Effects of temperature and shot peening on S-N behavior of a PM Ni-base superalloy UDIMET 720

  • Published:
Metallurgical and Materials Transactions A Aims and scope Submit manuscript

Abstract

Fatigue S-N (stress vs life) curve behavior for a powder metallurgy (PM) Ni-base superalloy UDIMET 720 in both polished and shot-peened surface conditions was investigated at room temperature and 600 °C in air. Tests were carried out under four-point bending at a load ratio of 0.1 and a frequency of 10 Hz. At 600 °C, an offset S-N curve was found for both polished and shot-peened surface conditions. This offset S-N curve is deduced to be controlled by the location of crack nucleation sites. Observations and deductions of crack nucleation sites, crack nucleation life, crack closure, environmental attack, and cyclic softening and hardening have been used to explain the experimental results.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. J.F. Knott: Fracture and Fracture Mechanics, Case Studies: 2nd Nat. Conf. on Fracture, R.B. Tait and G.G. Garrett, eds., 26–27 November 1984, Johannesburg, UK, Pergamon Press, Oxford, England, 1985, pp. 297–315.

    Google Scholar 

  2. T. Denda, P.L. Bretz, and K. Tien: Metall. Trans. A, 1992, vol. 23A, pp. 519–26.

    CAS  Google Scholar 

  3. D. Foumier and A. Pineau: Metall. Trans. A, 1977, vol. 8A, pp. 1095–1105.

    Google Scholar 

  4. S.D. Antolovich, S. Liu, and R. Baur: Metall. Trans. A, 1981, vol. 12A, pp. 473–81.

    Google Scholar 

  5. V. Singh, M. Sundararaman, W. Chen, and R.P. Wahi: Metall. Trans. A, 1991, vol. 22A, pp. 499–506.

    CAS  Google Scholar 

  6. M. Sundararaman, W. Chen, V. Singh, and R.P. Wahi: Acta Metall. Mater., 1990, vol. 38, pp. 1813–22.

    Article  CAS  Google Scholar 

  7. B.A. Lerch and V. Gerold: Metall. Trans. A, 1987, vol. 18A, pp. 2135–41.

    CAS  Google Scholar 

  8. R.E. Stoltz and A.G. Pineau: Mater. Sci. Eng., 1978, vol. 34, pp. 275–84.

    Article  CAS  Google Scholar 

  9. L.G. Fritzeneier and G.K. Tien: Acta Metall., 1988, vol. 36 (2), pp. 275–82.

    Article  Google Scholar 

  10. S. Bashir, P. Taupin, and S.D. Antolovich: Metall. Trans. A, 1975, vol. 10A, pp. 1481–90.

    Google Scholar 

  11. A. Saxen and S.D. Antolovich: Metall. Trans. A, 1975, vol. 6A, pp. 1809–28.

    Google Scholar 

  12. B. Lerch and V. Gerold: Acta Metall., 1985., vol. 33 (9), pp. 1709–16.

    Article  CAS  Google Scholar 

  13. H.F. Merrick: Metall. Trans. A, 1974, vol. 5, pp. 891–97.

    Article  CAS  Google Scholar 

  14. C.H. Wells and C.P. Sullivan: Trans. ASM, 1964, vol. 57, pp. 841–55.

    CAS  Google Scholar 

  15. C.H. Wells and C.P. Sullivan: Trans. ASM, 1965, vol. 58, pp. 391–402.

    CAS  Google Scholar 

  16. W. Renzhi: Fatigue Eng. Mater. Struct., 1979, vol. 2, pp. 413–18.

    Article  Google Scholar 

  17. G.H. Farrahi, J.L. Lebrun, and D. Couratin: Fatigue Fract. Eng. Mater. Struct., 1995, vol. 18 (2), pp. 211–20.

    Article  CAS  Google Scholar 

  18. Y. Mutoh, G.H. Fair, B. Noble, and R.B. Waterhouse: Fatigue Fract. Eng. Mater. Struct., 1987, vol. 10 (4), pp. 261–72.

    Article  Google Scholar 

  19. F.S. Ahmed: Modelling, Measurement and Control C: Ener., Chem., Earth, Environ. Biomed. Problems, 1995, vol. 47 (1–3), pp. 29–42.

    CAS  Google Scholar 

  20. J.F. Janowak and A. Alagarsamy: AFS Trans., 1990, vol. 98, pp. 511–18.

    CAS  Google Scholar 

  21. J.L. Doong, J.R. Hwang, and H.S. Chen: J. Mater. Sci., 1986, vol. 21, pp. 871–78.

    Article  CAS  Google Scholar 

  22. D.W. Becker and J.A. Psihoyious: ASME— Int. Combus. Engine Div. (publ.) ICE, 05–07 October 1986, Oakbrook, IL, USA, ASME Press, NY, USA, 1986, vol. 1, pp. 59–64.

    Google Scholar 

  23. K. Saruki, A. Yamada, and K. Ogawa: J. Soc. Mater. Jpn., 1988, vol. 37 (417), pp. 631–36.

    CAS  Google Scholar 

  24. H. Suzuki, A. Magata, W.M. Gong, and Y. Ito: Trans. Jpn. Soc. Mech. Eng., Part A, 1995, vol. 61 (591), pp. 2349–54.

    Google Scholar 

  25. H. Suzuki, K. Ito, S. Nishino, S. Yamada, and M. Moriya: Trans. Jpn. Soc. Mech. Eng., Part A, 1996, vol. 62 (595), pp. 627–31.

    Google Scholar 

  26. L.N. Ojha and M.C. Sharma: Fatigue 96—Proc. Int. Fatigue Congr., Berlin, G. Lütjering, and H. Nowack, eds., 6–10 May 1996, Berlin, Germany, Pergamon, Tarrytown, NY, USA, 1996, vol. 2, pp. 1433–36.

  27. D.R. Chang, D.D. Krueger, and R.A. Sprague: Superalloys 1984—Proc. 5th Int. Symp. on Superalloys, M. Gell, C.S. Kortovich, R.H. Bricknell, W.B. Kent, and J.F. Radavich, eds., 7–11 October 1984, Seven Springs, PA, USA, TMS-AIME, Warrendale, PA, USA, 1984, pp. 245–73.

  28. P. Forget, M. Jeandin and A. Lyoret: EUROMAT 93—3rd Eur. Conf. on Advanced Materials and Processes 8–10 June 1993, P.K.L. 20, Paris, Journal De Physique IV, Colloque C7, vol. 2, November 1993, pp. 322–26.

  29. H. Qi and X.R. Jing: Int. J. Fatigue, 1991., vol. 13 (4), pp. 322–26.

    Article  Google Scholar 

  30. F.E. Sczerzenie and G.E. Maurer: Superalloys 1984—Proc. 5th Int. Symp. on Superalloys, M. Gell, C.S. Kortovich, R.H. Bricknell., W.B. Kent, and J.F. Radavich, eds., 7–11 October 1984, Seven Springs, PA, USA, TMS-AIME, Warrendale, PA, USA, 1984, pp. 575–82.

  31. K.R. Bain, M.L. Gambone, J.M. Hyzak, and M.C. Thomas: Superalloys 1988—Proc. 6th Int. Symp. on Superalloys, D.N. Duhl, G. Maurer, S. Antolovich, C. Lund, and S. Reichman, eds., 18–22 September 1988. Champion, PA, USA, TMS-AIME, Warrendale, PA, USA, 1988, pp. 13–22.

  32. P.S. Prevey: in Shot Peening Theory and Application, J.S. Eckersley and J. Champeigne, eds., IITT-International, Gournay-Sur-Marne, France, 1991, pp. 81–93.

    Google Scholar 

  33. J. Luo and P. Bowen: Int. J. Fatigue, 2004, vol. 26, pp. 113–24.

    Article  CAS  Google Scholar 

  34. P.A.S. Reed, W.F. Gale, and J.E. King: Mater. Sci. Technol., 1993, vol. 9, pp. 281–87.

    CAS  Google Scholar 

  35. J.E. King: Fatigue Eng. Mater. Struct., 1981, vol. 4, pp. 311–20.

    Article  CAS  Google Scholar 

  36. J.E. King: Met. Sci., 1982, vol. 16, pp. 345–55.

    Article  Google Scholar 

  37. H. Ghonem, T. Nicholas, and A. Pineau: ASTM-AD Publ., 1991, vol. 21, pp. 1–18.

    Google Scholar 

  38. H. Ghonem and D. Zheng: Mater. Sci. Eng., 1992, vol. 150A, pp. 151–60.

    Google Scholar 

  39. D. Zheng and H. Ghonem: Metall Trans. A, 1992, vol. 23A, pp. 3169–71.

    CAS  Google Scholar 

  40. H. Teranishi and A.J. McEvily: Metall. Trans. A, 1979, vol. 10A, pp. 1806–08.

    CAS  Google Scholar 

  41. C.E. Shamblen and D.R. Chang: Metall. Trans. B, 1985, vol. 16B, pp. 775–84.

    CAS  Google Scholar 

  42. S. Bashir and S.D. Antolovich: Superalloys 1984—Proc. 5th Int. Symp. on Superalloys, M. Gell, C.S. Kortovich, R.H. Bricknell, W.B. Kent, and J.F. Radavich, eds., 7–11 October 1984, Seven Springs, PA, USA, TMS-AIME, Warrendale, PA, USA, 1984, pp. 295–307.

  43. P. Woollin and J.F. Knott: Fatigue 87-3rd Int. Conf. on Fatigue and Fatigue Thresholds, R.O. Ritchie and E.A. Starke, eds., EMAS, Charlottesville, VA, 1987, pp. 1087–99.

    Google Scholar 

  44. J. Luo and P. Bowen: Acta Mater., 2003, vol. 51, pp. 3521–35.

    Article  CAS  Google Scholar 

  45. P. Neumann: Acta Metall., 1974, vol. 22, pp. 1167–78.

    Article  Google Scholar 

  46. J.F. Knott: Fatigue Crack Growth: 30 Years of Progress—Proc. Conf. on Fatigue Crack Growth, R.A. Smith, ed., Pergamon, Cambridge, United Kingdom, 1984, pp. 31–52.

    Google Scholar 

  47. D.L. Davidson and S.J. Hudak, Jr.: Metall. Mater. Trans. A. 1995, vol. 26A, pp. 2247–57.

    Article  CAS  Google Scholar 

  48. J. Luo and P. Bowen: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3719–30.

    Article  CAS  Google Scholar 

  49. J. Luo and P. Bowen: Acta Mater., 2003, vol. 51, pp. 3537–50.

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Metallurgy and Materials, The University of Birmingham, Edgbaston, BIS 2TT, Birmingham, UK

    J. Luo (Research Fellow) & P. Bowen (Head)

Authors
  1. J. Luo
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. P. Bowen
    View author publications

    You can also search for this author in PubMed Google Scholar

Rights and permissions

Reprints and permissions

About this article

Cite this article

Luo, J., Bowen, P. Effects of temperature and shot peening on S-N behavior of a PM Ni-base superalloy UDIMET 720. Metall Mater Trans A 35, 1007–1016 (2004). https://doi.org/10.1007/s11661-004-1004-9

Download citation

  • Received:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11661-004-1004-9

Keywords

Search

Navigation