Abstract
Heavy metals in mine tailings lead to serious environmental problems. Cemented paste backfill (CPB) is widely used for treating the mine tailing. The high cost of ordinary Portland cement (OPC) reduces the profit of mine production. The work investigates the treatment of Cr(VI)-containing tailings by using slag-based cementitious materials for CPB. Flue gas desulfurization gypsum (FGDG) and limestone were used to modify the properties of samples. Results showed that the coupling addition of 6 wt% FGDG and 3 wt% limestone (A6L3) led to the highest compressive strength of CPB samples, which also presented satisfactory immobilization effects for Cr(VI). The compressive strength of CPB samples using A6L3 as a binder was comparable to the OPC-based sample, reaching about 5.53 MPa; the immobilization efficiency for Cr(VI) was about 99.5%. The effects of FGDG and limestone were twofold: the addition of FGDG favored the formation of ettringite and then contributed to a more compact structure; besides, incorporating limestone increased the packing density of the CPB system by decreasing the loosening and wedge effect.
Similar content being viewed by others
Data availability
There are no repository data.
References
Abdalqader AF, Jin F, Al-Tabbaa A (2015) Characterisation of reactive magnesia and sodium carbonate-activated fly ash/slag paste blends. Constr Build Mater 93:506–513. https://doi.org/10.1016/j.conbuildmat.2015.06.015
ASTM International (2021) Test method for compressive strength of cylindrical concrete specimens. ASTM International, West Conshohocken, PA. https://doi.org/10.1520/C0039_C0039M-20
Cao VD, Pilehvar S, Salas-Bringas C, Szczotok AM, Do NBD, Le HT, Carmona M, Rodriguez JF, Kjøniksen A-L (2018) Influence of microcapsule size and shell polarity on the time-dependent viscosity of geopolymer paste. Ind Eng Chem Res 57(29):9457–9464. https://doi.org/10.1021/acs.iecr.8b01961
Chen J, Wen S, Liu Y (2022) Research on the efficiency of the mining industry in China from the perspective of time and space. Res Policy 75:102475. https://doi.org/10.1016/j.resourpol.2021.102475
Chen T, Yan Z-A, Xu D, Wang M, Huang J, Yan B, Xiao X, Ning X (2020) Current situation and forecast of environmental risks of a typical lead-zinc sulfide tailings impoundment based on its geochemical characteristics. J Environ Sci (china) 93:120–128
Chindaprasirt P, Homwuttiwong S, Jaturapitakkul C (2007) Strength and water permeability of concrete containing palm oil fuel ash and rice husk–bark ash. Constr Build Mater 21(7):1492–1499. https://doi.org/10.1016/j.conbuildmat.2006.06.015
Chrysochoou M, Dermatas D (2006) Evaluation of ettringite and hydrocalumite formation for heavy metal immobilization: literature review and experimental study. J Hazard Mater 136(1):20–33. https://doi.org/10.1016/j.jhazmat.2005.11.008
Ebert BA, Geiker MR, Kunther W, Kirkelund GM (2021) Impact of electrodialytic remediation of MSWI fly ash on hydration and mechanical properties of blends with Portland cement. Construct Build Mater 309:125193. https://doi.org/10.1016/j.conbuildmat.2021.125193
Guo Z, Hou P, Xu Z, Gao J, Zhao Y (2022) Sulfate attack resistance of tricalcium silicate modified with nano-silica and supplementary cementitious materials. Construct Build Mater 321:126332. https://doi.org/10.1016/j.conbuildmat.2022.126332
Ismail SN, Ramli A, Aziz HA (2021) Influencing factors on safety culture in mining industry: a systematic literature review approach. Res Policy 74:102250. https://doi.org/10.1016/j.resourpol.2021.102250
Jeon D, Yum WS, Jeong Y, Oh JE (2018) Properties of quicklime(CaO)-activated Class F fly ash with the use of CaCl 2. Cem Concr Res 111:147–156. https://doi.org/10.1016/j.cemconres.2018.05.019
Jiang H, Qi Z, Yilmaz E, Han J, Qiu J, Dong C (2019) Effectiveness of alkali-activated slag as alternative binder on workability and early age compressive strength of cemented paste backfills. Constr Build Mater 218:689–700. https://doi.org/10.1016/j.conbuildmat.2019.05.162
Khatri RP, Sirivivatnanon V (1997) Methods for the determination of water permeability of concrete. ACI Mater J 94(3):257–261
Koohestani B, Darban AK, Mokhtari P, Darezereshki E, Yilmaz E, Yilmaz E (2020) Influence of hydrofluoric acid leaching and roasting on mineralogical phase transformation of pyrite in sulfidic mine tailings. Minerals 10(6):513. https://doi.org/10.3390/min10060513
Król A, Mizerna K, Bożym M (2019) An assessment of pH-dependent release and mobility of heavy metals from metallurgical slag. J Hazard mater:121502. https://doi.org/10.1016/j.jhazmat.2019.121502
Pandey SK, Bhattacharya T (2019) Mobility, ecological risk and change in surface morphology during sequential chemical extraction of heavy metals in fly ash: a case study. Environ Technol Innov 13:373–382. https://doi.org/10.1016/j.eti.2016.10.004
Provis JL (2008) Geopolymers: structure, processing, properties and industrial applications. Woodhead Pub, Cambridge, England, Boca Raton, FL. http://search.ebscohost.com/login.aspx?direct=true&scope=site&db=nlebk&db=nlabk&AN=691343
Provis JL, van Deventer JSJ (2014) Alkali activated materials, vol 13. Springer, Netherlands, Dordrecht
Qi C, Fourie A (2019) Cemented paste backfill for mineral tailings management: review and future perspectives. Min Eng 144:106025. https://doi.org/10.1016/j.mineng.2019.106025
Qiu J, Guo Z, Yang L, Jiang H, Zhao Y (2020) Effect of tailings fineness on flow, strength, ultrasonic and microstructure characteristics of cemented paste backfill. Construct Build Mater 263:120645. https://doi.org/10.1016/j.conbuildmat.2020.120645
Qiu J, Guo Z, Yang L, Jiang H, Zhao Y (2020b) Effects of packing density and water film thickness on the fluidity behaviour of cemented paste backfill. Powder Technol 359:27–35. https://doi.org/10.1016/j.powtec.2019.10.046
Qiu J, Zhao Y, Xing J (2019) Sun X (2019) Fly ash/blast furnace slag-based geopolymer as a potential binder for mine backfilling: effect of binder type and activator concentration. Adv Mater Sci Eng 3:1–12. https://doi.org/10.1155/2019/2028109
Scrivener K (ed) (2016) A practical guide to microstructural analysis of cementitious materials. Taylor & Francis Group
Sun X, Zhao Y, Tian Y, Wu P, Guo Z, Qiu J, Xing J, Xiaowei G (2021) Modification of high-volume fly ash cement with metakaolin for its utilization in cemented paste backfill: the effects of metakaolin content and particle size. Powder Technol 393:539–549. https://doi.org/10.1016/j.powtec.2021.07.067
Sun X, Zhao Y, Xing J, Qiu J, Li H (2016) Preparation of binding materials for backfill with alkali activated blast furnace slag and fly ash. Metal Mine (485):189–192. https://kns.cnki.net/kcms2/article/abstract?v=3uoqIhG8C44YLTlOAiTRKibYlV5Vjs7iAEhECQAQ9aTiC5BjCgn0Rp3_kt5GPu1qYEauq4XRBXioypyrEGrxACxRud_qTX1o&uniplatform=NZKPT
Suppes R, Heuss-Aßbichler S (2021) Resource potential of mine wastes: a conventional and sustainable perspective on a case study tailings mining project. J Clean Prod 297:126446. https://doi.org/10.1016/j.jclepro.2021.126446
Tambara L, Cheriaf M, Rocha JC, Palomo A, Fernández-Jiménez A (2020) Effect of alkalis content on calcium sulfoaluminate (CSA) cement hydration. Cement Concrete Res 128:105953. https://doi.org/10.1016/j.cemconres.2019.105953
Wang A, Cao S, Yilmaz E (2022) Effect of height to diameter ratio on dynamic characteristics of cemented tailings backfills with fiber reinforcement through impact loading. Construct Build Mater 322:126448. https://doi.org/10.1016/j.conbuildmat.2022.126448
Wang P, Sun Z, Hu Y, Cheng H (2019) Leaching of heavy metals from abandoned mine tailings brought by precipitation and the associated environmental impact. Sci Total Environ 695:133893. https://doi.org/10.1016/j.scitotenv.2019.133893
Wu M, Zhang Y, Jia Y, She W, Liu G, Yang Y, Rong Z, Sun W (2019) The influence of chemical admixtures on the strength and hydration behavior of lime-based composite cementitious materials. Cement Concr Compos 103:353–364. https://doi.org/10.1016/j.cemconcomp.2019.05.008
Wu Q, Xue Q, Yu Z (2021) Research status of super sulfate cement. J Clean Prod 294:126228. https://doi.org/10.1016/j.jclepro.2021.126228
Xing J, Zhao Y, Qiu J, Sun X (2019) Microstructural and mechanical properties of alkali activated materials from two types of blast furnace slags. Materials (Basel, Switzerland) 12(13). https://doi.org/10.3390/ma12132089
Xue G, Yilmaz E, Song W, Cao S (2020) Fiber length effect on strength properties of polypropylene fiber reinforced cemented tailings backfill specimens with different sizes. Construct Build Mater 241:118113. https://doi.org/10.1016/j.conbuildmat.2020.118113
Yuan B, Yu QL, Brouwers H (2017) Time-dependent characterization of Na 2 CO 3 activated slag. Cement Concr Compos 84:188–197. https://doi.org/10.1016/j.cemconcomp.2017.09.005
Yum WS, Jeong Y, Yoon S, Jeon D, Jun Y, Oh JE (2017) Effects of CaCl2 on hydration and properties of lime(CaO)-activated slag/fly ash binder. Cement Concr Compos 84:111–123. https://doi.org/10.1016/j.cemconcomp.2017.09.001
Zhang J, Scherer GW (2011) Comparison of methods for arresting hydration of cement. Cem Concr Res 41(10):1024–1036. https://doi.org/10.1016/j.cemconres.2011.06.003
Zhang J, Shi C, Zhang Z, Hu X (2022) Reaction mechanism of sulfate attack on alkali-activated slag/fly ash cements. Construct Build Mater 318:126052. https://doi.org/10.1016/j.conbuildmat.2021.126052
Zhang S, Du C, Qi W (2020a) Effects of alkali-activated slag binder on the fluidity and strength of cement paste backfill. Min Res Develop 40(03):87–92
Zhang S, Zhao Y, Guo Z, Ding H (2021) Stabilization/solidification of hexavalent chromium containing tailings using low-carbon binders for cemented paste backfill. J Environ Chem Eng 9(1):104738. https://doi.org/10.1016/j.jece.2020.104738
Zhang Y, Liu X, Xu Y, Tang B, Wang Y (2020) Preparation of road base material by utilizing electrolytic manganese residue based on Si-Al structure: mechanical properties and Mn2+ stabilization/solidification characterization. J Hazard Mater 390:122188. https://doi.org/10.1016/j.jhazmat.2020.122188
Zhang Y, Zhang S, Ni W, Yan Q, Gao W, Li Y (2019) Immobilisation of high-arsenic-containing tailings by using metallurgical slag-cementing materials. Chemosphere 223:117–123. https://doi.org/10.1016/j.chemosphere.2019.02.030
Zhao Y, Qiu J, Guo Z, Zhang S, Wu P, Sun X (2022) Activation the hydration properties of illite-containing tailings to prepare a binder for cemented paste backfill. Construct Build Mater 318:125989. https://doi.org/10.1016/j.conbuildmat.2021.125989
Zhao Y, Qiu J, Wu P, Guo Z, Zhang S, Sun X (2022) Preparing a binder for cemented paste backfill using low-aluminum slag and hazardous oil shale residue and the heavy metals immobilization effects. Powder Technol 399:117167. https://doi.org/10.1016/j.powtec.2022.117167
Zhao Y, Qiu J, Zhang S, Guo Z, Ma Z, Sun X, Xing J (2020) Effect of sodium sulfate on the hydration and mechanical properties of lime-slag based eco-friendly binders. Construct Build Mater 250:118603. https://doi.org/10.1016/j.conbuildmat.2020.118603
Zhao Y, Qiu J, Zhang S, Guo Z, Wu P, Sun X, Gu X (2021) Low carbon binder modified by calcined quarry dust for cemented paste backfill and the associated environmental assessments. J Environ Manage 300:113760. https://doi.org/10.1016/j.jenvman.2021.113760
Zhao Y, Qiu J, Zhang S, Guo Z, Wu P, Sun X, Gu X (2022) Recycling of arsenic-containing biohydrometallurgy waste to produce a binder for cemented paste backfill: mix proportion optimization. Powder Technol 398:117155. https://doi.org/10.1016/j.powtec.2022.117155
Zhao Y, Wu P, Qiu J, Guo Z, Tian Y, Sun X, Gu X (2022d) Recycling hazardous steel slag after thermal treatment to produce a binder for cemented paste backfill. Powder Technol 395:652–662. https://doi.org/10.1016/j.powtec.2021.10.008
Zheng J, Sun X, Guo L, Zhang S, Chen J (2019) Strength and hydration products of cemented paste backfill from sulphide-rich tailings using reactive MgO-activated slag as a binder. Constr Build Mater 203:111–119. https://doi.org/10.1016/j.conbuildmat.2019.01.047
Zheng J, Tang Y, Feng H (2021) Utilization of low-alkalinity binders in cemented paste backfill from sulphide-rich mine tailings. Construct Build Mater 290:123221. https://doi.org/10.1016/j.conbuildmat.2021.123221
Funding
The author thanks the financial support from the Science and Technology Department of Lvliang, GG2015050.
Author information
Authors and Affiliations
Contributions
Liding Zhao: data curation and writing original draft and methodology.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
This is not applicable.
Consent to publish
This is not applicable.
Competing interests
The authors declare no competing interests.
Additional information
Responsible Editor: Ioannis A. Katsoyiannis
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Zhao, L. Immobilization of Cr(VI)-containing tailings by using slag-cementing materials for cemented paste backfill: influence of sulfate and limestone addition. Environ Sci Pollut Res 30, 91984–91996 (2023). https://doi.org/10.1007/s11356-023-28605-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-023-28605-7