AFM-tip-induced crystallization of poly(ethylene oxide) melt droplets
- 78 Downloads
The AFM-tip-induced crystallization of poly(ethylene oxide) (PEO) melt droplets was studied. The melt droplets with a height of 50–100 nm and a lateral size of 2–3 μm were obtained by melting the PEO ultra-thin films on a mica surface. For the PEO samples with average molecular weights (M n) ranging from 1.0 × 103 g/mol to 1.0 × 104 g/mol, the lateral perturbation from the AFM tip in the hard-tapping or nanoscratch modes could not induce the growth of the flat-on lamellae. In contrast, under AFM nanoindentation mode, the tip-induced crystallization occurred when a sufficiently high vertical tip force was applied to the melt droplets of PEO with M n ⩾ 1.0 × 104 g/mol. Moreover, the experimental results indicated that the AFM-tip-induced crystallization of PEO in the nanoindentation process had molecular weight dependence.
Keywordsatomic force microscopy poly(ethylene oxide) tip-induced crystallization nanoindentation
Unable to display preview. Download preview PDF.
- 3.Vancso G J, Beekmans L G, Pearce R, Trifonova D, Varga J. From microns to nanometers: Morphology development in semicrystalline polymers by scanning force microscopy. J Macromol Sci Phys, 1999, B38: 491–503Google Scholar