Factors Affecting the Inclusion Potency for Acicular Ferrite Nucleation in High-Strength Steel Welds
- 421 Downloads
Factors affecting the inclusion potency for acicular ferrite nucleation in high-strength weld metals were investigated and the contribution of each factor was qualitatively evaluated. Two kinds of weld metals with different hardenabilities were prepared, in both, MnTi2O4-rich spinel formed as the predominant inclusion phase. To evaluate the factors determining the inclusion potency, the inclusion characteristics of size, phase distribution in the multiphase inclusion, orientation relationship with ferrite, and Mn distribution near the inclusion were analyzed. Three factors affecting the ferrite nucleation potency of inclusions were evaluated: the Baker–Nutting (B–N) orientation relationship between ferrite and the inclusion; the formation of an Mn-depleted zone (MDZ) near the inclusion; and the strain energy around the inclusion. Among these, the first two factors were found to be the most important. In addition, it was concluded that the increased chemical driving force brought about by the formation of an MDZ contributed more to the formation of acicular ferrite in higher-strength weld metals, because the B–N orientation relationship between ferrite and the inclusion was less likely to form as the transformation temperature decreased.
KeywordsFerrite Austenite Bainite Weld Metal Orientation Relationship
The work was supported by the Fundamental R&D Program for the Core Technology of Materials (K0006030, Development of joining materials by the control of phase transformation and critical energy) funded by the Ministry of Trade, Industry & Energy (MI, Korea), and by Fundamental Research Program of the Korean Institute of Materials Science (KIMS).
- 5. D.P. Fairchild, M.L. Macia, N.V. Bangaru and J.Y. Koo: Int. J. Offshore Polar Eng., 2004, vol. 14, pp. 18-28.Google Scholar
- 6. P.T. Oldland, C.W. Ramsay, D.K. Matlock and D.L. Olson: Weld. J., 1989, vol. 68, pp. 158s-68s.Google Scholar
- 19. S. Aihara, G. Shigesato, M. Sugiyama and R. Uemori: Nippon Steel Tech. Rep. No. 91, 2005, pp. 43-48.Google Scholar
- 24. A.G. Glover, J.T. McGrath, M.J. Tinkler and G.C. Weatherly: Weld. J., 1977, vol. 56, pp. 267s-73s.Google Scholar
- 28. K. Poorhaydari, B.M. Patchett and D.G. Ivey: Weld. J., 2005, vol. 84, pp. 149s-55s.Google Scholar
- 31. J.-H. Kang and S.-H. Kim: Kor. J. Met. Mater., 2010, vol. 48, pp. 730-40.Google Scholar
- 40. T. Pan, Z. Yang, B. Bai and H. Fang: Acta Metall. Sinica, 2003, vol. 39, pp. 1037-42.Google Scholar
- 42. A.R. Tanna and H.H. Joshi: World Academy of Science, Engineering and Technology, 2013, vol. 7, pp. 334-41.Google Scholar