Microplastics in the environment are a subject of intense research as they pose a potential threat to marine organisms. Plastic fibers from textiles have been indicated as a major source of this type of contaminant, entering the oceans via wastewater and diverse non-point sources. Their presence is also documented in terrestrial samples. In this study, the amount of microfibers shedding from synthetic textiles was measured for three materials (acrylic, nylon, polyester), knit using different gauges and techniques. All textiles were found to shed, but polyester fleece fabrics shed the greatest amounts, averaging 7360 fibers/m−2/L−1 in one wash, compared with polyester fabrics which shed 87 fibers/m−2/L−1. We found that loose textile constructions shed more, as did worn fabrics, and high twist yarns are to be preferred for shed reduction. Since fiber from clothing is a potentially important source of microplastics, we suggest that smarter textile construction, prewashing and vacuum exhaustion at production sites, and use of more efficient filters in household washing machines could help mitigate this problem.
Plastic production has increased rapidly since production began in the 1940s and current production in excess of 311 million tons (Org. 2015). Though plastics are essential to modern society, the long-term consequences of such intensive use is largely unknown. Microplastics, sources, fate, and effects, have received increasing attention both from the scientific community as well as from the general public and policy makers. The term “microplastic” normally refers to plastic particles that are < 5 mm in length (Thompson et al. 2004), though the term has more recently been applied to particles that are < 1 mm in size (Browne et al. 2007). Numerous studies demonstrate the ubiquitous presence of microplastics in various compartments of the environment including in water, sediment, terrestrial soil, and biota (Andrady 2011; Browne et al. 2011a, b; Cole et al. 2011; Collignon et al. 2012; Duis and Coors 2016; Enders et al. 2015; Lusher et al. 2013). These microplastics are thought to be hazardous to marine organisms (Della Torre et al. 2014; Lee et al. 2013; Lu et al. 2016; Rochman et al. 2013; Rochman et al. 2014; Wright et al. 2013). Evidence indicates that macroplastics, objects larger than 5 mm in size which typically include plastic litter, will weather and fragment in the environment to form microplastic particles (Lambert and Wagner 2016; Weinstein et al. 2016), but microplastics are also known to enter directly into the environment from multiple sources and routes, including road run off, waste water treatment plants (sewage), and potentially artificial turf (Browne et al. 2011a; Magnusson et al. 2016).
One commonly identified type of microplastic found in environmental samples is fibers, which are thought to originate from textiles. Both natural textile fibers (wool, linen, and cotton) and synthetic textile fibers (polyester, polyamide) are found in the marine environment (Mathalon and Hill 2014; Remy et al. 2015). These synthetic microfibers have also been shown to have negative effects in organisms such as Daphnia magna which were found to ingest polyester fibers, with increased mortality as a consequence (Jemec et al. 2016). A recent publication indicated that the number of fibers released from washing 6 kg of laundry could reach more than 700,000 fibers (Napper and Thompson 2016). A previous publication reported lower levels in wash effluent; outgoing water from washing machines could contain 100–300 fibers per liter (Browne et al. 2011a), though the information presented in that article is not detailed enough to fully quantify the amount of fibers released from the textiles. In addition, this study did not make use of detergent in washing procedures, for technical reasons, and may therefore present underestimated values.
Washing effluent will in many countries ultimately reach sewage treatment plants. Studies addressing the release of microplastics in sewage effluent indicate that 70–99% of microplastic particles can be retained in sludge, and that technologies at the sewage treatment plant, i.e., sand filters or membrane bioreactors (Magnusson and Norén 2014; Talvitie et al. 2017), can be of importance. However, microplastic fibers are still found in the outgoing effluent and have been reported at levels above 1770 particles per hour (Magnusson and Norén 2014; Magnusson and Wahlberg 2014) (or approximately 0.009 particles/L). These fibers are known to reach aquatic systems directly (Dris et al. 2015; Leslie et al. 2013) as well as terrestrial systems via the spreading of sludge (Habib et al. 1998; Murphy et al. 2016; Zubris and Richards 2005).
The release of synthetic fibers into the environment is not innocuous. There is widespread contamination in environmental habitats and in wildlife. Laboratory evidence (Rochman et al. 2013) suggests that there may be environmental impacts and consequences to wildlife from microplastics (Browne et al. 2015; GESAMP 2015; Rochman et al. 2016), though many of the published studies addressing effects of microplastics focus on “round” microplastics and not fibers, which could potentially have different, shape-dependent effects. Fibers have been found not only in sewage effluent, but have been found to be present in coastal waters and aquatic and marine organisms (De Witte et al. 2014; Desforges et al. 2015; Lusher et al. 2013; Mathalon and Hill 2014; Sussarellu et al. 2016; Wright et al. 2013) as well as terrestrial environments and organisms (Habib et al. 1998; Huerta Lwanga et al. 2016; Palmqvist et al. 2016; Zubris and Richards 2005). Microplastic fibers are also found in products meant for human consumption. This includes blue mussels (De Witte et al. 2014; Rochman et al. 2015), honey (Liebezeit and Liebezeit 2013), table salt (Yang et al. 2015), and beer (Liebezeit and Liebezeit 2014). However, it is important to note that these references provide differing levels of verification in their identification of the described particles, ranging from visual identification to μFTIR analyses.
Since we presume that textiles are important sources of synthetic fibers, based on our knowledge of quantities of fibers in the environment and pathways via which they may be spread, it is important to address questions concerning synthetic textiles. Use of synthetic materials in textiles and clothing garments has increased from an annual production of 2.1 million tons of synthetic fibers in 1950 to almost 50 million tons in 2010 (Aizenshtein 2012; Essel and Ahrens 2015). Synthetic fibers account for approximately 60% of the total global fiber production, and polyamide (nylon) and polyester (polyethylene terephthalate (PET)) dominate. As textile production continues to increase worldwide, the total numbers of fibers entering into and passing through waste water treatment plants will inevitably increase.
Shedding, although well-known for anyone handling textiles, is a complicated phenomenon embracing a wealth of mechanisms, including both tensile fracture and flex fatigue of fibers as well as splitting or peeling off from the very fiber surface, in addition to the transport mechanisms away from the fabric (Hearle et al. 1998; Hearle and Morton 2008). Both loads acting normal to the fiber as well as frictional and shearing loads acting in angles less than 90°are anticipated during washing. Pilling (Doustaneh et al. 2013), a separate phenomenon on its own, also adds to the complexity.
Due to the importance of textiles as a source of microfibers in the environment, we have conducted a study aimed at quantifying fiber loss for several types of textiles. While the textile industry conducts research concerning design, techniques, and technological advances used in production of textiles, these studies do not address the implications of technological techniques and developments with regard to shedding of fibers, and as a source of microplastics. The aim of this work was therefore to address these issues and to test whether different knitting techniques, or use of different synthetic fibers, mitigate fiber loss. We also aimed to carefully quantify fiber loss with repeated washing and with wearing of fabrics. The information provided by this study could be of great importance to manufacturers, policy makers, and consumers looking for means by which to reduce release of microplastics or synthetic fibers into the environment, i.e., changes in practices used in textile production could potentially reduce microfiber release, and standardization of these practices could be implemented within industry.
Specifically, we hypothesized (H1) that fleece will shed more than other type of fabrics, that (H2) the knitting technique will impact where more tightly knit materials will shed less, and that (H3) different polymeric materials could behave differently. In addition, we aimed to test (H4) whether used/damaged clothes shed more fibers than new items. Since use of detergent in assessing the release of fibers during washing of garments has been in question (Browne et al. 2011a; Napper and Thompson 2016), we addressed (H5) the use of detergent in washing methods and whether this will influence the amount of fibers shed. Finally, the hypothesis (H6) was put forward that the number of washings has an impact.
Materials and methods
Here, we studied polymer fabrics consisting of either polyester (polyethylene terephthalate), the most dominant synthetic fiber on the textile market (Aizenshtein 2012; Carmichael 2015), polyacrylic (polyacrylonitrile), or polyamide (commonly known as nylon). Most of the fabrics were produced in the textile knitting laboratory at The Swedish School of Textiles. For the purpose of this work, we manufactured our own fabrics, thereby gaining full control of the treatment history of the fabric (including washing). When purchasing garments, this information and control concerning handling or treatment of fabrics is lost. These were produced using a Camber Velnit N.S. single machine no. 12210 size 26″ (for fabrics produced with E18 gauge) or a Monarch single machine model RX-SDY size 26″ (for fabrics produced with E28 gauge). However, some fabrics were commercial, provided by Tenson AB (Askim, Sweden); see Table 1 for details. After production, 10 × 10 cm pieces of cloth were cut using a laser cutter, GCC LaserPro Spirit GLS (settings; speed 9.4, power 93, PPI 1417). This was done in order to avoid loss of fibers from the cut edges of fabric, as the edges were melted. Fabrics were then dyed using a jet machine, Mathis Lab-Jet JFO (Mathis AG, Oberhasli, Switzerland), thereby making it possible for us to distinguish between fibers from different fabrics during subsequent analyses, and to identify any possible contamination. This was done according to the ISO standardized method for color fastness to domestic and commercial laundering; SS-EN ISO 105-C06. Some of the fabrics were repolished to mimic wear and tear, for example, that which occurs in clothing during use (see Table 1). This was performed using a Black & Decker KA85 Belt Sander 75 × 457 mm, with an abrasive belt cloth of 60 grains, for 1 s using a pressure of 5 kg. This method of wearing the fabric, resulting in visual damage similar to normal wear and tear, was developed in our lab.
The following terms are used to describe the structure of the fabrics. Yarns are the basic constituents of any fabric and come in two types, filament and staple. These two differ in length, where filament is continuous and staple yarns are short (typically order of mm to cm) and spun together. Originally, all manmade fibers are filaments. However, these filaments can be cut up into pieces to produce staple fibers. Yarns constructed from filaments can be identified using standard descriptions of the weight and number of filaments. Here, for example, 100/144 was used, giving the weight of 10,000 m in grams (100), and the number of filaments (144). Staple fibers typically have attractive comfort properties (moisture management, pliability, etc.). Both staples as well as multifilament yarns were used in this study. Fabrics can also be described as knitwear, a fabric kept together by yarns bound together in interlocking loops. Different constructions, i.e., patterns, could be used. In this study, single jersey is used. Gauge refers to the number of loop-forming needles per inch (E18 or E28), equivalent to the number of loops per distance, in turn measuring loop and fabric density. Microfleece is knitted terrycloth which is mechanically napped and/or cut. Napping is a textile process whereby fabrics are fed over revolving cylinders creating a soft, velvety appearance. See Table 1 for a list of tested fabrics.
Washing of fabrics
All fabric samples were pre-washed in a Wascator FOM 71 Mp washing machine (Electrolux AB, Sweden) at 40 °C for 15 min, according to standards SS-EN ISO 6330, to remove loose fibers and dust but also to eliminate any differences between our manufactured fabrics and those we bought, since production processes will inevitably result in differing contamination of fabric with spin oils and other substances. No detergent was used during the pre-wash steps. The main washing steps used in production of experimental waste water for fiber analyses were conducted using a Gyrowash one bath 815/8 (James H. Head & Co Ltd., Halifax, England). This washer is a standardized laboratory washer, comparable to the Wascator but on a smaller scale, and is constructed to mimic a household washer, but with a closed container. Its use, as opposed to commercial washers, allows for further standardization of studies addressing textile shedding and washing procedures, as this research field grows. The Gyrowash uses steel cylinders with smooth surfaces and a volume of 255 mL. In order to mimic real household washing, 25 small stainless steel balls, 6 mm in diameter, are added. This is according to standard procedures and adds mechanical impact similar to the perforated and corrugated drum in machines like the Electrolux Wascator. Samples were washed according to SS-EN ISO 105-C06 standard protocol for color washing with one modification: sample sizes were 10 × 10 cm and not 10 × 4 cm. Samples were washed at 60° for 30 min, individually in separate container in the Gyrowash. Fabric was removed from the cylinder with tweezers and rinsed five times in 2 mL of water (10 mL in total), to simulate rinsing and to remove remaining loose fibers.
Fabric samples were washed with detergent. We used a commercially available detergent Liquid Via color (Unilever) as follows; 125 mL of water and 375 μL of liquid detergent were mixed and added to a Gyrowash steel container with 25 small metal balls. This detergent is known to contain C12–15 pareth-7, sodium laureth sulfate, potassium cocoate, and TEA-Cocoate. Several of the fabrics were also washed without detergent since a previous study (Browne et al. 2011a), only reported results from garments washed with water alone, see Table 1.
Filtering of water
All laboratory materials used in this experiment were thoroughly rinsed to reduce risk of contamination, as were work stations. Wash water and rinse water from each fabric (n = 6 for each type of textile/treatment) were collected in glass beakers. Prior to filtering the water, the glass container was lightly shaken to remove fibers adhered to the sides of the bottle. A glass filter (Whatman GF/C, pore size 1.2 μm) with a pore size of 1.2 μm, diameter 42.5 mm, was placed in a vacuum filtration assembly with glass collection flask, attached to a vacuum pump. Water from one sample at the time was poured carefully through the filter, and samples flasks were rinsed with ultrapure milliQ water to assure that no fibers were lost on the sides. The filter was moved to a thoroughly rinsed glass petri dish with cover using a pincette, prior to microscopic analysis.
The glass-fiber filters were divided into four areas, and each of these areas was divided further into another four areas (total 16 areas on each filter). This was done to allow for easier and accurate manual counting of the fibers. Filters were analyzed using a Carl Zeiss: 475,002–9902 Lyca light microscope with a magnification of 40×. Fibers in each area were counted; the entire filter was assessed for samples with few fibers but only half of each filter was quantified in cases where samples released large numbers of fibers. For samples with a low number of fibers, all fibers were further classified and quantified by size on a scale from 1 to 5 where 1 was smallest and 5 was longest. In samples with a large amount of fibers, representative fibers were measured and classified within a limited number of areas on the filter. Size 1 = 0.025 mm–0.25 mm, size 2 = 0.25 mm–1 mm, size 3 = 1 mm–1.75 mm, size 4 = 1.75 mm–3 mm, and size 5 = > 3 mm.
In all cases, six fabric swatch replicates were used for each test (n = 6), unless otherwise indicated. Results showed unequal variance indicating the need for data transformation. T tests were used to compare results between two fabrics or treatments. ANOVA with repeated measures was used to test the effect of fiber loss during sequential washes. Group wise comparisons were conducted using ANOVA tests, α = 0.05. Student-Newman-Keuls post hoc analyses were applied. All data was subjected to Levine’s test of homogeneity of variances and normal distributions. All data was analyzed using SPSS 23.
Results and discussion
The results from our analyses indicated that, as we predicted, fleece fabrics do release a significantly greater number of fibers when washed, compared to the other knit fabrics (F = 72.982, 58; p < 0.001), allowing us to reject our first null hypothesis. These results are depicted in Fig. 1. The knit fabrics, averaged together, released 9 ± 7 fibers per 100 cm2 of fabric. Fleece and microfleece (fabrics H–J, see Table 1) did in fact release an average of 1177 ± 135, 932 ± 59, and 1210 ± 96 fibers, respectively, per 100 cm2 of fabric. This is a much greater amount than the 1900 fibers per garment previously reported (Browne et al. 2011a), but perhaps closer to levels more recently reported (700,000 fibers per 6 kg wash) (Napper and Thompson 2016). Typically, around 1m2 of fabric is used for a garment for adults giving a scaling factor of 100 for comparison between our 100 cm2 sample and an average garment, indicating that one fleece garment could release approximately 110,000 fibers. These values are however difficult to compare to previous studies since the authors did not report fabric area, weight, or water volume in all cases. The seven other fabrics tested here also released fibers, though at lower amounts, with an average of nine fibers per test or approximately 900 fibers per garment.
A comparison of the knit polyester fabrics knit with different techniques (labeled A-E, see Table 1) revealed significant differences (F = 48.044, 41; p < 0.001); our second null hypothesis can therefore be rejected. Post hoc testing revealed that two types of polyester knits tested, tightly knit polyester and a knit staple, released more fibers than the remaining three polyester fabrics. The following relationship between fabrics in terms of fibers shed: PET-4 > PET-S > PET-1, PET-2, PET-3. One polyester fabric (PET-4, E28 100/144) released twice as many fibers as three of the other fabrics knit from filament yarn (PET 1–3, or A–C in Table 1), indicating that materials knit from yarns with a greater number of exposed filaments per area shed more fibers compared to fabrics made with yarns with fewer filaments. Here, the needle gauge and the yarn are important factors contributing to the release of fibers. The degree of shedding is related to how tightly the yarn is knitted into the fabric. More tightly knitted fabric, as indicated by the knitting gauge (for example, DE28), results in more fibers on the same area of fabric resulting in a greater fiber loss. See Fig. 1a and Table 1. Sample E (PET staples, PET-S) was also found to have a larger degree of shedding than the first three polyester fabrics tested (A–C) indicating that the staple yarns may also be a less desirable structure, from an environmental perspective. This has implications for textile industries where efforts are being made to produce fabrics that shed less and are therefore more environmentally friendly. Our tests did not find any significant differences between the three different fleece fabrics tested here (F = 2.478, 17; p = 0.165), nor did we find a difference between nylon and acrylic fabrics. Nylon and acrylic fabrics were found to shed fibers in similar amounts to PET 1–3 (F = 1.848, 41; p = 0.082). See Fig. 1b, c.
The number of microplastic fibers released during washing could be impacted by aging of garments, i.e., through usage and passage of time. A recently published report, commissioned by Patagonia (producers of outdoor clothing) found that aged garments indeed shed higher masses of fibers than newer garments (Bruce et al. 2016), and we had hypothesized that this would be the case in the current study as well. Several fabrics were repolished to mimic wear and tear, and our results (in Fig. 2) indicate that repolishing fabrics generally resulted in greater fiber loss compared to non-repolished, i.e., new, fabrics. The total number of fibers released from the repolished fabrics was significantly larger for all tested materials with the exception of PET-1. These results are shown in Fig. 2. The p values obtained from t tests for four different PET knits (PET 1–4), nylon, and two fleece fabrics (PET-PtMF and PET-TMF) were as follows: 0.061, 0.013, 0.002, 0.041, 0.007, 0.013, and < 0.001, respectively. We also classified and quantified fibers of different size (categorized as class 1–5). We found that for polyester knits (PET 2–4) and PET staples, repolishing resulted in an increase in the release of longer fibers while the opposite was true for nylon and acrylic.
It is important to note that our results are obtained from fabrics washed using a commercially available detergent, a factor that we included and tested in our fifth null hypothesis. We conducted a comparison of the number of fibers shed from a selected fabrics washed with and without detergent. Our data (Fig. 3) indicate that washing with detergent results in a significant increase in amount of fibers released for three out of four fabrics tested; p values obtained from t tests were 0.011, < 0.001, 0.560, and < 0.001 for acrylic (A1), Tenson fleece (PET-TFL), Tenson microfleece (PET-TMF), and Polartech microfleece (PET-PtMF), respectively. In the past, estimates of fibers shed from textiles were done with water alone, as effluent water containing detergent proved difficult to analyze since filters would tend to clog (Browne et al. 2011a). In the current study, we improved rinsing and filtering methods, allowing for a more realistic assessment of effects of washing routines as well as a better comparison of our results with previous work (Browne et al. 2011a). A more recent study has also shown that more fibers tended to be released from fabrics washed with bio-detergent and conditioner (Napper and Thompson 2016). These increases in fiber loss with the use of detergent are likely dependent upon a fundamental property of detergents; they decrease the surface tension. Knitwear, consisting of woven loops, forms a fabric surface that acts like a cage which incorporates particles including loose fibers, but the low surface tension resulting from detergent use is essentially equivalent to “better” wetting which in turn results in improved rinsing of the fabric, and whatever particles that are held in the 3D knitwear network might be released. In addition to this wetting aspect, another fundamental property of detergents is that they act as dispersing agents; dirt is dissolved in the medium (water) and kept there, thereby prevented from falling back onto the fabric. This property applies to fiber fragments as well; most fibers that are released from the fabric are also transported away and have an increased chance of being detected in the subsequent analysis. Our results, in concurrence with a recent study (Napper and Thompson 2016), indicate that levels of fibers released during washing are much higher than previously estimated.
In order to further increase the accuracy and realism of our estimates of fiber release from PET fabrics, we repeatedly washed two of the fabrics, PET-3 and PET-4, and quantified the number of fibers released after two, five, and ten washes. These two fabrics were chosen for this experiment since they are among the most common types found in clothing, and showed a high degree of variation in number and sizes of fibers released in previous tests. Results, shown in Fig. 4, indicated that PET-4 released significantly greater numbers of fibers during each wash, compared to PET-3 (p < 0.01 for all four comparisons). The number of fibers released from PET-4 decreases significantly after repeated washes (F = 5.159, 3; p = 0.012), indicating that older clothing may release fewer fibers than new garments. This is also in concurrence with the results presented in recent studies (Napper and Thompson 2016; Pirc et al. 2016). However, since wear and tear increases fiber release, it is likely that fabrics will continue shedding as they age. We did not, unfortunately, test both of these parameters simultaneously.
The results presented in this study provide a strong indication that the shedding of fibers from clothing during washing is an important emitter of microplastics; our results, together with newly reported levels of shedding from fabrics (Napper and Thompson 2016; Pirc et al. 2016), confirm that previously reported levels were underestimated (Browne et al. 2011a). Downstream consequences of this have been addressed, but are not fully understood. Microplastic fibers are known to reach both aquatic and terrestrial environments via sewage; previous studies have shown that a large portion of plastic fibers may be removed during sewage treatment, from waste water to the sludge. Magnusson and coworkers reported 10.7 ± 0.39 and 4.00 ± 0.58 in 1 m3 incoming and effluent water, respectively (Magnusson et al. 2016; Magnusson and Wahlberg 2014). These studies have analyzed samples filtered through 300 μm filters (Magnusson and Wahlberg 2014), which could potentially lead to loss of small fibers and an underestimation of fiber levels in water.
While reported levels are substantial, estimating the relative importance of sewage effluent as a source of microplastics is difficult to estimate. There are a number of reports indicating the importance of urban areas on synthetic fibers in the environment (Browne et al. 2011a, b; Thompson et al. 2004), but we still lack knowledge about spatial and temporal distribution of microplastics, as well as accurate descriptions of particle compositions and breakdown in the environment. Nevertheless, there is enough evidence supporting a move toward caution. Reports on levels and effects of microplastics in the aquatic environment indicate real and potential threats (Galloway and Lewis 2016; Wright et al. 2013), but these are not limited to the water. Terrestrial environments also face threats; the accumulation of fibers in sludge is a possible risk factor; as microplastic fibers may spread via sewage (Habib et al. 1998; Zubris and Richards 2005) thereby contaminating land areas and impacting organisms (Huerta Lwanga et al. 2016; Palmqvist et al. 2016). Potential impacts on human health have also been discussed (Bouwmeester et al. 2015; Koch and Calafat 2009; Thompson et al. 2009).
Our current knowledge concerning microplastics in the environment, together with the knowledge concerning fiber shedding presented here, provides a starting point for increased efforts to reduce environmental contamination by microplastics. We find several potential points of release of fibers from fabrics, i.e., during production, which could be improved using straight forward strategies. This begins with the first steps of textile production where companies may be inspired to choose or develop knitting techniques that reduce fiber loss. Furthermore, yarn choice has an impact, with tightly constructed yarns as the preferred choice. While the decrease in release of fibers after the first wash was not significant for all materials studied here, it could still be interesting to encourage industries to wash textiles prior to clothing production, thereby potentially decreasing the amounts of fibers released into the environment during the consumer phase. (Collected fibers would of course need to be handled properly to avoid release into the environment). Washing and rinsing and subsequent drying are common processes within the textile industry, and since this infrastructure is already in place, the cost for the consumer would be highly moderate. The same goes for another suggestion, namely adding an in-line vacuum system through which the fabric could be passed subsequent to any of the brushing, sanding, raising processes that are common in the textile industry for getting a better hand and comfort, thereby eliminating loose fibers via air filtration and exhaustion. This could potentially be done quickly, at full production speed. There is currently no industry standardized testing or labeling of garments which provides information concerning fiber release from fabrics, and we suggest that this could be explored further.
Reduction of fiber loss once garments reach consumers could be addressed via appliance manufacturers of washers and dryers who are encouraged to develop means of preventing fiber loss in wash water effluent, as has been previously suggested (Browne 2015). Further, downstream, the installation of additional filters for outgoing sewage effluent could prevent these fibers from reaching the environment. Finally, individual consumers are encouraged to purchase fabrics that release fewer fibers, and perhaps to wash them less often; airing clothing in sunlight after use will often reduce the number of washes for certain types of garments (i.e., outerwear).
Aizenshtein EM (2012) Production and use of chemical fibers in 2010. Fibre Chem 43:395–405
Andrady AL (2011) Microplastics in the marine environment. Mar Pollut Bull 62:1596–1605
Bouwmeester H, Hollman PCH, Peters RJB (2015) Potential health impact of environmentally released micro- and nanoplastics in the human food production chain: experiences from nanotoxicology. Environ Sci Technol 49:8932–8947
Browne MA (2015) Sources and pathways of microplastics to habitats. In: Bergmann M, Gutow L, Klages M (eds) Marine anthropogenic litter. Springer International Publishing, Cham, pp 229–244
Browne MA, Galloway T, Thompson R (2007) Microplastic—an emerging contaminant of potential concern? Integr Environ Assess Manag 3:559–561
Browne MA, Crump P, Niven SJ, Teuten E, Tonkin A, Galloway T, Thompson R (2011a) Accumulation of microplastic on shorelines woldwide: sources and sinks. Environ Sci Technol 45:9175–9179
Browne MA, Galloway TS, Thompson RC (2011b) Spatial patterns of plastic debris along estuarine shorelines. Environ Sci Technol 44:3404–3409
Browne MA, Underwood AJ, Chapman MG, Williams R, Thompson RC, van Franeker JA (2015): Linking effects of anthropogenic debris to ecological impacts. Philos Trans R Soc B 282, 2014–2929
Bruce N, Hartline N, Karba S, Ruff B, Sonar S (2016) Microfiber pollution and the apparel industry. Bren School of Environmental Science and Management, Santa Barbara
Carmichael A (2015) Man-made fibers continue to grow. In: Borneman J (ed) Textile World Textile Industries Media Group, LLC, http://www.textileworld.com/Issues/2015/_2014/Fiber_World/Man-Made_Fibers_Continue_To_Grow
Cole M, Lindeque P, Halsband C, Galloway TS (2011) Microplastics as contaminants in the marine environment: a review. Mar Pollut Bull 62:2588–2597
Collignon A, Hecq J-H, Glagani F, Voisin P, Collard F, Goffart A (2012) Neustonic microplastic and zooplankton in the north western Mediterranean Sea. Mar Pollut Bull 64:861–864
De Witte B, Devriese L, Bekaert K, Hoffman S, Vandermeersch G, Cooreman K, Robbens J (2014) Quality assessment of the blue mussel (Mytilus edulis): comparison between commercial and wild types. Mar Pollut Bull 85:146–155
Della Torre C, Bergami E, Salvati A, Faleri C, Cirino P, Dawson KA, Corsi I (2014) Accumulation and embryotoxicity of polystyrene nanoparticles at early stage of development of sea urchin embryos Paracentrotus lividus. Environ Sci Technol 48:12302–12311
Desforges J-PW, Galbraith M, Ross PS (2015) Ingestion of microplastics by zooplankton in the Northeast Pacific Ocean. Arch Environ Contam Toxicol 69:320–330
Doustaneh AH, Sh M, Mohammadian M, Jahangir A (2013) The effects of weave structure and yarn fiber specification on pilling of woven fabrics. World Appl Sci J 24:503–506
Dris R, Gasperi J, Rocher V, Saad M, Renault N, Tassin B (2015) Microplastic contamination in an urban area: a case study in Greater Paris. Environ Chem 12:592–599
Duis K, Coors A (2016) Microplastics in the aquatic and terrestrial environment: sources (with a specific focus on personal care products), fate and effects. Environ Sci Eur 28:2
Enders K, Lenz R, Stedmon CA, Nielsen TG (2015) Abundance, size and polymer composition of marine microplastics ≥10 μm in the Atlantic Ocean and their modelled vertical distribution. Mar Pollut Bull 100:70–81
Essel R, Ahrens RH 2015 Sources of microplastics relevant to marine protection in Germany, nova-Institut GmbH
Galloway TS, Lewis CN (2016) Marine microplastics spell big problems for future generations. Proc Natl Acad Sci 113:2331–2333
GESAMP (2015) Sources, fate and effects of microplastics in the marine environment: a global assessment, Joint group of experts on the scientific aspects of marine environmental protection
Habib D, Locke DC, Cannone LJ (1998) Synthetic fibers as indicators of municipal sewage sludge, sludge products, and sewage treatment plant effluents. Water Air Soil Pollut 103:1–8
Hearle JWS, Morton WE (2008) Physical properties of textile fibres In: Hearle JWS (ed) Woodhead Publishing in Textiles A2 - Morton, W.E. Woodhead Publishing, pp. xv–xix
Hearle JWS, Lomas B, Cooke WD (1998) Textile processing and testing, other fibre studies. In: Hearle JWS (ed) Atlas of fibre fracture and damage to textiles (Second edition). Woodhead Publishing, pp. 465
Huerta Lwanga E, Gertsen H, Gooren H, Peters P, Salánki T, van der Ploeg M, Besseling E, Koelmans AA, Geissen V (2016) Microplastics in the terrestrial ecosystem: implications for Lumbricus terrestris (Oligochaeta, Lumbricidae). Environ Sci Technol 50:2685–2691
Jemec A, Horvat P, Kunej U, Bele M, Kržan A (2016) Uptake and effects of microplastic textile fibers on freshwater crustacean Daphnia magna. Environ Pollut 219:201–209
Koch HM, Calafat AM (2009) Human body burdens of chemicals used in plastic manufacture. Philos Trans R Soc B Biol Sci 364:2063
Lambert S, Wagner M (2016) Characterisation of nanoplastics during the degradation of polystyrene. Chemosphere 145:265–268
Lee K-W, Shim WJ, Kwon OY, Kang J-H (2013) Size-dependent effects of micro polystyrene particles in the marine copepod Tigriopus japonicus. Environ Sci Technol 47:11278–11283
Leslie HA, van Velzen MJM, Vethaak AD (2013) Microplastic survey of the Dutch environment. Novel data set of microplastics in North Sea sediments, treated wastewater effluents and marine biota, The Netherlands
Liebezeit G, Liebezeit E (2013) Non-pollen particulates in honey and sugar. Food Addit Contam A 30:2136–2140
Liebezeit G, Liebezeit E (2014) Synthetic particles as contaminants in German beers. Food Addit Contam A 31:1574–1578
Lu Y, Zhang Y, Deng Y, Jiang W, Zhao Y, Geng J, Ding L, Ren H-q (2016) Uptake and accumulation of polystyrene microplastics in zebrafish (Danio rerio) and toxic effects in liver. Environ Sci Technol
Lusher AL, McHugh M, Thompson RC (2013) Occurrence of microplastics in the gastrointestinal tract of pelagic and demersal fish from the English Channel. Mar Pollut Bull 67:94–99
Magnusson K, Norén F (2014) Screening of microplastic partiles in and down-stream a wastewater treatment plant, Swedish Environmental Protection Agency
Magnusson K, Wahlberg C (2014) Mikroskopiska skräppartiklar i vatten från avloppsreningsverk, IVL - Swedish Environmental Institute
Magnusson K, Eliasson K, Fråne A, Haikonen K, Hultén J, Olshammar M, Stadmark J, Voisin A (2016) Swedish sources and pathways for microplastics to the marine environment, a review of existing data. IVL- Swedish Environmental Research Institute, Stockholm
Mathalon A, Hill P (2014) Microplastic fibers in the intertidal ecosystem surrounding Halifax Harbor, Nova Scotia. Mar Pollut Bull 81:69–79
Murphy F, Ewins C, Carbonnier F, Quinn B (2016) Wastewater treatment works (WwTW) as a source of microplastics in the aquatic environment. Environ Sci Technol 50:5800–5808
Napper IE, Thompson RC (2016) Release of synthetic microplastic plastic fibres from domestic washing machines: effects of fabric type and washing conditions. Mar Pollut Bull
Org. PE (2015) Plastics—the facts 2015
Palmqvist A, Magid J, Syberg K (2016) Does microplastic in recycled organic resources pose a risk to terrestrial environments? SETAC, Society for Environmental Toxicology and Chemsitry, Nantes
Pirc U, Vidmar M, Mozer A, Kržan A (2016) Emissions of microplastic fibers from microfiber fleece during domestic washing. Environ Sci Pollut Res 23:22206–22211
Remy F, Collard F, Gilbert B, Compère P, Eppe G, Lepoint G (2015) When microplastic is not plastic: the ingestion of artificial cellulose fibers by macrofauna living in seagrass Macrophytodetritus. Environ Sci Technol 49:11158–11166
Rochman CM, Hoh E, Kurobe T, Teh SJ (2013) Ingested plastic transfers hazardous chemicals to fish and induces hepatic stress. Sci Rep 3
Rochman CM, Kurobe T, Flores I, Teh SJ (2014) Early warning signs of endocrine disruption in adult fish from the ingestion of polyethylene with and without sorbed chemical pollutants from the marine environment. Sci Total Environ 493:656–661
Rochman CM, Tahir A, Williams SL, Baxa DV, Lam R, Miller JT, Teh F-C, Werorilangi S, Teh SJ (2015) Anthropogenic debris in seafood: plastic debris and fibers from textiles in fish and bivalves sold for human consumption. Sci Rep 5:14340
Rochman CM, Browne MA, Underwood AJ, van Franeker JA, Thompson Richard C, Amaral-Zettler LA (2016) The ecological impacts of marine debris: unraveling the demonstrated evidence from what is perceived. Ecology 97:302–312
Sussarellu R, Suquet M, Thomas Y, Lambert C, Fabioux C, Pernet MEJ, Le Goïc N, Quillien V, Mingant C, Epelboin Y, Corporeau C, Guyomarch J, Robbens J, Paul-Pont I, Soudant P, Huvet A (2016) Oyster reproduction is affected by exposure to polystyrene microplastics. Proc Natl Acad Sci 113:2430–2435
Talvitie J, Mikola A, Koistinen A, Setälä O (2017) Solutions to microplastic pollution—removal of microplastics from wastewater effluent with advanced wastewater treatment technologies. Water Res 123:401–407
Thompson RC, Olsen Y, Mitchell RP, Davis A, Rowland SJ, John AWG, McGonigle D, Russell AE (2004) Lost at sea: where is all the plastic? Science 304:838
Thompson RC, Moore CJ, vom Saal FS, Swan SH (2009) Plastics, the environment and human health: current consensus and future trends. Philos Trans R Soc B Biol Sci 364:2153–2166
Weinstein JE, Crocker BK, Gray AD (2016) From macroplastic to microplastic: degradation of high-density polyethylene, polypropylene, and polystyrene in a salt marsh habitat. Environ Toxicol Chem 35:1632–1640
Wright SL, Thompson RC, Galloway TS (2013) The physical impacts of microplastics on marine organisms: a review. Environ Pollut 178:483–492
Yang D, Shi H, Li L, Li J, Jabeen K, Kolandhasamy P (2015) Microplastic pollution in table salts from China. Environ Sci Technol 49:13622–13627
Zubris KAV, Richards BK (2005) Synthetic fibers as an indicator of land application of sludge. Environ Pollut (Barking, Essex : 1987) 138:201–211
The authors would like to thank Ann Åström for important contributions and discussions in the design of the study; her input was valuable. We would also like to thank Ulrika Marklund for useful input into this study and the anonymous reviewers who provided useful comments on the manuscript. We are also thankful for funding from The Swedish Research Council, Formas, and the European Regional Development Fund, Interreg, in Öresund-Kattegat-Skagerrak.
• Fleece fabric shed significantly more fibers than other knits.
• PET fleece sheds an estimated 110,000 fibers per garment and wash.
• All fabrics shed fibers, but no significant difference was found between nylon, acrylic, and PET knits.
• More loosely knit textile construction resulted in greater fiber loss.
• Shedding of fibers can potentially be mitigated with smarter textile construction.
Responsible editor: Philippe Garrigues
About this article
Cite this article
Carney Almroth, B.M., Åström, L., Roslund, S. et al. Quantifying shedding of synthetic fibers from textiles; a source of microplastics released into the environment. Environ Sci Pollut Res 25, 1191–1199 (2018). https://doi.org/10.1007/s11356-017-0528-7
- Synthetic textiles