Abstract
In this paper, the BaO-0.6ZnO-xTiO2 ceramics with x=2.5–2.8 have been prepared by the conventional solid-state ceramic route for the purpose of investigating the effect of TiO2 content on the microwave dielectric properties. The XRD results showed that the main crystal phase in the sintered ceramics was Ba4ZnTi11O27 and that the additional phases: Ba2ZnTi5O13 and BaZn2.03Ti3.93O10.89 were presented, depending on the TiO2 contents. The SEM photographs of the samples sintered at 1200°C for 2 h showed a high compact microstructure. Because the phase composition of ceramics samples was changed with TiO2 content, the dielectric constant (ɛ r ), the quality factor values (Q×f) and the temperature coefficient of resonant frequency (τ f ) were first increased, continuously came up to a peak value, and then let up. It was lucky to find that the sample with composition BaO-0.6ZnO-2.7TiO2 had both the maximum dielectric constant ε r =36.1 and the maximum Q×f value of 29320 GHz, and more importantly, it had an acceptable temperature coefficient of resonant frequency τ f =10.45 ppm/°C.
Similar content being viewed by others
References
Nishigaki S, Kato H, Yano S, et al. Microwave dielectric properties of (Ba,Sr)O-Sm2O3-TiO2 ceramics. Am Ceram Soc Bull, 1987, 66: 1405–1410
Wakino K, Minai K, Tamura H. Microwave characteristics of (Zr,Sn)TiO4 and BaO-PbO-Nd2O3-TiO2 dielectric resonator. J Am Ceram Soc, 1984, 67: 278–281
Takada T, Wang S F, Yoshikawa S, et al. Effect of glass additions on BaO-TiO2-WO3 microwave ceramics. J Am Ceram Soc, 1994, 77: 1909–1916
Lin W Y, Gerhardt R A, Speyer R F. Thermal processing and properties of BaTi4O9 and Ba2Ti9O20 dielectric resonators. J Mater Sci, 1999, 33: 3021–3025
Wang G Q, Wu S H, Su H. Microwave dielectric ceramics in the BaO-TiO2-ZnO system doped with MnCO3 and SnO2. Mater Lett, 2005, 59: 2229–2231
Wu S H, Wang G Q, Zhao Y S, et al. BaO-TiO2 microwave ceramics. J Euro Ceram Soc, 2003, 23: 2565–2568
Roth R S, Rawn C J, Lindsay C G. Phase equilibria and crystal chemistry of the binary and ternary barium polytitanates and crystallography of the barium zinc polytitanates. J Solid Chem, 1993, 104: 99–118
Belous A G, Ovchar O V, Marjeta M K, et al. The homogeneity range and the microwave dielectric properties of the BaZn2Ti4O11 ceramics. J Euro Ceram Soc, 2006, 26: 3733–3739
Zhou H F, Chen X L, Fang L, Hu C Z. Preparation and characterization of a new microwave dielectric ceramic Ba4ZnTi11O27. J Am Ceram Soc, 2010, 93: 1537–1539
Hakki B W, Coleman P D. A dielectric resonator method of measuring inductive capacities in the millimeter range. IEEE Trans Microwave Theory Tech, 1960, MTT8: 402–410
Huang C L, Hou J L, Pan C L, et al. Effect of ZnO additive on sintering behavior and microwave dielectric properties of 0.95MgTiO3-0.05CaTiO3 ceramics. J Alloys Compd, 2008, 450: 359–363
Zhou D, Pang L X, Yao X, et al. Influence of sintering process on the microwave dielectric properties of Bi(V0.008Nb0.992)O4 ceramics. Mater Chem Phys, 2008, 115: 126–131
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yu, S., Long, M., Tang, B. et al. Effect of TiO2 content on the microwave dielectric properties of BaO-ZnO-TiO2 ceramics. Sci. China Technol. Sci. 54, 1532–1536 (2011). https://doi.org/10.1007/s11431-011-4391-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-011-4391-3