Abstract
In this work we have studied the adsorption of water on TiC-coated quartz crystals to evaluate the use of TiC as a potential candidate for overcoats on magnetic media. It was observed that at room temperature the amount of adsorbed water onto thick sputtered TiC films, up to 20 nm in thickness, was similar to the amount of water adsorbed on standard amorphous 1.0–5.0 nm thick CHx films, which are currently used as protective overcoats on magnetic media. The sputtered TiC lubricated with Fomblin ZO3 in Vertrel XF solution also shows similar amounts of water adsorption as compared to unlubricated CH x films. The amount of water adsorbed on TiC and CH x films was measured in-situ by a quartz-crystal microbalance apparatus in an ultra-high vacuum chamber.
Similar content being viewed by others
References
S. V. Dudiy and B. I. Lundqvist, Phys. Rev. B 64 (2001) 045403.
S. V. Dudiy, L. Hartford and B. I. Lundqvist, Phys. Rev. Lett. 85 (2000) 1898.
Q. Dai and G. Vurens, Langmuir 13 (1997) 4401.
Z. Zhao and B. Bhusan, Proceedings of the Institution of Mechanical Engineers, Part J: J. Eng. Tribol. 211 (1997) 295.
S. S. Perry, G. A Somarjai, C. M. Mate and R. White, Tribol. Lett. 1 (1995) 47.
B. D. Strom, D. B. Bogy, C. S. Bhatia and B. Bhusan, J. Tribol. 113 (1991) 689.
T. E. Karis, J. Colloid Inter. Sci. 225 (2000) 196.
M. Smallen, J. K. Lee, A Chao and J. Enguero, IEEE T. Magn. 30(6) (1994) 4137.
N. Shukla, E. B. Svedberg, R. J. M. van de Veerdonk, X. Ma, J. Gui and A. J. Gellman, Tribol. Lett. 15(1) (2003) 9.
R. P. Chiarello, J. Krim and C. Thompson, Surf. Sci. 306 (1994) 359.
C. L. Wang and J. Krim, JVSTA A7 (1989) 2481.
J. Krim, E. T. Watts and J. Digel, JVSTA 8 (1990) 3417.
P. B. Merrill, S. S. Perry, P. Frantz and S. V. Didziulis, J. Phys. Chem. B 102 (1998) 7606.
N. Shukla, A. J. Gellman, X. Ma and J. Gui, Tribol. Lett. 12(2) (2002) 105.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Svedberg, E.B., Shukla, N. Adsorption of Water on Lubricated and Non Lubricated TiC Surfaces for Data Storage Applications. Tribology Letters 17, 947–951 (2004). https://doi.org/10.1007/s11249-004-8107-8
Issue Date:
DOI: https://doi.org/10.1007/s11249-004-8107-8