Effect of Processing Parameters on Plastic Flow and Defect Formation in Friction-Stir-Welded Aluminum Alloy

Article
  • 2 Downloads

Abstract

The effect of processing parameters on material flow and defect formation during friction stir welding (FSW) was investigated on 6.0-mm-thick 2014Al-T6 rolled plates with an artificially thickened oxide layer on the butt surface as the marker material. It was found that the “S” line in the stir zone (SZ) rotated with the pin and stayed on the retreating side (RS) and advancing side (AS) at low and high heat inputs, respectively. When the tool rotation rate was extremely low, the oxide layer under the pin moved to the RS first and then to the AS perpendicular to the welding direction, rather than rotating with the pin. The material flow was driven by the shear stresses produced by the forces at the pin–workpiece interface. With increases of the rotation rate, the depth of the shoulder-affected zone (SAZ) first decreased and then increased due to the decreasing shoulder friction force and increasing heat input. Insufficient material flow appeared in the whole of the SZ at low rotation rates and in the bottom of the SZ at high rotation rates, resulting in the formation of the “S” line. The extremely inadequate material flow is the reason for the lack of penetration and the kissing bonds in the bottom of the SZ at extremely low and low rotation rates, respectively.

Notes

Acknowledgment

This work was supported by the National Natural Science Foundation of China under Grant No. 51331008.

References

  1. 1.
    W.M. Thomas, E.D. Nicholas, J.C. Needham, M.G. Murch, P. Templesmith, and C.J. Dawes, G.B. Patent Application No.9125978.8, 1991.Google Scholar
  2. 2.
    R.S. Mishra and Z.Y. Ma: Mater. Sci. Eng. R, 2005, vol. 50, pp. 1–78.CrossRefGoogle Scholar
  3. 3.
    S. Ji, Z. Li, Z. Zhou and B. Wu: J. Mater. Eng. Perform., 2017, vol. 26, pp. 5085–96.CrossRefGoogle Scholar
  4. 4.
    Z.Y. Ma: Metall. Mater. Trans. A, 2008, vol. 39A, pp. 642–58.CrossRefGoogle Scholar
  5. 5.
    D. Zhemchuzhnikova, S. Mironov and R. Kaibyshev: Metall. Mater. Trans. A, 2016, vol. 48A, pp. 150–58.Google Scholar
  6. 6.
    X.C. Liu and C.S. Wu: Mater. Des., 2016, vol. 90, pp. 350–58.CrossRefGoogle Scholar
  7. 7.
    Y. Tao, Z. Zhang, D.R. Ni, D. Wang, B.L. Xiao and Z.Y. Ma: Mater. Sci. Eng. A, 2014, vol. 612, pp. 236–45.CrossRefGoogle Scholar
  8. 8.
    W.J. Arbegast: Scr. Mater., 2008, vol. 58, pp. 372–76.CrossRefGoogle Scholar
  9. 9.
    Z. Zhu, M. Wang, H. Zhang, X. Zhang, T. Yu and Z. Wu: Metals, 2017, vol. 7, pp. 256–571.CrossRefGoogle Scholar
  10. 10.
    P. Heurtier, M.J. Jonesb, C. Desrayauda, J.H. Driver, F. Montheillet and D. Allehauxc: J. Mater. Process. Technol., 2006, vol. 171, pp. 348–57.CrossRefGoogle Scholar
  11. 11.
    J.A. Schneider and A.C. Nunes: Metall. Mater. Trans. B, 2004, vol. 35B, pp. 777–83.CrossRefGoogle Scholar
  12. 12.
    F. Simoes and D.M. Rodrigues: Mater. Des., 2014, vol. 59, pp. 344–51.CrossRefGoogle Scholar
  13. 13.
    Z. Zhang, B.L. Xiao, D. Wang and Z.Y. Ma: Metall. Mater. Trans. A, 2010, vol. 42A, pp. 1717–26.Google Scholar
  14. 14.
    J.H. Yan, M.A. Sutton and A.P. Reynolds: Sci. Technol. Weld. Join., 2005, vol. 10, pp. 725–36.CrossRefGoogle Scholar
  15. 15.
    S.W. Xu and X.M. Deng: Acta Mater., 2008, vol. 56, pp. 1326–41.CrossRefGoogle Scholar
  16. 16.
    Y. Pan and D.A. Lados: Metall. Mater. Trans. A, 2017, vol. 48A, pp. 1708–26.CrossRefGoogle Scholar
  17. 17.
    K. Colligan: Weld. J., 1999, vol. 78, pp. 229–37.Google Scholar
  18. 18.
    Y. Morisada, H. Fujii, Y. Kawahito, K. Nakata and M. Tanaka: Scr. Mater., 2011, vol. 65, pp. 1085–88.CrossRefGoogle Scholar
  19. 19.
    X.C. Liu, C.S. Wu and G.K. Padhy: Scr. Mater., 2015, vol. 102, pp. 95–98.CrossRefGoogle Scholar
  20. 20.
    H.N.B. Schmidt, T.L. Dickerson and J.H. Hattel: Acta Mater., 2006, vol. 54, pp. 1199–1209.CrossRefGoogle Scholar
  21. 21.
    P. Pourahmad, M. Abbasi and T. Nonferr: Metal. Soc., 2013, vol. 23, pp. 1253–61.Google Scholar
  22. 22.
    Y. Shimoda, M. Tsubaki, T. Yasui, M. Fukumoto, T. Fujita and J. Osawa: Steel. Res. Int., 2010, vol. 81, pp. 1108–11.Google Scholar
  23. 23.
    M. Fukumoto, M. Tsubaki, T. Yasui and K. Miyagawa: Steel. Res. Int., 2010, vol. 81, pp. 1096–99.Google Scholar
  24. 24.
    Y. S. Sato, F. Yamashita, Y. Sugiura, S. H. C. Park and H. Kokawa: Scr. Mater., 2004, vol. 50, pp. 365–69.CrossRefGoogle Scholar
  25. 25.
    S.S. Di, X.Q. Yang, D.P. Fang and G.H. Luan: Mater. Chem. Phys., 2007, vol. 104, pp. 244–48.CrossRefGoogle Scholar
  26. 26.
    Y.S. Sato, H. Takauchi, S.H.C. Park and H. Kokawa: Mater. Sci. Eng. A, 2005, vol. 405, pp. 333–38.CrossRefGoogle Scholar
  27. 27.
    Z. Zhang, B.L. Xiao and Z.Y. Ma: Metall. Mater. Trans. A, 2013, vol. 44A, pp. 4081–97.CrossRefGoogle Scholar
  28. 28.
    Z. Zhang, B.L. Xiao and Z.Y. Ma: Mater. Sci. Eng. A, 2005, vol. 614, pp. 6–15.CrossRefGoogle Scholar
  29. 29.
    K. Ramanjaneyulu, G. M. Reddy and A. V. Rao: Trans. Indian Inst. Met., 2014, vol. 67, pp. 769–80.CrossRefGoogle Scholar
  30. 30.
    A.K. Kadian and P. Biswas: J. Mater. Eng. Perform., 2015, vol. 24, pp. 4119–27.CrossRefGoogle Scholar
  31. 31.
    A.K. Kadian and P. Biswas, J. Manuf. Process., 2017, vol. 26, pp. 382–92.CrossRefGoogle Scholar
  32. 32.
    Z. Zhang and H.W. Zhang: J. Mater. Process. Technol., 2009, vol. 209, pp. 241–70.CrossRefGoogle Scholar
  33. 33.
    Z.W. Chen, T. P. Sang and Y. Qi: Mater. Sci. Eng. A, 2008, vol. 474, pp. 312–16.CrossRefGoogle Scholar
  34. 34.
    D.K. Yaduwanshi, S. Bag and S. Pal: Mater. Des., 2016, vol. 92, pp. 166–83.CrossRefGoogle Scholar
  35. 35.
    Y.C. Lin, J. J. Liu and J. N. Chen: Exp. Mech., 2013, vol. 53, pp. 1573–82.CrossRefGoogle Scholar
  36. 36.
    M. Mehta, K. Chatterjee and A. De: Sci. Technol. Weld. Joining, 2013, vol. 18, pp. 191–97.CrossRefGoogle Scholar
  37. 37.
    Q. Li and M. Lovell: J. Mater. Process. Technol., 2005, vol. 160, pp. 245–56.CrossRefGoogle Scholar
  38. 38.
    Z.Y. Ma, S.R. Sharma and R.S. Mishra: Mater. Sci. Eng. A, 2006, vol. 422, pp. 269–78.CrossRefGoogle Scholar
  39. 39.
    X.X. Zhang, B.L. Xiao and Z.Y. Ma: Metall. Mater. Trans. A, 2011, vol. 42, pp. 3218–28.CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society and ASM International 2018

Authors and Affiliations

  1. 1.Institute of Metal Research, Chinese Academy of SciencesShenyang National Laboratory for Materials ScienceShenyangPeople’s Republic of China
  2. 2.University of Chinese Academy of SciencesBeijingChina

Personalised recommendations