Durability of a Stress Concentrator-Containing Cantilever Beam Under Cyclic Loading in Bending

  • Published:
Strength of Materials Aims and scope

The procedure and results of studies on the durability of the cantilever beam metal over the stress concentrator area in pulsed cyclic bending are presented. Comparison of experimental and numerical simulation data resulted in establishing the relation between the durability and cyclic inelastic strain amplitude. The effect of strain hardening and plastic strains on durability was elucidated.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. N. A. Makhutov and M. M. Gadenin, “Substantiation of strength, lifetime, reliability, and safety of hydroelectric plants,” in: Enhancement of Reliability and Operating Efficiency of Power Plants and Energy Systems [in Russian], Proc. All-Russian Practical-Scientific Conf. (June 1–3, 2010, Moscow), MÉI, Moscow (2010), pp. 201–205.

  2. A. S. Kurkin and G. P. Batov, “Plastic limit – universal local criterion fracture characteristic for lifetime assessment of welded structures,” Zavod. Lab., 76, No. 6, 45–54 (2010).

    Google Scholar 

  3. PNAÉ G-7-002-86. Norms of Strength Calculations for the Equipment and Pipelines of Atomic Power Plants [in Russian], Énergoatomizdat, Moscow (1989).

  4. Yu. G. Dragunov, A. S. Zubchenko, O. Yu. Petrova, and I. L. Kharina, “Effect of high-parameter water on the tendency of 10GN2MFA steel to decelerated deformation corrosion cracking,” Mashinostr. Inzh. Obraz., No. 4, 35–41 (2007).

  5. N. G. Chausov, A. A. Lebedev, L. V. Zaitseva, and A. V. Getmanchuk, “Effect of the form of stressed state on the kinetics of damage accumulation and crack resistance of body steel 15Kh2MFA under different conditions. Communication 1. Stagewise process of steel KP60 failure,” Strength Mater., 25, No. 3, 157–162 (1993).

    Google Scholar 

  6. G. V. Stepanov, Elastoplastic Deformation and Fracture of Materials under Pulse Loading [in Russian], Naukova Dumka, Kiev (1991).

    Google Scholar 

  7. ANSYS HTML. Online Documentation, SAS IP Inc. (2005).

  8. V. T. Troshchenko (Ed.), Deformation and Fracture Resistance of Materials. Handbook [in Russian], Part 1, Naukova Dumka, Kiev (1993).

Download references

Author information

Authors and Affiliations

  1. Pisarenko Institute of Problems of Strength, National Academy of Sciences of Ukraine, Kiev, Ukraine

    G. V. Stepanov & I. A. Mameev

Authors
  1. G. V. Stepanov
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. I. A. Mameev
    View author publications

    You can also search for this author in PubMed Google Scholar

Additional information

Translated from Problemy Prochnosti, No. 4, pp. 43 – 49, July – August, 2014.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Stepanov, G.V., Mameev, I.A. Durability of a Stress Concentrator-Containing Cantilever Beam Under Cyclic Loading in Bending. Strength Mater 46, 477–482 (2014). https://doi.org/10.1007/s11223-014-9572-4

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11223-014-9572-4

Keywords

Search

Navigation