Plasma electrolytic oxidation (PEO) coatings were formed on 7075 aluminum alloy in silicateborate based electrolyte with different duty cycles. The physical and chemical properties of the PEO coatings were thoroughly investigated. The wearing and corrosion properties of the coatings were evaluated by wearing experiments and potentiodynamic polarization tests, respectively. The results showed that the micro-hardness of the coatings first increased and then decreased with the increasing duty cycle. As a results, the wearing resistance of the coatings first increased and then decreased with the increasing duty cycle. Composition analysis proved that the coatings were mainly composed of α-Al2O3 and γ-Al2O3. The presence of wear scars on the worn surface morphology demonstrates that the three-body rolling was the main wear mechanism for coated specimen. The corrosion study showed that the coating formed in the mixed electrolyte with duty cycle of 80% showed the most superior corrosion resistance.
Similar content being viewed by others
References
Wen L, Wang Y, Zhou Y, et al. Corrosion Evaluation of Microarc Oxidation Coatings Formed on 2024 Aluminium Alloy[J]. Corros. Sci., 2010, 52(8): 2687–2696
Ding H Y, Dai Z D, Skuiry S C, et al. Corrosion Wear Behaviors of Micro-arc Oxidation Coating of Al2O3 on 2024Al in Different Aqueous Environments at Fretting Contact[J]. Tribol. Int., 2010, 43(5–6): 868–875
Zhang Y, Fan W, Du H Q, et al. Microstructure and Wearing Properties of PEO Coatings: Effects of and TiO2[J]. Surf. Rev. Lett., 2018, 25(1): 1850102
Jiang Y, Zhang Y, Bao Y, et al. Sliding Wear Behavior of Plasma Electrolytic Oxidation Coating on Pure Aluminium[J]. Wear, 2011, 271(9–10): 1667–1670
Wang W B, Dong P, Wang H Y, et al. Synergistic Corrosion Inhibition Effect of Molybdate and Phosphate Ions for Anodic Oxidation Film Formed on 2024 Aluminum Alloy[J]. J. Wuhan Univ. Technol., 2018, 32(7): 426–432
Sui Y W, Chen X, Wang R, et al. Wear Behavior of In-situ TiC Particles Reinforced Aluminum Matrix Composite[J]. J. Wuhan Univ. Technol., 2017, 32(7): 552–556
Xiang N, Song R G, Zhao J, et al. Microstructure and Mechanical Properties of Ceramic Coatings Formed on 6063 Aluminium Alloy by Micro-arc Oxidation[J]. Trans. Nonferrous Met. Soc. China, 2015, 25(10): 3323–3328
Lv G, Gu W, Chen H, et al. Characteristic of Ceramic Coatings on Aluminum by Plasma Electrolytic Oxidation in Silicate and Phosphate Electrolyte[J]. Appl. Surf. Sci., 2006, 253(5): 2947–2952
Lukiyanchuk I V, Rudnev V S, Kuryavyi V G, et al. Surface Morphology, Composition and Thermal Behavior of Tungsten-containing Anodic Spark Coatings on Aluminium Alloy[J]. Thin Solid Films, 2016, 446(1): 54–60
Xiang N, Song R G, Xiang B, et al. A Study on Photocatalytic Activity of Micro-arc Oxidation TiO2 Films and Ag+/MAO-TiO2 Composite Films[J]. Appl. Surf. Sci., 2015, 347(30): 454–460
Xiang N, Song R G, Li H, et al. Study on Microstructure and Electrochemical Corrosion Behavior of PEO Coatings Formed on Aluminum Alloy[J]. J. Mater. Eng. Perform., 2015, 24(12): 5022–5031
Lim TS, Ryu HS, Hong SH. Electrochemical Corrosion Properties of CeO2-containing Coatings on AZ31 Magnesium Alloys Prepared by Plasma Electrolytic Oxidation[J]. Corr. Sci., 2012, 62(9): 104–111
Bayati M R, Golestani-Fard F, Moshfegh A Z. Visible Photodecomposition of Methylene Blue over Micro Arc Oxidized WO3-loaded TiO2 Nano-porous Layers[J]. Appl. Catal. A, 2010, 382(2): 322–331
Wang J H, Wang J, Lu Y, et al. Effects of Single Pulse Energy on the Properties of Ceramic Coating Prepared by Micro-arc Oxidation on Ti Alloy[J]. Appl. Surf. Sci., 2015, 324(1): 405–413
Tadića N. S., Stojadinovića S, Radićb N, et al. Characterization and Photocatalytic Properties of Tungsten Doped TiO2 Coatings on Aluminum Obtained by Plasma Electrolytic Oxidation[J]. Surf. Coat. Tech., 2016, 305(11): 192–199
Wang X, Zhu Z, Li Y, et al. Characterization of Micro-arc Oxidation Coatings on 6N01 Aluminum Alloy Under Different Electrolyte Temperature Control Modes[J]. J. Mater. Eng. Perform., 2018, 27(4): 1–8
Yu C, Cui L Y, Zhou Y F, et al. Self-degradation of Micro-arc Oxidation/Chitosan Composite Coating on Mg-4Li-1Ca Alloy[J]. Surf. Coat. Technol., 2018, 344(6): 1–11
Xiang N, Song R G, Zhuang J J, et al. Effects of Current Density on Microstructure and Properties of Plasma Electrolytic Oxidation Ceramic Coatings Formed on 6063 Aluminum Alloy[J]. Trans. Nonferrous Met. Soc. China, 2016, 26(3): 806–813
Dehnavi V, Luan B L, Shoesmith D W, et al. Effect of Duty Cycle and Applied Current Frequency on Plasma Electrolytic Oxidation (PEO) Coating Growth Behavior[J]. Surf. Coat. Technol., 2013, 226(7): 100–107
Stojadinovic S, Vasilic R, Belca I, et al. Characterization of the Plasma Electrolytic Oxidation of Aluminium in Sodium Tungstate[J]. Corros. Sci., 2010, 52(10): 3258–3265
Zhou X, Thompson G E, Skeldon P, et al. Film Formation and Detachment during Anodizing of Al-Mg Alloys[J]. Corros. Sci., 1999, 41(8): 1599–1613
Liu F, Xu J, Wang F, et al. Biomimetic Deposition of Apatite Coatings on Micro-arc Oxidation Treated Biomedical NiTi Alloy[J]. Sur. Coat. Technol., 2010, 204(20): 3294–3299
Sabatini G, Ceschini L, Martini C, et al. Improving Sliding and Abrasive Wear Behaviour of Cast A356 and Wrought AA7075 Aluminium Alloys by Plasma Electrolytic Oxidation[J]. Mater. Design, 2010, 31(2): 816–828
Srinivasan P B, Liang J, Blawert C, et al. Characterization of Calcium Containing Plasma Electrolytic Oxidation Coatings on AM50 Magnesium Alloy[J]. Appl. Surf. Sci., 2010, 256(12): 4017–4022
Liang J, Srinivasan P B, Blawert C, et al. Comparison of Electrochemical Corrosion Behaviour of MgO and ZrO2 Coatings on AM50 Magnesium Alloy Formed by Plasma Electrolytic Oxidation[J]. Corros. Sci., 2009, 51(10): 2483–2492
Zhang R F, Zhang S F, Shen Y L, et al. Influence of Sodium Borate Concentration on Properties of Anodic Coatings Obtained by Micro Arc Oxidation on Magnesium Alloys[J]. Appl. Surf. Sci., 2012, 258(17): 6602–6610
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the National Natural Science Foundation of China (No. 11802117), the Natural Science Foundation of the Jiangsu Higher Education Institutions of China (No. 19KJB430024), the Science Foundation of the Jiangsu Industrial Software Engineering Research Center (No. ZK190401)
Rights and permissions
About this article
Cite this article
Shi, Y., Wang, Y., Cheng, C. et al. Properties and Structure of PEO Treated Aluminum Alloy. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 36, 424–432 (2021). https://doi.org/10.1007/s11595-021-2426-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-021-2426-6