Effects of Nb Modification and Cooling Rate on the Microstructure in an Ultrahigh Carbon Steel

  • Matthew D. Hecht
  • Bryan A. Webler
  • Yoosuf N. Picard
Article
  • 15 Downloads

Abstract

In this study, two different melting methods were used to investigate effects of Nb modification on microstructure in ultrahigh carbon steel (UHCS). Nb-free and Nb-modified UHCS samples were produced by melting and resolidifying an industrially produced base UHCS with and without addition of Nb powder. Microstructure was characterized using scanning electron microscopy, X-ray diffraction, and electron dispersive spectroscopy. Equilibrium computations of phase fractions and compositions were utilized to help describe microstructural changes caused by the Nb additions. Nb combined with C to form NbC structures before and during austenite solidification, reducing the effective amount of carbon available for the other phases. Cementite network spacing in the Nb-free samples was controlled by the cooling rate during solidification (faster cooling led to a more refined network). Network spacing in the Nb-modified UHCS could be enlarged by NbC structures that formed cooperatively with austenite.

Notes

Acknowledgments

The authors appreciate Miller Centrifugal Casting for providing the mill roll parts for this study. This project was financed in part by a grant from the Commonwealth of Pennsylvania Department of Community and Economic Development (DCED), Developed in PA Program (D2PA). Funding support is also acknowledged from the National Science Foundation, CMMI Award No. 1436064. The authors acknowledge use of the Materials Characterization Facility at Carnegie Mellon University supported by Grant MCF-677785.

References

  1. 1.
    D.R. Lesuer, C.K. Syn, A. Goldberg, J. Wadsworth, and O.D. Sherby: JOM, 1993, vol. 45, pp. 40–46.CrossRefGoogle Scholar
  2. 2.
    M.D. Hecht, B.A. Webler, and Y.N. Picard: Mater. Charact., 2016, vol. 117, pp. 134–43.CrossRefGoogle Scholar
  3. 3.
    B. Walser and O.D. Sherby: Metall. Trans. A, 1979, vol. 10, pp. 1461–71.CrossRefGoogle Scholar
  4. 4.
    M.A. Hamidzadeh, M. Meratian, and A. Saatchi: Mater. Sci. Eng. A, 2013, vol. 571, pp. 193–98.CrossRefGoogle Scholar
  5. 5.
    M.A. Hamidzadeh, M. Meratian, and M. Mohammadi Zahrani: Mater. Sci. Eng. A, 2012, vol. 556, pp. 758–66.CrossRefGoogle Scholar
  6. 6.
    G.D. de Almeida Soares, L.H. de Almeida, T.L. da Silveira, and I. Le May: Mater. Charact., 1992, vol. 29, pp. 387–96.CrossRefGoogle Scholar
  7. 7.
    A. Noorian, S. Kheirandish, and H. Saghafian: Iran. J. Mater. Sci. Eng., 2010, vol. 7, pp. 22–29.Google Scholar
  8. 8.
    B.A. Migachev: Met. Sci. Heat Treat., 2001, vol. 43, pp. 103–6.CrossRefGoogle Scholar
  9. 9.
    C. He-Xing, C. Zhe-Chuan, L. Jin-Cai, and L. Huai-Tao: Wear, 1993, vol. 166, pp. 197–201.CrossRefGoogle Scholar
  10. 10.
    X. Zhi, J. Xing, H. Fu, and B. Xiao: Mater. Lett., 2008, vol. 62, pp. 857–60.CrossRefGoogle Scholar
  11. 11.
    H. Mohrbacher: Materials Science and Technology Conference and Exhibition 2011, MS & T’11. Materials Science and Technology Conference and Exhibition 2011, MS & T’11. Columbus, OH, USA, 16–20 October 2011. pp. 434–45.Google Scholar
  12. 12.
    M.E. Maja, M.G. Maruma, L.A. Mampuru, and S.J. Moema: J. South. African Inst. Min. Metall., 2016, vol. 116, pp. 981–86.CrossRefGoogle Scholar
  13. 13.
    M. Fiset, K. Peev, and M. Radulovic: J. Mater. Sci. Lett., 1993, vol. 12, pp. 615–17.CrossRefGoogle Scholar
  14. 14.
    M.D. Hecht, Y.N. Picard, and B.A. Webler: Metall. Mater. Trans. A, 2017, vol. 48, pp. 2320–35.CrossRefGoogle Scholar
  15. 15.
    M.D. Abràmoff, P.J. Magalhães, and S.J. Ram: Biophotonics Int., 2004, vol. 11, pp. 36–42.Google Scholar
  16. 16.
    R. Powell, T. Holland, and B. Worley: J. Metamorph. Geol., 1998, vol. 16, pp. 577–88.CrossRefGoogle Scholar
  17. 17.
    K.G. Buchanan and M. V. Kral: Metall. Mater. Trans. A , 2012, vol. 43, pp. 1760–69.CrossRefGoogle Scholar
  18. 18.
    F. Haddad, S.E. Amara, R. Kesri, and S. Hamar-Thibault: J. Phys. IV Fr., 2004, vol. 122, pp. 35–39.CrossRefGoogle Scholar
  19. 19.
    E.E. Underwood: J. Microsc., 1969, vol. 89, pp. 161–80.CrossRefGoogle Scholar
  20. 20.
    J. Wang, P. van der Wolk, and S. van der Zwaag: Mater. Trans. JIM, 2000, vol. 41, pp. 761–68.CrossRefGoogle Scholar
  21. 21.
    Y.M. Won and B.G. Thomas: Metall. Mater. Trans. A, 2001, vol. 32, pp. 1755–67.CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society and ASM International 2018

Authors and Affiliations

  • Matthew D. Hecht
    • 1
  • Bryan A. Webler
    • 1
  • Yoosuf N. Picard
    • 1
  1. 1.Materials Science and EngineeringCarnegie Mellon UniversityPittsburghUSA

Personalised recommendations