Abstract
Alternating multilayer films of hydrogen diluted hydrogenated protocrystalline silicon (pc-Si:H) were prepared using a plasma- enhanced chemical vapor deposition technique. The microstructure of the deposited films and photoresponse characteristics of their Schottky diode structures were investigated by Raman scattering spectroscopy, Fourier transform infrared spectroscopy and photocurrent spectra. Microstructure and optical absorption analyses suggest that the prepared films were pc-Si:H multilayer films with a two-phase structure of silicon nanocrystals (NCs) and its amorphous counterpart and the band gap of the films showed a decreasing trend with increasing crystalline fraction. Photocurrent measurement revealed that silicon NCs facilitate the spatial separation of photo-generated carriers, effectively reduce the non-radiative recombination rate, and induce a photoresponse peak value shift towards the short-wavelength side with increasing crystallinity. However, the carrier traps near the surface defects of silicon NCs and their spatial carrier confinement result in a significant reduction of the diode photoresponse in the long-wavelength region. An enhancement of the photoresponse from 350 to 1000 nm was observed when applying an increased bias voltage in the diode, showing a favorable carrier transport and an effective collection of photo-generated carriers was achieved. Both the spatial separation of the restricted electron-hole pairs in silicon NCs and the de-trapping of the carriers at their interface defects are responsible for the red-shift in photoresponse spectra and enhancement of external quantum efficiency. The results provide fundamental data for the carrier transport control of high-efficiency pc-Si:H solar cells.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Lim K S, Kwak J H, Kwon S W, et al. Highly and rapidly stabilized protocrystalline silicon multilayer solar cells. Mater Res Soc Symp Proc, 2005, 862: A11.2.1–A11.2.12
Staebler D L, Wronski C R. Reversible conductivity changes in discharge-produced amorphous Si. Appl Phys Lett, 1997, 31: 292–294
Kwon S W, Kwak J, Myong S Y, et al. Characterization of the protocrystalline silicon multilayer. J Non-Crystal Solids, 2006, 352: 1134–1137
Myong S Y, Kwon S W, Kondo M, et al. Development of a rapidly stabilized protocrystalline silicon multilayer solar cell. Semicond Sci Technol, 2006, 21: L11–L15
Myong S Y, Kwon S W, Lim K S, et al. Inclusion of nanosized silicon grains in hydrogenated protocrystalline silicon multilayers and its relation to stability. Appl Phys Lett, 2006, 88: 083118
Yoon J H, Lee C H. Stability of undoped hydrogenated amorphous silicon multilayer film grown with alternating substrate temperature. Appl Phys Lett, 1996, 69: 1250–1252
Zhang R, Chen X Y, Zhang K, et al. Photocurrent response of hydrogenated nanocrystalline silicon thin films. J Appl Phys, 2006, 100: 104310
Gao X Y, Zhao J T, Liu Y F, et al. Characterized microstructure and electrical properties of hydrogenated nanocrystalline silicon films by Raman and electrical conductivity spectra. Acta Phys Polon A, 2009, 115: 738–741
Han D X, Wang K D, Owens J M, et al. Hydrogen structures and the optoelectronic properties in transition films from amorphous to microcrystalline silicon prepared by hot-wire chemical vapor deposition. J Appl Phys, 2003, 93: 3776–3783
Ahn J Y, Jun K H, Lim K S, et al. Stable protocrystalline silicon and unstable microcrystalline silicon at the onset of a microcrystalline regime. Appl Phys Lett, 2003, 82: 1718–1720
Zhang S B, Liao X B, Xu Y Y, et al. Microstructure of the silicon film prepared near the phase transition regime from amorphous to nanocrystalline. Mat Res Soc Symp Proc, 2003, 737: F8.11.1–F8.11.7
Wu X L, Tong S, Liu X N, et al. X-ray diffraction study of alternating nanocrystalline silicon/amorphous silicon multilayers. Appl Phys Lett, 1997, 70: 838–840
Gracin D, Sancho-Paramon J, Juraic K, et al. Analysis of amorphous-nano-crystalline multilayer structures by optical, photo-deflection and photo-current spectroscopy. Micron, 2009, 40: 56–60
Viera G, Huet S, Boufendi L. Crystal size and temperature measurements in nanostructured silicon using Raman spectroscopy. J Appl Phys, 2001, 90: 4175–4183
Jun K H, Ouwens J D, Schropp R E I. Low degradation and fast annealing effects of amorphous silicon multilayer processed through alternate hydrogen dilution. J Appl Phys, 2000, 88: 4881–4888
Han D X, Wang K D, Owens J M, et al. Hydrogen structures and the optoelectronic properties in transition films from amorphous to microcrystalline silicon prepared by hot-wire chemical vapor deposition. J Appl Phys, 2003, 93: 3776–3783
Kamei T, Stradins P, Matsuda A. Effects of embedded crystallites in amorphous silicon on light-induced defect creation. Appl Phys Lett, 1999, 74: 1707–1709
Zhang R, Chen X Y, Lu J J, et al. Photocurrent of hydrogenated nanocrystalline silicon thin film/crystalline silicon heterostructure. J Appl Phys, 2007, 102: 123708
He Y L, Hu G Y, Yu M B, et al. Conduction mechanism of hydrogenated nanocrystalline silicon films. Phys Rev B, 1999, 59: 15352–15357
Author information
Authors and Affiliations
Corresponding author
Additional information
This article is published with open access at Springerlink.com
Rights and permissions
This article is published under an open access license. Please check the 'Copyright Information' section either on this page or in the PDF for details of this license and what re-use is permitted. If your intended use exceeds what is permitted by the license or if you are unable to locate the licence and re-use information, please contact the Rights and Permissions team.
About this article
Cite this article
Yu, W., Zhu, H., Zhao, Y. et al. Photoresponse and carrier transport of protocrystalline silicon multilayer films. Chin. Sci. Bull. 57, 2624–2630 (2012). https://doi.org/10.1007/s11434-012-5190-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11434-012-5190-3