaidyanathan, S., Moorthy, V., Kalyanasundaram, P. et al. Effect of different stages of tensile deformation on micromagnetic parameters in high-strength, low-alloy steel. Metall Mater Trans A 30, 2067–2072 (1999). https://doi.org/10.1007/s11661-999-0017-9

Download citation

  • Received:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11661-999-0017-9

Keywords

Navigation