Abstract
Intermetallic Ni-Al coatings on the Ni substrate were prepared by the mechanical alloying (MA) method in mechanical activators of vibratory and planetary type. It was found that coatings that were fabricated in a high-energy (planetary) activator in comparison with those fabricated in a low-energy (vibratory) activator are more homogeneous, have higher density, and experience better adhesion to the substrate. It was shown that different intermetallic phases (NiAl, NiAl3, and Ni2Al3) can form directly during the MA treatment in the planetary activator.
Similar content being viewed by others
Notes
SPEX is a trademark of SPEX SamplePrep, LLC, Metuchen, NJ.
References
T. Czeppe and S. Wierzbinski: Int. J. Mech. Sci., 2000, vol. 42, pp. 1499–1518.
C. Sierra and A.J. Vázquez: Surf. Coat. Technol., 2006, vol. 200, pp. 4383–88.
G. Prévot, D. Schmausa, and S. Le Moal: Surf. Sci., 2010, vol. 604, pp. 770–77.
H. Guo, Y. Cui, H. Peng, and S. Gong: Corros. Sci., 2010, vol. 52, pp. 1440–46.
S.D. Kaloshkin, Y. Hayasaka, Z. Sagdoldina, S.V. Komarov, N. Hayashi, and E. Kasai: J. Alloys Compd., 2009, vol. 483, pp. 386–88.
S. Romankov, S. Kaloshkin, Y. Hayasaka, N. Hayashi, E. Kasai, and S.V. Komarov: J. Alloys Compd., 2009, vol. 484, pp. 665–73.
S. Romankov, S.V. Komarov, E. Vdovichenko, Y. Hayasaka, N. Hayashi, S.D. Kaloshkin, and E. Kasai: Int. J. Refract. Met. Hard Mater., 2009, vol. 27, pp. 492–97.
Z. Zhana, Y. He, D. Wang, and W. Gao: Intermetallics, 2006, vol. 14, pp. 75–81.
W. Hu, M. Li, and M. Fukumoto: Mater. Sci. Eng. A, 2008, vol. 478, pp. 1–8.
G. Gupta, K. Mondal, and R. Balasubramaniam: J. Alloys Compd., 2009, vol. 482, pp. 118–22.
B. Li, R. Ding, Y. Shen, Y. Hu, and Y. Guo: Mater. Des., 2012, vol. 35, pp. 25–36.
I. Farahbakhsh, A. Zakeri, P. Manikandan, and K. Hokamoto: Appl. Surf. Sci., 2011, vol. 257, pp. 2830–37.
R. Pouriamanesh, J. Vahdati-Khaki, and Q. Mohammadi: J. Alloys Compd., 2009, vol. 488, pp. 430–36.
S.K. Pabi and B.S. Murty: Mater. Sci. Eng., 1996, vol. A214, pp. 146–52.
V.K. Portnoy, A.M. Blinov, I.A. Tomilin, V.N. Kuznetsov, and T. Kulik: J. Alloys Compd., 2002, vol. 336, pp. 196–201.
V. Zadorozhnyy, S. Kaloshkin, E. Kaevitser, and S. Romankov: J. Alloys Compd., 2011, vol. 509S, pp. S507–S509.
Y.D. Yagodkin and S.V. Dobyatkin: Inorgan. Mater., 2008, vol. 44, pp. 1520–30.
T. Chen, J.M. Hampikian, and N.N. Thadhani: Acta Mater., 1999, vol. 47, pp. 2567–79.
E.V. Shelekhov, V.V. Tcherdyntsev, L.Y. Pustov, S.D. Kaloshkin, and I.A. Tomilin: Mater. Sci. Forum, 2000, vols. 343–346, pp. 603–08.
L. Yu. Pustov, S.D. Kaloshkin, V.V. Tcherdyntsev, I.A. Tomilin, E.V. Shelekhov, and A.I. Salimon: Mater. Sci. Forum, 2001, vols. 360–363, pp. 373–78.
E.V. Shelekhov, V.V. Tcherdyntsev, L.Y. Pustov, S.D. Kaloshkin, and I.A. Tomilin: NATO Sci. Ser. 3: High Technol., 2000, vol. 80, pp. 139–45.
Y.S. Kwon, K.B. Gerasimov, and S.K. Yoon: J. Alloys Compd., 2002, vol. 346, pp. 276–81.
A.E. Kudryashov, E.I. Zamulaeva, P.V. Vakaev, E.A. Levashov, and T.A. Sviridova: Non-Ferrous Met., 2002, vol. 9, pp. 73–79.
Acknowledgments
This work was done in the frame of the federal target program “Scientific and scientific-pedagogical personnel of innovative Russia,” Proposal No. 2012-1.2.1-12-000-4004-005 and RFBR Grant No. 11-08-00450-a.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted May 12, 2012.
Rights and permissions
About this article
Cite this article
Zadorozhnyy, V.Y., Kaloshkin, S.D., Churyukanova, M.N. et al. Formation of Intermetallic Ni-Al Coatings by Mechanical Alloying with Different Intensities. Metall Mater Trans A 44, 1779–1784 (2013). https://doi.org/10.1007/s11661-012-1544-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-012-1544-3