Oxide transformation and break-up of liquid metal in boiling solutions

Abstract

The non-toxic gallium-based liquid metals (LMs) are promising for various newly emerging areas due to having excellent fluidity, high electrical and heat conductivity. However, the oxide layers often affect their applications. In this paper, we disclosed a straightforward boiling strategy to efficiently remove the oxide of LM in deionized water. Meanwhile such method was also demonstrated to be capable of quickly breaking up LM into droplets (mean 0.51 mm, SD 0.20 mm) in NaCl solution, which has important value for manufacture purpose. According to the force analysis, surface tension of LM dominates the interaction between solution bubbles and LM under the same heating conditions. Then we characterized the surface morphology and compositions of LM droplets boiled (LMDB) using scanning electron microscope (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) and tested the dynamic force between a rod and LMDB. It was shown that after being boiled in water, most of Ga2O3 was transformed to scattered α-GaOOH nanorods which has less restriction to the deformation of LM and large resistance force (0.8 mN) was tested; otherwise, after boiled in NaCl solution, more Ga2O3 with contact patch structure reduces the surface resistance of LM (0.2 mN) and makes it to be broken up by bubbles. The different surface products are determined by the inhibition of hydrolysis of Ga3+ by NaCl solution. This study paved a simple way for oxide removal in neutral solution and mass production of LMD. It also suggests an efficient approach for exploring mechanisms of interactions between LM and bubbles, which is difficult to study otherwise in sonication.

This is a preview of subscription content, log in to check access.

References

  1. 1

    Daeneke T, Khoshmanesh K, Mahmood N, et al, Liquid metals: Fundamentals and applications in chemistry, Chem Soc Rev, 2018, 47: 4073–4111

    Google Scholar 

  2. 2

    Ma K Q, Liu J, Heat-driven liquid metal cooling device for the thermal management of a computer chip, J Phys D-Appl Phys, 2007, 40: 4722–4729

    Google Scholar 

  3. 3

    Deng Y, Liu J, Hybrid liquid metal-water cooling system for heat dissipation of high power density microdevices, Heat Mass Transfer, 2010, 46: 1327–1334

    Google Scholar 

  4. 4

    Tan S C, Zhou Y X, Wang L, et al, Electrically driven chip cooling device using hybrid coolants of liquid metal and aqueous solution, Sci China Tech Sci, 2016, 59: 301–308

    Google Scholar 

  5. 5

    Jeong S H, Hagman A, Hjort K, et al, Liquid alloy printing of microfluidic stretchable electronics, Lab Chip, 2012, 12: 4657–4664

    Google Scholar 

  6. 6

    Tabatabai A, Fassler A, Usiak C, et al, Liquid-phase gallium-indium alloy electronics with microcontact printing, Langmuir, 2013, 29: 6194–6200

    Google Scholar 

  7. 7

    Zhang Q, Zheng Y, Liu J, Direct writing of electronics based on alloy and metal (DREAM) ink: A newly emerging area and its impact on energy, environment and health sciences, Front Energy, 2012, 6: 311–340

    Google Scholar 

  8. 8

    Wang L, Liu J, Liquid phase 3D printing for quickly manufacturing conductive metal objects with low melting point alloy ink, Sci China Tech Sci, 2014, 57: 1721–1728

    Google Scholar 

  9. 9

    Ladd C, So J H, Muth J, et al. 3D printing of free standing liquid metal microstructures. Adv Mater, 2013, 25: 5081–5085

    Google Scholar 

  10. 10

    Mei S, Gao Y, Li H, et al, Thermally induced porous structures in printed gallium coating to make transparent conductive film, Appl Phys Lett, 2013, 102: 041905

    Google Scholar 

  11. 11

    Tang X, Tang S Y, Sivan V, et al, Photochemically induced motion of liquid metal marbles, Appl Phys Lett, 2013, 103: 174104

    Google Scholar 

  12. 12

    Zhang J, Sheng L, Liu J, Synthetically chemical-electrical mechanism for controlling large scale reversible deformation of liquid metal objects, Sci Rep, 2014, 4: 7116

    Google Scholar 

  13. 13

    Fang W Q, He Z Z, Liu J, Electro-hydrodynamic shooting phenomenon of liquid metal stream, Appl Phys Lett, 2014, 105: 134104

    Google Scholar 

  14. 14

    Tang S Y, Joshipura I D, Lin Y, et al, Liquid-metal microdroplets formed dynamically with electrical control of size and rate, Adv Mater, 2016, 28: 604–609

    Google Scholar 

  15. 15

    Kim D, Lee J B. Magnetic-field-induced liquid metal droplet manipulation. J Korean Phys Soc, 2015, 66: 282–286

    Google Scholar 

  16. 16

    Zavabeti A, Daeneke T, Chrimes A F, et al, Ionic imbalance induced self-propulsion of liquid metals, Nat Commun, 2016, 7: 12402

    Google Scholar 

  17. 17

    Downs A J. Chemistry of Aluminium, Gallium, Indium and Thallium. New York: Springer Science & Business Media, 1993

    Google Scholar 

  18. 18

    Liu T, Sen P, Kim C J, Characterization of nontoxic liquid-metal alloy galinstan for applications in microdevices, J Microelectromech Syst, 2012, 21: 443–450

    Google Scholar 

  19. 19

    Cheng S, Wu Z, Hallbjorner P, et al, Foldable and stretchable liquid metal planar inverted cone antenna, IEEE Trans Antennas Propagat, 2009, 57: 3765–3771

    Google Scholar 

  20. 20

    Gao M, Gui L, A handy liquid metal based electroosmotic flow pump, Lab Chip, 2014, 14: 1866–1872

    Google Scholar 

  21. 21

    Tang S Y, Khoshmanesh K, Sivan V, et al, Liquid metal enabled pump, Proc Natl Acad Sci USA, 2014, 111: 3304–3309

    Google Scholar 

  22. 22

    Kramer R K, Majidi C, Sahai R, et al, Soft curvature sensors for joint angle proprioception, In: 2011 IEEE/RSJ International Conference on Intelligent Robots and Systems. San Francisco, 2011. 1919–1926

    Google Scholar 

  23. 23

    Majidi C, Kramer R, Wood R J, A non-differential elastomer curvature sensor for softer-than-skin electronics, Smart Mater Struct, 2011, 20: 105017

    Google Scholar 

  24. 24

    Hutter T, Bauer W A C, Elliott S R, et al, Formation of spherical and non-spherical eutectic gallium-indium liquid-metal microdroplets in microfluidic channels at room temperature, Adv Funct Mater, 2012, 22: 2624–2631

    Google Scholar 

  25. 25

    Yu Y, Wang Q, Yi L, et al, Channelless fabrication for large-scale preparation of room temperature liquid metal droplets, Adv Eng Mater, 2014, 16: 255–262

    Google Scholar 

  26. 26

    Friedman H, Reich S, Popovitz-Biro R, et al. Micro-and nano-spheres of low melting point metals and alloys, formed by ultrasonic cavitation. Ultrasons Sonochem, 2013, 20: 432–444

    Google Scholar 

  27. 27

    Scharmann F, Cherkashinin G, Breternitz V, et al, Viscosity effect on GaInSn studied by XPS, Surf Interface Anal, 2004, 36: 981–985

    Google Scholar 

  28. 28

    Zheng Y, He Z Z, Yang J, et al, Personal electronics printing via tapping mode composite liquid metal ink delivery and adhesion mechanism, Sci Rep, 2014, 4: 4588

    Google Scholar 

  29. 29

    Giguère P A, Lamontagne D, Polarography with a dropping gallium electrode, Science, 1954, 120: 390–391

    Google Scholar 

  30. 30

    Kim D, Lee Y, Lee D, et al, Hydrochloric acid-impregnated paper for liquid metal microfluidics, In: 2013 Transducers & Eurosensors XXVII: The 17th International Conference on Solid-State Sensors, Actuators and Microsystems. Barcelona, 2013. 2620–2623

    Google Scholar 

  31. 31

    Kim D, Thissen P, Viner G, et al, Recovery of nonwetting characteristics by surface modification of gallium-based liquid metal droplets using hydrochloric acid vapor, ACS Appl Mater Interfaces, 2012, 5: 179–185

    Google Scholar 

  32. 32

    Zhang J, Yao Y, Sheng L, et al, Self-fueled biomimetic liquid metal mollusk, Adv Mater, 2015, 27: 2648–2655

    Google Scholar 

  33. 33

    Sheng L, Zhang J, Liu J, Diverse transformations of liquid metals between different morphologies, Adv Mater, 2014, 26: 6036–6042

    Google Scholar 

  34. 34

    Shanmugan S, Mutharasu D, Structural and optical properties of ultrahigh pure hot water processed Ga2O3 thin film, Mater Sci, 2016, 22: 166–169

    Google Scholar 

  35. 35

    Zavabeti A, Ou J Z, Carey B J, et al, A liquid metal reaction environment for the room-temperature synthesis of atomically thin metal oxides, Science, 2017, 358: 332–335

    Google Scholar 

  36. 36

    Zeng L Z, Klausner J F, Mei R, A unified model for the prediction of bubble detachment diameters in boiling systems—I, Pool boiling. Int J Heat Mass Transfer, 1993, 36: 2261–2270

    Google Scholar 

  37. 37

    Gupta M K, Sharma D S, Lakhera V J, Detachment forces on spherical bubble during formation, Mater Today-Proc, 2017, 4: 4130–4136

    Google Scholar 

  38. 38

    Baes C F, Mesmer R S. The Hydrolysis of Cations. New York: Wiley, 1976

    Google Scholar 

  39. 39

    Sato T, Nakamura T, Studies of the crystallisation of gallium hydroxide precipitated from hydrochloric acid solutions by various alkalis, J Chem Technol Biotechnol, 1982, 32: 469–475

    Google Scholar 

  40. 40

    Diakonov I I, Pokrovski G S, Bénézeth P, et al, Gallium speciation in aqueous solution, Experimental study and modelling: Part 1. Thermodynamic properties of Ga(OH)4–to 300°C. Geochim Cosmochim Acta, 1997, 61: 1333–1343

    Google Scholar 

  41. 41

    Uchida M, Okuwaki A, Solubility of gallium(III) oxyhydroxide in aqueous NaCl solutions at 100°C, J Solution Chem, 1997, 26: 699–708

    Google Scholar 

  42. 42

    Horasawa N, Nakajima H, Takahashi S, et al, Behavior of pure gallium in water and various saline solutions, Dental Mater J, 1997, 16: 200–208, 226

    Google Scholar 

  43. 43

    Surdu-Bob C C, Saied S O, Sullivan J L, An X-ray photoelectron spectroscopy study of the oxides of GaAs, Appl Surf Sci, 2001, 183: 126–136

    Google Scholar 

  44. 44

    Ha J S, Park S-J, Kim S-B, et al, Correlation of surface morphology with chemical structures of sulfur-passivated GaAs(100) investigated by scanning tunneling microscopy and X-ray photoelectron spectroscopy, J Vac Sci Tech A, 1995, 13: 646–651

    Google Scholar 

  45. 45

    Yu S, Qing-Qing S, Lin D, et al, Improvement of atomic-layer-deposited Al2O3/GaAs interface property by sulfuration and NH3 thermal nitridation, Chin Phys Lett, 2008, 25: 3954–3956

    Google Scholar 

  46. 46

    Dar M I, Sampath S, Shivashankar S A, Exploiting oriented attachment in stabilizing La3+-doped gallium oxide nano-spindles, RSC Adv, 2014, 4: 49360–49366

    Google Scholar 

  47. 47

    Hinkle C L, Milojevic M, Brennan B, et al, Detection of Ga suboxides and their impact on III-V passivation and Fermi-level pinning, Appl Phys Lett, 2009, 94: 162101

    Google Scholar 

  48. 48

    Larsen R J, Dickey M D, Whitesides G M, et al, Viscoelastic properties of oxide-coated liquid metals, J Rheol, 2009, 53: 1305–1326

    Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Jing Liu.

Additional information

This work was supported by the Dean’s Research Funding, Frontier Funding from Chinese Academy of Sciences, and the National Natural Science Foundation of China (Grant No. 91748206).

Electronic supplementary material

Supplementary material, approximately 2.08 MB.

Supplementary material, approximately 1.22 MB.

Oxide transformation and break-up of liquid metal in boiling solutions

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yang, L., Zhao, X., Xu, S. et al. Oxide transformation and break-up of liquid metal in boiling solutions. Sci. China Technol. Sci. 63, 289–296 (2020). https://doi.org/10.1007/s11431-018-9444-5

Download citation

Keywords

  • liquid metal
  • boiling solutions
  • oxide transformation
  • break-up
  • hydrolysis inhibition