Investigation on surface sulfate attack of nanoparticle-modified fly ash concrete

  • Research Article
  • Published:
Environmental Science and Pollution Research Aims and scope Submit manuscript

Abstract

Sulfate attack on concrete structures is a major durability concern wherein concrete interacts with marine water, swamp water, groundwater, sewage water, freshwater, etc. In this study, the supplementary cementitious materials such as fly ash (FA) and nanoparticles are together incorporated into conventional concrete aiming to enhance the resistance of concrete against the penetration of sulfates. The present work is focused to understand the degradation in FA concrete modified with nanoparticles by surface sulfate attack. Concrete mix such as FA and FA modified with 2 wt% nano-TiO2 (FAT), nano-CaCO3 (FAC), and 1:1 ratio of nano-TiO2 to nano-CaCO3 (FATC) was fabricated. The specimens were exposed in 3% of ammonium and sodium sulfate for 90 days. The deterioration effects and changes in microstructural properties in all the specimens were comparatively studied. Results showed FAT, FAC, and FATC concrete have been deteriorated in ammonium and sodium sulfate solution compared with FA concrete. Partial replacement of cement with fly ash decreases the quantity of freely available reactive aluminates. Consumption of free lime by the fly ash prevents to react with sulfate. The enhanced properties of fly ash concrete against sulfate attack could be achieved with less C3A content thus reducing the available Ca(OH)2 and reducing the possibility of development of deleterious ettringite and gypsum.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  • Al-Akhras, Nabil M (2006) Durability of metakaolin concrete to sulfate attack. Cem Concr Res 36:1727–1734

    CAS  Google Scholar 

  • Alasali MM, Malhotra VM (1991) Role of structural concrete incorporating high volumes of fly ash in controlling expansion due to alkali aggregate reaction. ACI Mater J 88:159–163

    CAS  Google Scholar 

  • Amin M, Bassuoni MT (2018) Performance of concrete with blended binders in ammonium-sulphate solution. J Sustain Cem Based Mater 7:15–37

    CAS  Google Scholar 

  • ASTM C494 / C494M-17 (2017) Standard specification for chemical admixtures for concrete, ASTM International, West Conshohocken, PA. www.astm.org

  • Baghabra OS, Al-Amoudi (2002) Attack on plain and blended cements exposed to aggressive sulfate environments. Cem Concr Compos 24:305–316

    Google Scholar 

  • Bassuoni MT, Nehdi ML (2007) Resistance of self-consolidating concrete to sulfuric acid attack with consecutive pH reduction. Cem Concr Res 37:1070–1084

    CAS  Google Scholar 

  • Bassuoni MT, Nehdi ML (2009) Durability of self-consolidating concrete to different exposure regimes of sodium sulfate attack. Mater Struct 42:1039–1057

    CAS  Google Scholar 

  • Benammar A, Messaoudene I, Merbouh M, Bella N, Moumene A (2015) Durability of Portland cements compounds to external ammonium sulphate and sulfuric acid solution attacks. Digital Proceeding of ICOCEE –CAPPADOCIA, Sahinkaya S and Kalıpcı E (Editors), Nevsehir, TURKEY, May 20-23

  • Bilodeau A, Sivasundaram V, Painter KE, Malhotra VM (1994) Durability of concrete incorporating high volumes of fly ash. U.S. ACI Mater J 91:3–12

    CAS  Google Scholar 

  • Collepardi M (2001) Ettringite formation and sulfate attack on concrete, Proceedings of Fifth CANMET/ACI International Symposium on Recent Advances in Concrete Technology. Singapore, 29 July - 1 August 2001, SP 200, 21-38

  • Faiz UA, Shaikh S, Supit WM (2014) Mechanical and durability properties of high-volume fly ash (HVFA) concrete containing calcium carbonate (CaCO3) nanoparticles. Constr Build Mater 70:309–321

    Google Scholar 

  • Ferraris CF, Stutzman PE and Snyder KA (2006) Sulfate resistance of concrete: a new approach. PCA R&D Serial No. 2486. Published by PCA without copyright, Illinois, USA

  • Fraay ALA, Bijen JM, De Haan YM (1989) The reaction of fly ash in concrete a critical examination. Cem Concr Res 19:235–246

    CAS  Google Scholar 

  • Gao J, Yu Z, Song L, Wang T, Wei S (2013) Durability of concrete exposed to sulfate attack under flexural loading and drying–wetting cycles. Constr Build Mater 39:33–38

    Google Scholar 

  • Ghafoori N, Najimi M, Diawara H, Islam MS (2015) Effects of class F fly ash on sulfate resistance of Type V Portland cement concretes under continuous and interrupted sulfate exposures. Construction and Building Materials, 78, pp.85-91

  • Haynes H, Bassuoni MT (2011) Physical salt attack on concrete. Concr Int 33:38–42

    CAS  Google Scholar 

  • Helmuth R (1987) Fly ash in cement and concrete, Portland Cement Association. J Cem Concr Res 30:201–204

    Google Scholar 

  • Hooton RD (1993) Influence of silica fume replacement of cement on physical properties and resistance of sulfate attack, freezing and thawing, and alkali silica reactivity. ACI Mater J 90:143–151

    CAS  Google Scholar 

  • Jianming G, Zhenxin Y, Luguang S (2013) Tingxiu Wang, Sun Wei, Durability of concrete exposed to sulfate attack under flexural loading and drying–wetting cycles. Constr Build Mater 39:33–38

  • Jin ZQ, Sun W, Zhang YS, Jiang YS, Lai YZ (2007) Interaction between sulfate and chloride solution attack of concretes with and without fly ash. Cem Concr Res 37:223–1232

  • Jo BW, Kim CH, Tae GH, Park JB (2007) Characteristics of cement mortar with nano-SiO2 particle. Constr Build Mater 21:1351–1355

    Google Scholar 

  • Kaiwei L, Deng M, Mo L (2013) Effect of fly ash on resistance to sulfate attack of cement-based materials. Key Eng Mater 539:124–129

    Google Scholar 

  • Kalny J, Marcharnd, Odler I (2002) Sulfate attack on concrete. Spon Press/Taylor and Francis, London

    Google Scholar 

  • Katpady DN, Takewaka K, Yamaguchi T, Moritaka Y, Tatara Y (2012) Experimental study on deterioration monitoring of shirasu concrete in hot spring environment. Int J Earth Sci Eng 5:1020–1026

    Google Scholar 

  • Kawashima S, Seo JWT, Corr D, Hersam MC, Shah SP (2014) Dispersion of CaCO3 nanoparticles by sonication and surfactant treatment for application in fly ash–cement systems. Mater Struct 47:1011–1023

    CAS  Google Scholar 

  • Lea FM (1970) The chemistry of cement and concrete. Third Edition, Edward Arnold (Publishers) Ltd., London, 270–279

  • Li H, Xiao H, Ou J (2004) A study on mechanical and pressure-sensitive properties of cement mortar with nanophase materials. Cem Concr Res 34:435–438

    Google Scholar 

  • Li Z, Wang H, He Y, Lu S, Wang M (2006) Investigations on the preparation and mechanical properties of the nano-alumina reinforced cement composite. Mater Lett 60:356–359

    CAS  Google Scholar 

  • Lin DF, Lin KL, Chang WC, Luo HL, Cai MQ (2008) Improvements of nano-SiO2 on sludge/fly ash mortar. Waste Manag 28:1081–1087

    CAS  Google Scholar 

  • Liu K, Mo L, Deng M (2015) Influence of pH on the formation of gypsum in cement materials during sulfate attack. Adv Cem Res 27:487–493

    Google Scholar 

  • Madej J (1992) Corrosion resistance of normal and silica fume-modified mortars made from different types of cements, Proceedings of 1992;the 4th International Conference on Fly Ash, Silica Fume, Slag and Natural Pozzolans in Concrete, Istanbul, Turkey. American Concrete Institute Detroit, Special Publication 132 (2): 1189– 1207

  • March B, Day R, Bonner D (1985) Pore structure characteristics affecting the permeability of cement paste containing fly ash. Cem Concr Res 15:1027–1038

    Google Scholar 

  • Mbessa M, Péra J (2001) Durability of high-strength concrete in ammonium sulfate solution. Cement and Concrete Research 31:1227–1231

    CAS  Google Scholar 

  • Mohamed Z, Mohamed Bassuoni T, Said A (2017) Physical salt attack on concrete incorporating nano-silica. J Sustain Cem Based Mater 6:195–216

    Google Scholar 

  • Nazari A, Riahi S (2011a) Al2O3 nanoparticles in concrete and different curing media. Energy Build 43:480–1488

    Google Scholar 

  • Nazari A, Riahi S (2011b) The effects of TiO2 nanoparticles on properties of binary blended Concrete. J Compos Mater 45:1181–1188

    CAS  Google Scholar 

  • Nazari A, Riahi S, Riahi S, Shamekhi SF, Khademno A (2010a) Assessment of the effects of the cement paste composite in presence TiO2 nanoparticles. J Am Sci 6:43–46

    Google Scholar 

  • Nazari A, Riahi S, Riahi S, Shamekhi SF, Khademno A (2010b) Benefits of Fe2O3 nanoparticles in concrete mixing matrix. J Am Sci 6:102–106

    Google Scholar 

  • Nehdi M, Hayek M (2005) Behavior of blended and cement mortars exposed to sulfate solutions cycling in relative humidity. Cem Concr Res 35:731–742

    CAS  Google Scholar 

  • Nie Q, Zhou C, Shu X, He Q, Huang B (2014) Chemical, mechanical, and durability properties of concrete with local mineral admixtures under sulfate environment in Northwest China. Materials 7:3772–3785

    CAS  Google Scholar 

  • Papadakis VG (2002) Effect of supplementary cementing materials on concrete resistance against carbonation and chloride ingress. Cem Concr Res 30:291–299

    Google Scholar 

  • Pera J, Husson S, Guilhot B (1999) Influence of finely ground limestone on cement hydration. Cem Concr Compos 21:99–105

    CAS  Google Scholar 

  • Piasta W, Marczewska JULIA, Jaworska MONIKA (2014) Some aspects and mechanisms of sulphate attack. Structure Environ 6(3):19–24

    Google Scholar 

  • Qing Y, Zenan Z, Deyu K, Rongshen C (2007) Influence of nano-SiO2 addition on properties of hardened cement pastes as compared with silica fume. Constr Build Mater 21:539–545

    Google Scholar 

  • Ramachandran D, George RP, Vishwakarma V, Kamachi Mudali U (2017) Strength and durability studies of fly ash concrete in sea water environments compared with normal and superplasticizer concrete. KSCE J Civ Eng 21:1–9

    Google Scholar 

  • Rangan VB (2008) Low-calcium, fly-ash-based geopolymer concrete. Chapter 26, Concrete construction engineering handbook

  • Sato T, Beaudoin JJ (2011) Effect of nano-CaCO3 on hydration of cement containing supplementary cementitious materials. Adv Cem Res 23:33–43

    CAS  Google Scholar 

  • Sudha U, George RP, Vishwakarma V, Ramachandran D, Thinaharan C, Viswanathan K, Kamachi Mudali U (2018) Surface modification of fly ash concrete through nanophase incorporation for enhanced chemical deterioration resistance. J Bio Tribo Corros 4:1–10

    Google Scholar 

  • Tao JT (2005) Preliminary study on the water permeability and microstructure of concrete incorporating nano-SiO2. Cem Concr Res 35:1943–1947

    Google Scholar 

  • Tikalsky PJ and Carrasquillo RL (1989). The effect of fly ash on the sulfate resistance of concrete‟, Center for Transportation Research, Bureau of Engineering Research. The University of Texas at Austin, Research Report 481–5

  • Uthaman S, George RP, Vinita V, Ramachandran D, Thinaharan C, Viswanathan K, Kamachi Mudali U (2018) Surface modification of fly ash concrete through nanophase incorporation for enhanced chemical deterioration resistance. J Bio-and Tribo-Corrosion 4:1–10

  • Vijaya Sekhar Reddy M, Ramana Reddy IV, Madan Mohan Reddy K, Ravi Kumar CM (2013) Durability aspects of standard concrete. Int J Struct Civ Eng Res 2:40–46

    Google Scholar 

  • Winter NB (2009) Understanding cement: an introduction to cement production, cement hydration and deleterious processes in concrete. 182

  • Yazdi NA, Arefi MR, Mollaahmadi E, Nejand BA (2011) To study the effect of adding Fe2O3 nanoparticles on the morphology properties and microstructure of cement mortar. Life Sci J 8(4):550–554

    Google Scholar 

  • Yu Z, Ma J, Shi H, Shen X and Ye G (2016) Delayed ettringite formation in fly ash concrete under moist curing conditions. 5th International Conference on Durability of Concrete Structures June 30–July 1

Download references

Funding

Financial support from the Board of Research in Nuclear Sciences (BRNS), Mumbai (2013/36/33-BRNS/2355) is greatly acknowledged.

Author information

Authors and Affiliations

  1. Centre for Nanoscience and Nanotechnology, Sathyabama Institute of Science and Technology, Chennai, Tamil Nadu, 600119, India

    Vinita Vishwakarma, Sudha Uthaman, Ramachandran Dasnamoorthy & Viswanathan Kanagasabai

Authors
  1. Vinita Vishwakarma
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Sudha Uthaman
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ramachandran Dasnamoorthy
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Viswanathan Kanagasabai
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Vinita Vishwakarma.

Additional information

Responsible editor: Philippe Garrigues

Publisher’s note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Vishwakarma, V., Uthaman, S., Dasnamoorthy, R. et al. Investigation on surface sulfate attack of nanoparticle-modified fly ash concrete. Environ Sci Pollut Res 27, 41372–41380 (2020). https://doi.org/10.1007/s11356-020-10134-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11356-020-10134-2

Keywords

Search

Navigation