Abstract
Nanocrystalline ZnO was prepared with ZnCl2·2H2O and (NH4)2CO3 as raw materials by direct precipitation method. The precursor was proved to be [Zn5(OH)6(CO3)2] by TG-DTG-DTA and IR analysis. This precursor was calcined at 300°C for 1, 2 and 3 hours respectively, and then the nanocrystalline ZnO of different grain size were obtained. The nanocrystalline ZnO was characterized using X-ray diffraction (XRD), TEM and Brunner-Emmett-Teller method (BET). Experimental results for nanocrystalline ZnO showed that the minimum size was about 8nm, the maximum was about 15 nm and the mean grain size was 12 nm, the surface area was 80.56 m2/g and the purity was 99.9% when the precursor was calcined at 300°C for 2 h.
Similar content being viewed by others
References
Yan Zifeng, Nanocrystalline catalytic technology, Beijing: Chemical Industrial Press, 2003, 68
Gong Hengxiang, He Yunyao, Wang Qifeng, Jin Guojuan, Fang Zebo and Wang Yinyue, Polycrystalline ZnO films deposited on glass by RF reactive sputtering, Semicond. Photonics & Technol., 2004, 10(2): 97–100
Zhang Xitang, Zhuang Jiaqi, Xu Jinjie, Xie Tengfeng, Wang Dejun, Bai Yubai, Li Tiejin, Yao Jiannian. Studies of surface photovoltage spectnoscopy on quantum-sized ZnO nanoparticles, Chem J Chin Univ, 1999, 20(12): 1945–1947
Xian Caijun, Nanocrystalline build material, Beijing: Chemical Industrial Press, 2003, 50–51
Deng H.M., Ding J., Shi Y., Liu X.Y. and Wang J., Ultrafine Zinc oxide powders prepared by precipitation/mechanical milling, J. Mater. Sci., 2001, 36: 3273–3276
Gao Lian, Li Wei. Nanocrystalline ceramics, Beijing: Chemical Industrial Press, 2002, 45–48
Yu Baolong, Zhang Guilan, Tang Guoqing, Wu Xiaochun and Chen Wenju, Electronic spin resonance properties of ZnO nanocrystalline, Acta Physico-Chimica Sinica, 1995, 11(7): 587–589 (in Chinese)
Chen Yifeng, Tang Motang, Yang Shenghai, Zhang Baoping and Yang Jianguang, Preparation of Tetrapod-like ZnO Whiskers from Waste Hot Dipping Zinc, J.Cent.South Univ. Technol., 2004, 11(1): 51–54
Jing Liqiang, Xu Zili, Shang Jing, Sun Xiaojun, Cai Weimin, Guo Haichen, The preparation and characterization of ZnO ultrafine particles, Mater. Sci. & Eng., 2002, 332(7): 356–362
Lu Qingfeng, Wei Hongxiang, Hu Zhudong, ZnO Nanoneedles Fabricated by a Simple Approach and Their Optical Properties, Trans. Nonferrous Met. Soc. China, 2004, 14(5): 973–976
Yang Weizhong, Zhou Dali, Yin Guangfu, Wang Runsheng and Zhang Yun, Characterization of ZnO Based Varistor Derived from Nano ZnO Powders and Ultrafine Dopants, J.Mater. Sci. Technol., 2005, 21(2): 183–186
Chen Sihai, Ren Xinmin, Mechanism study on the formation of ZnO nanoparticle in ethanol solution, Acta Physico-Chimica Sinica, 1999, 11(2): 171–174 (in Chinese)
Wang Wenliang, Li Dongsheng, Hou Xiangyang, Shi Zhenmin, Wang Jiwu and Zhou Caihua, Ultrasonic Radiation Precipitation Preparation and Characterization on Nanocrystalline Zinc Oxide, Chem. Res. & Appl., 2001, 13(2): 157–159 (in Chinese)
Xu Jiaqiang, Pan Qingyi, Sun Yuan and Li Zhanchai, Emulsion Synthesis Microstructure and Gas Sensing Properties of Nanocrystalline ZnO Ceramics, Chin. J. Inorg. Chem., 1998, 14(3): 355–359 (in Chinese)
Ding Shiwen, Zhang Shaoyan, Liu Shujuan, Ding Yu, Kang Quanying and Liu Yanchao, Synthesis and Photocatalyzing Property of Nano-ZnO, Chin. J. Inorg. Chem., 2002, 18(10): 1015–1018 (in Chinese)
He Yongjun, Synthesis of ZnO nanoparticles with narrow size distribution under pulsed microwave heating, China Particulogy, 2004, 2(4): 168–170
Xu C.X., Sun X.W., Chen B.J., Sun C.Q. and Tay B.K., Nanostructural ZnO fabricated by vapor-phase transport in air, Intern. J. Mod. Phys. B, 2004, 18(2): 225–232
Wan Q., Yu K., Wang T.H., Lin C.L., Low-field electron emission from tetrapod-like ZnO nanostructures synthesized by rapid evaporation, Appl. Phys. Lett., 2003, 83(11): 2253–2255
Zhang Xianxi, Wang Xiaojuan, Zhai Guanjie and Jiang Jianzhuang, Nanocrystalline ZnO preparation through basic Zinc carbonate calcinations, Chin. J. Inorg. Chem., 2002, 18(10): 1038–1040 (in Chinese)
He Yongning, Shen Xiaoliang, Ma Lidun, Synthesis and characterization of nanocrystalline-sized Zinc oxide, Chin. J. Appl. Chem., 1996, 13(4): 92–94 (in Chinese)
Liu Chaofeng, Hu xingfang, Zu Yong, Nanocrystalline-sized Zinc oxide prepared by using urea as precipitating agent, J. Inorg. Marer., 1999, 14(3): 390–396 (in Chinese)
Fendler J.H., Nanoparticles and Nanostructured Films. Beijing: Chemical Industrial Press, 2003, 8: 5–8
Author information
Authors and Affiliations
Corresponding author
Additional information
__________
Translated from Journal of Inner Mongolia Normal University (Natural Science Edition), 2006, 35(1) (in Chinese)
About this article
Cite this article
Siqingaowa, Z., Yao, H. & Garidi Preparation and characterization of nanocrystalline ZnO by direct precipitation method. Front. Chem. China 1, 277–280 (2006). https://doi.org/10.1007/s11458-006-0036-7
Issue Date:
DOI: https://doi.org/10.1007/s11458-006-0036-7