Study of the fusion zone and heat-affected zone microstructures in tungsten inert gas-welded INCONEL 738LC superalloy

  • Published:
Metallurgical and Materials Transactions A Aims and scope Submit manuscript

Abstract

The fusion zone and heat-affected zone (HAZ) microstructures obtained during tungsten inert gas (TIG) welding of a commercial superalloy IN 738LC were examined. The microsegregation observed during solidification in the fusion zone indicated that while Co, Cr, and W segregated to the γ dendrites, Nb, Ti, Ta, Mo, Al, and Zr were rejected into the interdendritic liquid. Electron diffraction and energy-dispersive X-ray microanalyses using a transmission electron microscope (TEM) of secondary phases, extracted from the fusion zone on carbon replicas, and of those in thin foils prepared from the fusion zone showed that the major secondary solidification constituents, formed from the interdendritic liquid, were cubic MC-type carbides and γ-γ’ eutectic. The terminal solidification reaction product was found to consist of M3B2 and Ni7Zr2 formed in front of the interdendritic γ-γ’ eutectic. Based on the knowledge of the Ni-Ti-C ternary system, a pseudoternary solidification diagram was adapted for IN 738 superalloy, which adequately explained the as-solidified microstructure. The HAZ microfissuring was observed in regions surrounding the fusion zone. Closer and careful microstructural examination by analytical scanning electron microscopy revealed formation of re-solidified constituents along the microfissured HAZ grain boundaries, which suggest that HAZ cracking in this alloy involves liquation cracking. Liquation of various phases present in preweld alloy as well as characteristics of the intergranular liquid film contributing to the alloy’s low resistance to HAZ cracking were identified and are discussed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. M.J. Strum, L.T. Summers, and J.W. Morris, Jr.: Welding J., 1983, vol. 62, pp. 235-S–42-S.

    Google Scholar 

  2. S.A. David, J.M. Vitek, S.S. Babu, L.A. Boatner, and R.W. Reed: Sci. Technol. Welding Joining, 1997, vol. 2 (2), pp. 79–88.

    CAS  Google Scholar 

  3. S.S. Babu, S.A. David, and J.M. Vitek, and M.K. Miller: J. Phys. IV, 1996, vol. 6 (C5), pp. 253–58.

    CAS  Google Scholar 

  4. R. Nakkalil, N.L. Richards, and M.C. Chaturvedi: Scripta Metall., 1992, vol. 26, pp. 545–50.

    Article  CAS  Google Scholar 

  5. M. Prager and C.S. Shira: Welding Res. Council Bull., 1968, No. 128.

  6. M.H. Haafkens and G.H. Matthey: Welding J., 1982, vol. 61, pp. 25–30.

    CAS  Google Scholar 

  7. W.A. Owczarski, D.S. Duvall, and C.P. Sullvan: Welding J., 1966, vol. 45, pp. 145S-55S.

    CAS  Google Scholar 

  8. L.C. Lim, J.Z. Yi, N. Liu, and Q. Ma: Mater. Sci. Technol., 2002, vol. 18, pp. 407–12.

    Article  CAS  Google Scholar 

  9. O.A. Ojo, N.L. Richards, and M.C. Chaturvedi: Mater. Sci. Technol., 2004, vol. 20, pp. 1027–34.

    Article  CAS  Google Scholar 

  10. O.A. Ojo, N.L. Richards, and M.C. Chaturvedi: J. Mater. Sci., 2004, vol. 39, pp. 7401–04.

    Article  CAS  Google Scholar 

  11. R. Rosenthal and D.R.F. West: Mater. Sci. Technol., 1999, vol. 15, pp. 1387–94.

    CAS  Google Scholar 

  12. P.N. Quested and M. McLean: Conf. on Solidification Technology in the Foundry and Cast House, The Metals Society, London, 1980, pp. 586–91.

    Google Scholar 

  13. P.R. Sahm and F. Schubert: Proc. Conf. on Solidification and Casting of Metals, Sheffield, England, 1979, pp. 389–400.

  14. T.E. Bower, H.D. Brody, and M.C. Flemings: Trans. AIME, 1966, vol. 236, pp. 615–24.

    Google Scholar 

  15. E. Scheil: Z. Metallkd., 1942, vol. 34, pp. 70–75.

    Google Scholar 

  16. J.N. DuPont, C.V. Robino, A.R. Marder, and M.R. Notis: Metall. Mater. Trans. A, 1998, vol. 29A, pp. 2797–2806.

    Article  CAS  Google Scholar 

  17. R. Nakkalil, N.L. Richards, and M.C. Chaturvedi: Metall. Trans. A, 1993, vol. 24A, pp. 1169–79.

    CAS  Google Scholar 

  18. M.J. Cieslak, J.J. Stephens, and M.J. Carr: Metall. Trans. A, 1988, vol. 19A, pp. 657–67.

    CAS  Google Scholar 

  19. M. Taha and W. Kurz: Z. Metallkd. 1981, vol. 72, pp. 546–49.

    CAS  Google Scholar 

  20. M.C. Flemings: Solidification Processing, McGraw-Hill, New York, NY, 1974.

    Google Scholar 

  21. G.A. Knornovsky, M.J. Cieslak, T.J. Headley, A.D. Romig, Jr., and W.F. Hammetter: Metall. Trans. A, 1989, vol. 20A, pp. 2149–58.

    Google Scholar 

  22. R.G. Thompson, D.E. Mayo, and B. Radhakrishann: Metall. Trans. A, 1991, vol. 22A, pp. 557–67.

    CAS  Google Scholar 

  23. Y. Nakao and K. Shinozaki: Proc. Intl. Conf. on High Temperature Materials, Liege, Belgium, 1990, pp. 24–27.

    Google Scholar 

  24. Y. Zhu, S. Zhang, L. Xu, B. Jing, H. Zhuangqi, and C. Shi: Superalloys. TMS-AIME, Warrendale, PA, 1988, pp. 703–12.

    Google Scholar 

  25. R. Vincent: Acta Metall., 1985, vol. 33, pp. 1205–16.

    Article  CAS  Google Scholar 

  26. P. Nash and C.S. Jayanth: Bull. Alloy Phase Diagrams, 1984, vol. 5, p. 144.

    CAS  Google Scholar 

  27. G.H. Chen and C. Chen: Scripta Metall. Meter., 1992, vol. 27, pp. 121–26.

    Article  CAS  Google Scholar 

  28. E. Samuelsson, P.W. Keefe, and R.W. Furgason: Proc. Superalloys Conf. 1992, S.D. Antolovich, R.W. Stusrud, R.A. Mackay, D.L. Anton, T. Khan, R.D. Kissinger, and D.L. Klarstrom, eds., TMS, Warrendale, PA, 1992, pp. 361–70.

    Google Scholar 

  29. Z. Yunrong, W. Yuping, X. Jizhou, P. Caron, and T. Khan: Proc. Superalloys Conf. 1988, S. Reichman, D.N. Duhi, G. Maurer, S. Antolovich, and C. Lund, eds., TMS-AIME, Warrendale, PA, 1988, pp. 335–44.

    Google Scholar 

  30. Y. Murata and N. Yukawa: Scripta Metall., 1986, vol. 20, pp. 693–96.

    Article  CAS  Google Scholar 

  31. R. Sellamuthu and A.F. Giamei: Metall. Trans. A, 1986, vol. 17A, pp. 419–28.

    CAS  Google Scholar 

  32. A.J. Baldan: Mater. Sci. 1990, vol. 25, pp. 4341–48.

    Article  CAS  Google Scholar 

  33. L. Backerud, B. Carlsson, R. Oskarsson, and M. Mikus: Scand. J. Metall., 1976, vol. 3, pp. 225–35.

    Google Scholar 

  34. P. Willemin and M. Durand-Charre: J. Mater. Sci., 1990, vol. 25, pp. 168–74.

    Article  CAS  Google Scholar 

  35. M.J. Starink, H. Cama, and R.C. Thomson: Scripta Mater., 1998, vol. 38, pp. 73–80.

    CAS  Google Scholar 

  36. B. Radhakrishnan and R.G. Thompson: Metall. Trans. A, 1991, vol. 22A, pp. 887–902.

    CAS  Google Scholar 

  37. F.N. Rhines: Phase Diagrams in Metallurgy, McGraw-Hill Book Co., New York, NY, 1956.

    Google Scholar 

  38. D.L. Sponseller: Superalloys Conf., Mineral, Metals, and Materials Society, Champion, PA, 1996, pp. 259–70.

    Google Scholar 

  39. N. Yukawa, Y. Murata, and T. Noda: Superalloys Conf., Metallurgical Society of AIME, Champion, PA, 1984, pp. 83–92.

    Google Scholar 

  40. J.J. Pepe and W.F. Savage: Welding J., 1967, vol. 46, p. 411-s.

  41. J. Lecomte-Beckers: Metall. Trans. A, 1988, vol. 19A, p. 2333.

    CAS  Google Scholar 

  42. O.A. Ojo, N.L. Richards, and M.C. Chaturvedi: Scripta Mater., 2004, vol. 51, pp. 141–46.

    Article  CAS  Google Scholar 

  43. M.J. Cieslak: Welding J., 1991, vol. 70, pp. 49S-56S.

    Google Scholar 

  44. G. Bailey and H. Watkins: J. Inst. Met., 1951, vol. 80, pp. 57–76.

    CAS  Google Scholar 

  45. I.A. Aksay, C.E. Hoge, and J.A. Pask: J. Phys. Chem., 1974, vol. 78, pp. 1178–86.

    Article  CAS  Google Scholar 

  46. R. Nakkalil, N.L. Richards, and M.C. Chaturvedi: Acta Metall. Mater., 1993, vol. 41, pp. 3381–92.

    Article  CAS  Google Scholar 

  47. Y. Zhu, S. Zhang, T. Zhang, J. Zhang, Z. Hu, X. Xie, and C. Shi: Superalloys, 1992, TMS, Warrendale, PA, 1992, pp. 145–54.

    Google Scholar 

  48. J. Zou, H.P. Wang, R. Doherty, and E.M. Perry: Proc. Superalloys Conf. 1992, S.D. Antolovich, R.W. Stusrud, R.A. Mackay, D.L. Anton, T. Khan, R.D. Kissinger, and D.L. Klarstrom, eds., TMS, Warrendale, PA, 1992, pp. 165–74.

    Google Scholar 

  49. K. Masubuchi: J. Met., 1981, vol. 33, pp. 19–23.

    CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. the Department of Mechanical and Manufacturing Engineering, University of Manitoba, R3T 5V6, Winnipeg, MB, Canada

    O. A. Ojo (Postdoctoral Fellow), N. L. Richards (Professor) & M. C. Chaturvedi (Distinguished Professor and Canada Research Chair)

Authors
  1. O. A. Ojo
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. N. L. Richards
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. M. C. Chaturvedi
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Ojo, O.A., Richards, N.L. & Chaturvedi, M.C. Study of the fusion zone and heat-affected zone microstructures in tungsten inert gas-welded INCONEL 738LC superalloy. Metall Mater Trans A 37, 421–433 (2006). https://doi.org/10.1007/s11661-006-0013-2

Download citation

  • Received:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11661-006-0013-2

Keywords

Search

Navigation