Abstract
The tribological properties of a-C:H coating sliding against a SUJ2 ball, a SUJ2 roller, and an a-C:H coated roller were investigated under temperatures ranging from 20 to 80 °C in PAO with different additives. The additives had a glycerol and hydroxyl functional group in one molecule to enhance additive adsorption for mating with the a-C:H coating disk material and to build a phosphorus oxide tribolayer. Additives with different numbers of hydroxyl groups and primary or secondary-type C6H13O structures were also prepared. The tribolayer derived from each additive was analyzed via EDS, XPS, and ToF-SIMS. XPS depth analysis for the tribolayers revealed that additives were dissociated by friction and suggested C–O bond cleavage occurred.
Graphical Abstract
Similar content being viewed by others
References
Murashima, M., Imaizumi, Y., Murase, R., Umehara, N., Tokoroyama, T., Saito, T., Takeshima, M.: Active friction control in lubrication condition using novel metal morphing surface. Tribol. Int. 156 (2021). https://doi.org/10.1016/j.triboint.2020.106827
Murashima, M., Imaizumi, Y., Kawaguchi, M., Umehara, N., Tokoroyama, T., Saito, T., Takeshima, M., Ttukiyama, Y., Nitta, I.: Realization of a novel morphing surface using additive manufacturing and its active control in friction. J. Tribol. 143 (2021). https://doi.org/10.1115/1.4050269
Lee, W.Y., Tokoroyama, T., Jang, Y.J., Umehara, N.: Effect of substrate bias and temperature on friction and wear properties for ta-C coating prepared under different substrate bias voltages with filtered cathodic vacuum arc deposition. Tribology Online 13(5), 241–247 (2018). https://doi.org/10.2474/trol.13.241
Lee, W.Y., Tokoroyama, T., Jang, Y.J., Umehara, N.: Investigating running-in behavior to understand wear behavior of ta-C coating with filtered cathodic vacuum arc deposition. J. Tribol. 23, 38–47 (2019)
Lee, W.Y., Jang, Y.J., Umehara, N., Tokoroyama, T., Murashima, M.: Effect of defects on wear behavior in ta-C coating prepared by filtered cathodic vacuum arc deposition. Diam. Relat. Mater. 105 (2020). https://doi.org/10.1016/j.diamond.2020.107789
Mustafa, M.M.B., Umehara, N., Tokoroyama, T., Murashima, M., Shibata, A., Utsumi, Y., Moriguchi, H.: Effect of pillar and mesh structure of tetrahedral amorphous carbon ta-C coatings on the wear properties and fracture toughness of the coating. Tribology Online 14(5), 388–397 (2019). https://doi.org/10.2474/trol.14.388
Deng, X., Kousaka, H., Tokoroyama, T., Umehara, N.: Tribological behaviors of tetrahedral amorphous carbon (ta-C) coatings at elevated temperature. Tribol. Int. 75, 98–103 (2014). https://doi.org/10.1016/j.triboint.2014.04.002
Deng, X., Kousaka, H., Tokoroyama, T., Umehara, N.: Thermal stabiligy and high-temperature tribological properties of a-C: H and Si-DLC deposited by microwave sheath voltage combination plasma. Tribology Online 8, 257–264 (2013). https://doi.org/10.2474/trol.8.257
Taib, M.T.B., Umehara, N., Tokoroyama, T., Murashima, M.: The effects of oil additives and mating materials to the friction, wear and seizure characteristics of a-C: H coating. J. Tribol. 18, 1–19 (2018)
Nyberg, H., Tokoroyama, T., Wiklund, U., Jacobson, S.: Design of low-friction PVD coating systems with enhanced running-in performance - carbon overcoats on TaC/aC. Surf. Coat. Technol. 222, 48–54 (2013). https://doi.org/10.1016/j.surfcoat.2013.02.003
Deng, X., Kousaka, H., Tokoroyama, T., Umehara, N.: Deposition and tribological behaviors of ternary BCN coatings at elevated temperatures. Surf. Coat. Technol. 259, 2–6 (2014). https://doi.org/10.1016/j.surfcoat.2014.08.087
Taib, M.T.B., Umehara, N., Tokoroyama, T.: Murashima M, The effect of UV irradiation to a-C: H on friction and wear properties under PAO oil lubrication including MoDTC and ZnDTP. Tribology Online 13(3), 119–130 (2018). https://doi.org/10.2474/trol.13.119
Tasdemir, H.A., Wakayama, M., Tokoroyama, T., Kousaka, H., Umehara, N., Mabuchi, Y., Higuchi, T.: Wear behaviour of tetrahedral amorphous diamond-like carbon in additive containing lubricants. Wear 307(1–2), 1–9 (2013). https://doi.org/10.1016/j.wear.2013.08.011
Aboua, K.A.M., Umehara, N., Kousaka, H., Tokoroyama, T., Murashima, M., Tasdemir, H.A., Mabuchi, Y., Higuchi, T.: Effect of ZnDTP triboflim’s morphology on friction behaviors of DLC coatings: tribofilm characterization by 3D scanning electron microscope observation. JAMDSM 12, 7 (2018). https://doi.org/10.1299/jamdsm.2018jamdsm0129
Kassim, K.A.M., Tokoroyama, T., Murashima, M., Umehara, N.: The wear classification of molybdenum-derived particles on silicon and hydrogenated diamond-like carbon at room temperature. Tribol. Int. 147 (2020). https://doi.org/10.1016/j.triboint.2020.106176
Kassim, K.A.M., Tokoroyama, T., Murashima, M., Lee, W.-Y., Umehara, N., Mustafa, M.M.B.: Wear acceleration of a-C:H coatings by molybdenum-derived particles: mixing and temperature effects. Tribol. Int. 159 (2021). https://doi.org/10.1016/j.triboint.2021.106944
Espejo, C., Thiebaut, B., Jarnias, F., Wang, C., Neville, A., Morina, A.: MoDTC tribochemistry in steel/steel and steel/diamond-like-carbon systems lubricated with model lubricants and fully formulated engine oils. ASME J. Tribol. 141, 12 (2019). https://doi.org/10.1115/1.4041017
Ohara, K., Hanyuda, K., Kawamura, Y., Omura, S., Kameda, I., Umehara, N., Kousaka, H.: Analysis of wear track on DLC coatings after sliding with MoDTC-containing lubricants. Tribology Online 12 (2017). https://doi.org/10.2474/trol.12.110
Ohara, K., Masuripan, N.A.B., Umehara, N., Kousaka, H., Tokoroyama, T., Inami, S., Zushi, K., Fujita, M.: Evaluation of transformed layers of DLC after sliding in oil with spectroscopic reflectometry. Tribol. Int. 65, 270–277 (2013). https://doi.org/10.1016/j.triboint.2013.01.010
Tasdemir, H.A., Tokoroyama, T., Kousaka, H., Umehara, N., Mabuchi, Y.: Influence of zinc dialkyldithiophosphate tribofilm formation on the tribological performance of self-mated diamond-like carbon contacts under boundary lubrication. Thin Solid Film 562(1), 389–397 (2014)
Masripan, N.A.B., Ohara, K., Umehara, N., Kousaka, H., Tokoroyama, T., Inami, S., Zushi, K., Fujita, M.: Hardness effect of DLC on tribological properties for sliding bearing under boundary lubrication condition in additive-free mineral base oil. Tribol. Int. 65, 265–269 (2013). https://doi.org/10.1016/j.triboint.2013.01.016
Liu, X., Yamaguchi, R., Umehara, N., Murashima, M., Tokoroyama, T.: Effect of oil temperature and counterpart material on the wear mechanism of ta-CNx coating under base oil lubrication. Wear 390, 312–21 (2017)
Kosarieh, S., Morina, A., Laine, E., Flemmig, J., Neville, A.: The effect of MoDTC-type friction modifier on the wear performance of a hydrogenated DLC coating. Wear 302, 890–898 (2013). https://doi.org/10.1016/j.wear.2012.12.052
De Feo, M., De Barros Bouchet, M.I., Minfray, C., Le Mogne, Th., Meunier, F., Yang, L., Thiebaut, B., Martin, J.M.: MoDTC lubrication of DLC-involving contacts. Impact of MoDTC degradation. Wear 348–349, 116–125 (2016). https://doi.org/10.1016/j.wear.2015.12.001
Mustafa, M.M.B., Umehara, N., Tokoroyama, T., Murashima, M., Shibata, A., Utsumi, Y., Moriguchi, H.: Effect of mesh structure of tetrahedral amorphous carbon ta-C coating on friction and wear properties under base-oil lubrication condition. Tribol. Int. 147 (2020). https://doi.org/10.1016/j.triboint.2019.01.016
Abdollah, M.F.B., Yamaguchi, Y., Akao, T., Inayoshi, N., Umehara, N., Tokoroyama, T.: Phase Transformation Studies on a-C Coating under Repetitive Impacts. Surf. Coat. Technol. 205(2), 625–631 (2010). https://doi.org/10.1016/j.surfcoat.2010.07.062
Abdollah, M.F.B., Yamaguchi, Y., Akao, T., Inayoshi, N., Miyamoto, N., Tokoroyama, T., Umehara, N.: Deformation-wear transition map of DLC coating under cyclic impact loading. Wear 274–275(27), 435–441 (2012). https://doi.org/10.1016/j.wear.2011.11.007
Nishimura, H., Umehara, N., Kousaka, H., Tokoroyama, T.: Clarification of relationship between friction coefficient and transformed layer of CNx coating by in-situ spectroscopic analysis. Tribol. Int. 93, 660–665 (2016). https://doi.org/10.1016/j.triboint.2014.12.015
Tokoroyama, T., Murashima, M., Umehara, N.: The Surface Enhanced Raman Scattering analysis for carbonaceous coating by using Au Nano-Particles. Tribology 15, 300–308 (2020). https://doi.org/10.1016/j.triboint.2014.12.015
Liu, X., Umehara, N., Tokoroyama, T., Murashima, M.: Tribological properties of ta-CNx coating sliding against steel and sapphire in unlubricated condition. Tribol. Int. 131, 102–111 (2019). https://doi.org/10.1016/j.triboint.2018.10.022
Tokoroyama, T., Goto, M., Umehara, N., Nakamura, T., Honda, F.: Effect of Nitrogen atoms desorption on the friction of the CNx coating against Si3N4 ball in Nitrogen gas. Tribol. Lett. 22, 215–220 (2004). https://doi.org/10.1007/s11249-006-9084-x
Tokoroyama, T., Kamiya, M., Umehara, N., Wang, C., Diao, D.F.: Influence of UV irradiation for low friction performance of CNx coatings. Lubr. Sci. 24, 129–139 (2012). https://doi.org/10.1002/ls.1168
Tokoroyama, T., Hattori, T., Umehara, N., Kousaka, H., Manabe, K., Kishi, M., Fuwa, Y.: Ultra-low friction properties of carbon nitride tantalum coatings in the atmosphere. Tribol. Int. 103, 388–393 (2016). https://doi.org/10.1016/j.triboint.2016.07.015
Tokoroyama, T., Tagami, Y., Murashima, M., Lee, W.Y., Umehara, N., Kousaka, H.: Tribological property of ta-CNx: Ta deposited via ion beam assisted-filtered arc deposition. Tribol. Int. 168 (2022). https://doi.org/10.1016/j.triboint.2022.107450
Aboua, K.A.M., Umehara, N., Kousaka, H., Tokoroyama, T., Murashima, M., Mabuchi, Y., Higuchi, T., Kawaguchi, M.: Effect of carbon diffusion on friction and wear behaviors of diamond-like carbon coating against Cr-plating in boundary base oil lubrication. Tribology Online 13, 290–300 (2018). https://doi.org/10.2474/trol.13.290
Aboua, K.A.M., Umehara, N., Kousaka, H., Tokoroyama, T., Murashima, M., Mabuchi, M., Higuchi, T., Kawaguchi, M.: Effect of carbon diffusion on friction and wear behaviors of diamond-like carbon coating against germanium in boundary base oil lubrication. Triblogy Lett. 67, 65 (2019). https://doi.org/10.1007/s11249-019-1179-2
Aboua, K.A.M., Umehara, N., Kousaka, H., Tokoroyama, T., Murashima, M., Mustafa, M.M.B., Mabuchi, Y., Higuchi, T., Kawaguchi, M.: Effect of mating material and graphitization on wear of a-C: H coating in boundary base oil lubrication. Tribol. Lett. 68, 24 (2020). https://doi.org/10.1007/s11249-019-1248-6
Kano, M., Yasuda, Y., Okamoto, Y., Mabuchi, Y., Hamada, T., Ueno, T., Ye, J., Konishi, S., Takeshima, S., Martin, J.M., De Barros Bouchet, M.I., Le Mogne, Th.: Ultralow friction of DLC in presence of glycerol mono-oleate (GNO). Tribol. Lett. 18, 245 (2005). https://doi.org/10.1007/s11249-004-2749-4
Tasdemir, H.A., Wakayama, M., Tokoroyama, T., Kousaka, H., Umehara, N., Mabuchi, Y., Higuchi, T.: Ultra-low friction of tetrahedral amorphous diamond-like carbon (ta-C DLC) under boundary lubrication in poly alpha-olefin (PAO) with additives. Tribol. Int. 65, 286–294 (2013). https://doi.org/10.1016/j.triboint.2013.03.014
Tasdemir, H.A., Wakayama, M., Tokoroyama, T., Kousaka, H., Umehara, N., Mabuchi, Y., Higuchi, T.: The effect of oil temperature and additive concentration on the wear of non-hydrogenated DLC coating. Tribol. Int. 77, 65–71 (2014). https://doi.org/10.1016/j.triboint.2014.04.015
Kani, T., Tokoroyama, T., Umehara, N., Murashima, M., Lee, W.Y., Yagishita, K.: The tribological properties of hydrogenated DLC coating lubrication with additive having glycerol and phosphonate structure. Tribology Online 16(4), 263–270 (2021). https://doi.org/10.2474/trol.16.263
Mezzi, A., Kaciulis, S.: Surface investigation of carbon films: from diamond to graphite. Surf. Int. Anal. 42, 1082–1084 (2010). https://doi.org/10.1002/sia.3348
Kaciulis, S.: Spectroscopy of carbon: from diamond to nitride films. Surf. Int. Anal. 48, 92 (2012). https://doi.org/10.1002/sia.4892
Mangolini, F., Rossi, A., Spencer, N.D.: Chemical reactivity of triphenyl phosphorothionate (TPPT) with ion: An ATR/FT-IR and XPS investigation. J. Phys. Chem. 155, 1339–1354 (2011). https://doi.org/10.1021/jp107617d
Torres-Ceron, D.A., Amaya-Roncancio, S., Riva, J.S., Vargas-Eudor, A., Escobar-Rincon, D., Restre-Parra, E.: Incorporation of P5+ and P3– from phosphate precursor in TiO2:P coatings produced by PEO:XPS and DFT study. Surf. Coat. Technol. 421 (2021). https://doi.org/10.1016/j.surfcoat.2021.127437
Shih, P.Y., Yung, S.W., Chin, T.S.: FTIR and XPS studies of P2O5–Na2O–CuO glasses. J. Non-Crystal Sol. 244, 211–22 (1999). https://doi.org/10.1016/S0022-3093(99)00011-3
Ewen, J.P., Latorre, C.A., Gattinoni, C., Khajeh, A., Moore, J.D., Remias, J.E., Martini, A., Dini, D.: Substituent effects on the thermal decomposition of phosphate esters on ferrous surfaces. J. Phys. Chem. C 124, 9852–9865 (2020). https://doi.org/10.1021/acs.jpcc.9b11787
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interest
The authors have no relevant financial or nonfinancial interests to disclose.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Tokoroyama, T., Tanaka, K., Kani, T. et al. The Tribological Property of a-C:H Coating with Tribolayer by Additive Having Glycerol and Phosphate Oxide Structure. Tribol Lett 70, 118 (2022). https://doi.org/10.1007/s11249-022-01659-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11249-022-01659-3