Abstract
The effect of withdrawal rate on hot tearing or solidification cracking during directional solidification (DS) was explored. High withdrawal rates were found to reduce the hot tearing tendency. There is a general refinement of the microstructure when the withdrawal rate is increased. First, the dendrite arm spacing appears smaller. Second, the columnar grain size is reduced. Third, the remaining liquid is finely dispersed and increasingly discontinuous. Finally, a more uniform distribution of strain is obtained because of the presence of more grain boundaries, and grain boundary cohesion becomes stronger due to the elimination of continuous liquid films. The reduced hot tearing susceptibility is attributed to the uniform distribution of strain and stronger grain boundary cohesion.
Similar content being viewed by others
References
M. Mclean: Directional Solidified Materials for High Temperature Service, Metals Society, London, 1983, pp. 5–53.
G.K. Sigworth: AFS Trans., 1996, vol. 155, pp. 1053–62.
J. Campbell: Castings, Butterworth-Heinemann Ltd., London, 1991, pp. 219–29.
D.N. Duhl and C.P. Sullivan: J. Met., 1971, vol. 23 (7), pp. 38–40.
J.E. Doherty, B.H. Kear, and A.F. Giamei: J. Met., 1971, vol. 23 (11), pp. 59–62.
C.T. Sims, N.S. Stoloff, and W.C. Hagel: Superalloys II, John Wiley & Sons, New York, NY, 1987, pp. 121–29.
K. Heck, J.R. Blackford, and R.F. Singer: Mater. Sci. Technol., 1999, vol. 15, pp. 213–20.
C.Q. Sun, Q.J. Li, C.X. Wu, S.F. Tian, and J.F. Radavich: in Superalloys 1996, R.D. Kissinger, D.J. Deye, D.L. Anton, A.D. Cetel, M.V. Nathal, T.M. Pollock, and D.A. Woodford, eds., TMS, Warrendale, PA, 1996, pp. 507–13.
T.L. Lin, S.H. Huang, and C.Q. Sun: in Superalloys 1988, S. Reichman, D.N. Duhl, G. Maurer, S. Antolovich, and C. Lund, eds., TMS, Warrendale, PA, 1988, pp. 345–54.
T.W. Clyne and G.J. Davies: Br. Foundrymen, 1981, vol. 74, pp. 65–73.
M. Rappaz, J.M. Drezet, and M. Gremaud: Metall. Mater. Trans. A, 1999, vol. 30A, pp. 449–55.
J.M. Drezet: J. Phys. IV France, 1999, vol. 9, pp. 53–62.
H.F. Bishop, C.G. Ackerlind, and W.S. Pellini: AFS Trans., 1957, vol. 65, pp. 247–58.
J. Zhang and R.F. Singer: Acta Mater., 2002, vol. 50, pp. 1869–79.
J. Zhang and R.F. Singer: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 1337–42.
J. Zhang and R.F. Singer: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 939–46.
M. Rappaz, A. Jacot, and W.J. Boettinger: Metall. Mater. Trans. A, 2003, vol. 34A, pp. 467–79.
J. Zhang and R.F. Singer: Z. Metallkd., 2002, vol. 93, pp. 806–11.
W. Kurz and D.J. Fisher: Acta Metall., 1981, vol. 29, pp. 11–20.
M.G. Ardakani, N. D’Souza, A. Wagner, B.A. Shollock, and M. McLean: in Superalloys 2000, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. McLean, S. Olson, and J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 219–28.
Y.X. Zhu, S.N. Zhang, T.X. Zhang, J.H. Zhang, Z.Q. Hu, X.S. Xie, and C.X. Shi: in Superalloys 1992, S.D. Antolovich, R.W. Stusrud, R.A. MacKay, D.L. Anton, T. Khan, R.D. Kissinger, and D.L. Klarstrom, eds., TMS, Warrendale, PA, 1992, pp. 145–54.
Y.X. Zhu, J.F. Radavich, Z. Zheng, X.Z. Ning, L.H. Lou, X.S. Xie, and C.X. Shi: in Superalloys 2000, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. McLean, S. Olson, and J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 329–39.
A. Lohmüller, W. Esser, J. Grossmann, M. Hördler, J. Preuhs, and R.F. Singer: in Superalloys 2000, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. McLean, S. Olson, and J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 181–88.
M. Konter, E. Kats, and N. Hofmann: in Superalloys 2000, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. McLean, S. Olson, and J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 189–95.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Zhou, Y., Volek, A. & Singer, R.F. Influence of solidification conditions on the castability of nickel-base superalloy IN792. Metall Mater Trans A 36, 651–656 (2005). https://doi.org/10.1007/s11661-005-0181-5
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-005-0181-5