Graphene oxide supported tin dioxide: synthetic approaches and electrochemical characterization as anodes for lithium- and sodium-ion batteries

Abstract

The review addresses synthetic approaches to composite materials based on graphene oxide and nano tin dioxide and their electrochemical properties as anodes for lithium- and sodiumion batteries. The introduction of a carbon matrix into the composite material improves the electrochemical characteristics of the anodes. In most methods, the synthesis of graphene oxide–tin dioxide composites is based on the use of tin(II,IV) chlorides as the starting compounds, and the most efficient electrode materials were obtained by the hydrothermal or solvothermal routes. Thermal processing is much more economic than the gas phase deposition protocols but requires heating of a large volume of dilute tin oxide dispersions in an autoclave. Mechanochemistry (ball milling) is also economically unfavorable for the synthesis of composite materials. In addition, large volumes of acidic wastes that should be neutralized and safely discarded are formed when tin chlorides are used. An alternative environmentally friendly technique based on the use of aqueous peroxide solutions can be applied for the production of efficient anode materials based on graphene oxide and tin dioxide. This process does not involve acidic wastes, uses hydrogen peroxide and ethanol as reagents, and accomplishes film deposition (coating) at room temperature. Final thermal treatment is required only for the active material, which minimizes energy expenses and equipment costs.

This is a preview of subscription content, log in to check access.

References

  1. 1.

    M. Armand, J. M. Tarascon, Nature, 2008, 451,652.

    Article  CAS  PubMed  Google Scholar 

  2. 2.

    J. B. Goodenough, Y. Kim, Chem. Mater., 2010, 22,587.

    Article  CAS  Google Scholar 

  3. 3.

    J. M. Tarascon, M. Armand, Nature, 2001, 414,359.

    Article  CAS  PubMed  Google Scholar 

  4. 4.

    V. Etacheri, R. Marom, R. Elazari, G. Salitra, D. Aurbach, Energy Environ. Sci., 2011, 4, 3243.

    Article  CAS  Google Scholar 

  5. 5.

    J. B. Goodenough, K.-S. Park, J. Am. Chem. Soc., 2013, 135, 1167.

    Article  CAS  PubMed  Google Scholar 

  6. 6.

    S. M. Rezvanizaniani, Z. Liu, Y. Chen, J. Lee, J. Power Sources, 2014, 256,110.

    Article  CAS  Google Scholar 

  7. 7.

    L. Lu, X. Han, J. Li, J. Hu, M. Ouyang, J. Power Sources, 2013, 226,272.

    Article  CAS  Google Scholar 

  8. 8.

    J. Jaguemont, L. Boulon, Y. Dube, Appl. Energy, 2016, 164,99.

    Article  CAS  Google Scholar 

  9. 9.

    J.-Y. Hwang, S.-T. Myung, Y.-K. Sun, Chem. Soc. Rev., 2017, 46, 3529.

    Article  CAS  PubMed  Google Scholar 

  10. 10.

    K. Kubota, S. Komaba, J. Electrochem. Soc., 2015, 162, A2538.

    Article  CAS  Google Scholar 

  11. 11.

    H. Pan, Y.-S. Hu, L. Chen, Energy Environ. Sci., 2013, 6, 2338.

    Article  CAS  Google Scholar 

  12. 12.

    Lithium-Ion Batteries, Eds M. Yoshio, R. J. Brodd, A. Kozawa, Springer, New York, 2009, 452 pp.

  13. 13.

    D. Aurbach, B. Markovsky, I. Weissman, E. Levi, Y. Ein-Eli, Electrochim. Acta, 1999, 45,67.

    Article  CAS  Google Scholar 

  14. 14.

    N. Nitta, F. Wu, J. T. Lee, G. Yushin, Mater. Today, 2015, 18,252.

    Article  CAS  Google Scholar 

  15. 15.

    D. Aurbach, Y. Talyosef, B. Markovsky, E. Markevich, E. Zinigrad, L. Asraf, J. S. Gnanaraj, H.-J. Kim, Electrochim. Acta, 2004, 50,247.

    Article  CAS  Google Scholar 

  16. 16.

    S. S. Zhang, J. Power Sources, 2006, 162, 1379.

    Article  CAS  Google Scholar 

  17. 17.

    S.-W. Kim, D.-H. Seo, X. Ma, G. Ceder, K. Kang, Adv. Energy Mater., 2012, 2,710.

    Article  CAS  Google Scholar 

  18. 18.

    N. Yabuuchi, K. Kubota, M. Dahbi, S. Komaba, Chem. Rev., 2014, 114, 11636.

    Article  CAS  PubMed  Google Scholar 

  19. 19.

    H. Y. Kang, Y. C. Liu, K. Z. Cao, Y. Zhao, L. F. Jiao, Y. J. Wang, H. T. Yuan, J. Mater. Chem. A, 2015, 3, 17899.

    Article  CAS  Google Scholar 

  20. 20.

    T. L. Kulova, A. M. Skundin, Elektrokhim. Energetika [Electro chemical Power Engineering], 2016, 16, 122 (in Russian).

    Google Scholar 

  21. 21.

    T. L. Kulova, A. M. Skundin, Russ. Chem. Bull., 2017, 66, 1329.

    Article  CAS  Google Scholar 

  22. 22.

    D. A. Stevens, J. R. Dahn, J. Electrochem. Soc., 2000, 147, 1271.

    Article  CAS  Google Scholar 

  23. 23.

    S. Komaba, W. Murata, T. Ishikawa, N. Yabuuchi, T. Ozeki, T. Nakayama, A. Ogata, K. Gotoh, K. Fujiwara, Adv. Funct. Mater., 2011, 21, 3859.

    Article  CAS  Google Scholar 

  24. 24.

    M. A. Munoz-Marquez, D. Saurel, J. L. Gomez-Camer, M. Casas-Cabanas, E. Castillo-Martinez, T. Rojo, Adv. Funct. Mater., 2017, 7, 1700463.

    Google Scholar 

  25. 25.

    Y. Kim, K.-H. Ha, S. M. Oh, K. T. Lee, Chem. Eur. J., 2014, 20, 11980.

    Article  CAS  PubMed  Google Scholar 

  26. 26.

    P. G. Balakrishnan, R. Ramesh, T. P. Kumar, J. Power Sources, 2006, 155,401.

    Article  CAS  Google Scholar 

  27. 27.

    B. Barnett, D. Ofer, S. Sriramulu, R. Stringfellow, in Batteries for Sustainability, Ed. R. Brodd, Springer, New York, 2013, p.285.

  28. 28.

    M. Winter, J. O. Besenhard, Electrochim. Acta, 1999, 45,31.

    Article  CAS  Google Scholar 

  29. 29.

    R. Demir-Cakan, Y.-S. Hu, M. Antonietti, J. Maier, M.-M. Titirici, Chem. Mater., 2008, 20, 1227.

    Article  CAS  Google Scholar 

  30. 30.

    Z. Chen, M. Zhou, Y. Cao, X. Ai, H. Yang, J. Liu, Adv. Energy Mater., 2012, 2,95.

    Article  CAS  Google Scholar 

  31. 31.

    F. Han, W.-C. Li, M.-R. Li, A.-H. Lu, J. Mater. Chem., 2012, 22, 9645.

    Article  CAS  Google Scholar 

  32. 32.

    L.-Y. Jiang, X.-L. Wu, Y.-G. Guo, L.-J. Wan, J. Phys. Chem. C, 2009, 113, 14213.

    Article  CAS  Google Scholar 

  33. 33.

    X. Zhou, L.-J. Wan, Y.-G. Guo, Adv. Mater., 2013, 25, 2152.

    Article  CAS  PubMed  Google Scholar 

  34. 34.

    Z. Li, J. Ding, H. Wang, K. Cui, T. Stephenson, D. Karpuzov, D. Mitlin, Nano Energy, 2015, 15,369.

    Article  CAS  Google Scholar 

  35. 35.

    Y. Chen, B. Song, R. M. Chen, L. Lu, J. Xue, J. Mater. Chem. A, 2014, 2, 5688.

    Article  CAS  Google Scholar 

  36. 36.

    N. Yesibolati, M. Shahid, W. Chen, M. N. Hedhili, M. C. Reuter, F. M. Ross, H. N. Alshareef, Small, 2014, 10, 2849.

    Article  CAS  PubMed  Google Scholar 

  37. 37.

    C. J. Pelliccione, E. V. Timofeeva, C. U. Segre, J. Phys. Chem. C, 2016, 120, 5331.

    Article  CAS  Google Scholar 

  38. 38.

    R. Hu, D. Chen, G. Waller, Y. Ouyang, Y. Chen, B. Zhao, B. Rainwater, Ch. Yang, M. Zhu, M. Liu, Energy Environ. Sci., 2016, 9,595.

    Article  CAS  Google Scholar 

  39. 39.

    J. Y. Huang, L. Zhong, C. M. Wang, J. P. Sullivan, W. Xu, L. Q. Zhang, S. X. Mao, N. S. Hudak, X. H. Liu, A. Subramanian, H. Fan, L. Qi, A. Kushima, J. Li, Science, 2010, 330, 1515.

    Article  CAS  PubMed  Google Scholar 

  40. 40.

    C.-M. Wang, W. Xu, J. Liu, J.-G. Zhang, L. V. Saraf, B. W. Arey, D. Choi, Z.-G. Yang, J. Xiao, S. Thevuthasan, D. R. Baer, Nano Lett., 2011, 11, 1874.

    Article  CAS  PubMed  Google Scholar 

  41. 41.

    J. W. Wang, X. H. Liu, S. X. Mao, J. Y. Huang, Nano Lett., 2012, 12, 5897.

    Article  CAS  PubMed  Google Scholar 

  42. 42.

    L. F. Xiao, Y. L. Cao, J. Xiao, W. Wang, L. Kovarik, Z. M. Nie, J. Liu, Chem. Commun., 2012, 48, 3321.

    Article  CAS  Google Scholar 

  43. 43.

    M. Lao, Y. Zhang, W. Luo, Q. Yan, W. Sun, S. X. Dou, Adv. Mater., 2017, 29, 1700622.

    Article  CAS  Google Scholar 

  44. 44.

    V. L. Chevrier, G. Ceder, J. Electrochem. Soc., 2011, 158, A1011.

    Article  CAS  Google Scholar 

  45. 45.

    M. Gu, A. Kushima, Y. Shao, J.-G. Zhang, J. Liu, N. D. Browning, J. Li, C. Wang, Nano Lett., 2013, 13, 5203.

    Article  CAS  PubMed  Google Scholar 

  46. 46.

    L. D. Ellis, T. D. Hatchard, M. N. Obrovac, J. Electrochem. Soc., 2012, 159, A1801.

    Article  CAS  Google Scholar 

  47. 47.

    Z. Li, J. Ding, D. Mitlin, Acc. Chem. Res., 2015, 48, 1657.

    Article  CAS  PubMed  Google Scholar 

  48. 48.

    J. S. Chen, X. W. Lou, Small, 2013, 9, 1877.

    Article  CAS  PubMed  Google Scholar 

  49. 49.

    S. Goriparti, E. Miele, F. D. Angelis, E. D. Fabrizio, R. P. Zaccaria, C. Capiglia, J. Power Sources, 2014, 257,421.

    Article  CAS  Google Scholar 

  50. 50.

    A. K. Geim, K. S. Novoselov, Nat. Mater., 2007, 6,183.

    Article  CAS  PubMed  Google Scholar 

  51. 51.

    X. Yu, H. Cheng, M. Zhang, Y. Zhao, L. Qu, G. Shi, Nat. Rev. Mater., 2017, 2, 17046.

    Article  CAS  Google Scholar 

  52. 52.

    L. Ji, P. Meduri, V. Agubra, X. Xiao, M. Alcoutlabi, Adv. Energy Mater., 2016, 6, 1502159.

    Article  CAS  Google Scholar 

  53. 53.

    M. J. Allen, V. C. Tung, R. B. Kaner, Chem. Rev., 2010, 110,132.

    Article  CAS  PubMed  Google Scholar 

  54. 54.

    X. Cai, L. Lai, Z. Shen, J. Lin, J. Mater. Chem. A, 2017, 5, 15423.

    Article  CAS  Google Scholar 

  55. 55.

    V. Chabot, D. Higgins, A. Yu, X. Xiao, Z. Chen, J. Zhang, Energy Environ. Sci., 2014, 7, 1564.

    Article  CAS  Google Scholar 

  56. 56.

    R. K. Singh, R. Kumar, D. P. Singh, RSC Adv., 2016, 6, 64993.

    Article  CAS  Google Scholar 

  57. 57.

    B. C. Brodie, Ann. Chim. Phys., 1860, 59,466.

    Google Scholar 

  58. 58.

    L. Staudenmaier, Ber. Dtsch. Chem. Ges., 1898, 31, 1481.

    Article  CAS  Google Scholar 

  59. 59.

    S. Hummers, R. E. Offeman, J. Am. Chem. Soc., 1958, 80, 1339.

    Article  CAS  Google Scholar 

  60. 60.

    H. Yu, B. Zhang, C. Bulin, R. Li, R. Xing, Sci. Rep., 2016, 6, 36143.

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  61. 61.

    Z. Spitalsky, M. Danko, J. Mosnacek, Curr. Org. Chem., 2011, 15, 1133.

    Article  CAS  Google Scholar 

  62. 62.

    D. R. Dreyer, S. Park, C. W. Bielawski, R. S. Ruoff, Chem. Soc. Rev., 2010, 39,228.

    Article  CAS  PubMed  Google Scholar 

  63. 63.

    O. C. Compton, S. T. Nguyen, Small, 2010, 6,711.

    Article  CAS  PubMed  Google Scholar 

  64. 64.

    J. Liu, Y. Li, X. Huang, R. Ding, Y. Hu, J. Jiang, L. Liao, J. Mater. Chem., 2009, 19, 1859.

    Article  CAS  Google Scholar 

  65. 65.

    K.-C. Hsu, C.-Y. Lee, H.-T. Chiu, RSC Adv., 2014, 4, 26115.

    Article  CAS  Google Scholar 

  66. 66.

    J. Zhu, G. Zhang, S. Gu, B. Lu, Electrochim. Acta, 2014, 150,308.

    Article  CAS  Google Scholar 

  67. 67.

    Z. Wen, F. Zheng, H. Yu, Z. Jiang, K. Liu, Mater. Charact., 2013, 76,1.

    Article  CAS  Google Scholar 

  68. 68.

    D. Lei, M. Zhang, Q. Hao, L. Chen, Q. Li, E. Zhang, T. Wang, Mater. Lett., 2011, 65, 1154.

    Article  CAS  Google Scholar 

  69. 69.

    Y. Wang, J. Y. Lee, J. Phys. Chem. B, 2004, 108, 17832.

    Article  CAS  Google Scholar 

  70. 70.

    M.-S. Park, G.-X. Wang, Y.-M. Kang, D. Wexler, S.-X. Dou, H.-K. Liu, Angew. Chem., Int. Ed., 2007, 119,764.

    Article  Google Scholar 

  71. 71.

    Z. Ying, Q. Wan, H. Cao, Z. T. Song, S. L. Feng, Appl. Phys. Lett., 2005, 87, 113108.

    Article  CAS  Google Scholar 

  72. 72.

    N. H. Zhao, L. C. Yang, P. Zhang, G. J. Wang, B. Wang, B. D. Yao, Y. P. Wu, Mater. Lett., 2010, 64,972.

    Article  CAS  Google Scholar 

  73. 73.

    H. Z. Li, L. Y. Yang, J. Liu, S. T. Li, L. B. Fang, Y. K. Lu, H. R. Yang, S. L. Liu, M. Lei, J. Power Sources, 2016, 324,780.

    Article  CAS  Google Scholar 

  74. 74.

    B. H. Zhou, S. L. Yang, L. D. Wu, W. Wu, W. F. Wei, L. B. Chen, H. B. Zhang, J. Pan, X. Xiong, RSC Adv., 2015, 5, 49926.

    Article  CAS  Google Scholar 

  75. 75.

    A. Abnavi, M. S. Faramarzi, A. Abdollahi, R. Ramzani, S. Ghasemi, Z. Sanaee, Nanotechnol., 2017, 28, 255404.

    Article  CAS  Google Scholar 

  76. 76.

    S. Wang, N. Du, H. Zhang, J. X. Yu, D. R. Yang, J. Phys. Chem. C, 2011, 115, 11302.

    Article  CAS  Google Scholar 

  77. 77.

    L. M. Li, X. M. Yin, S. A. Liu, Y. G. Wang, L. B. Chen, T. H. Wang, Electrochem. Commun., 2010, 12, 1383.

    Article  CAS  Google Scholar 

  78. 78.

    W. Q. Zeng, F. P. Zheng, R. Z. Li, Y. Zhan, Y. Y. Li, J. P. Liu, Nanoscale, 2012, 4, 2760.

    Article  CAS  PubMed  Google Scholar 

  79. 79.

    W. J. Lee, M. H. Park, Y. Wang, J. Y. Lee, J. Cho, Chem. Commun., 2010, 46,622.

    Article  CAS  Google Scholar 

  80. 80.

    N. Du, H. Zhang, B. D. Chen, X. Y. Ma, X. H. Huang, J. P. Tu, D. R. Yang, Mater. Res. Bull., 44,211.

  81. 81.

    L. L. Xing, B. He, Y. X. Nie, P. Deng, C. X. Cui, X. Y. Xue, Mater. Lett., 2014, 105,169.

    Article  CAS  Google Scholar 

  82. 82.

    J. Yue, W. P. Wang, N. N. Wang, X. F. Yang, J. K. Feng, J. Yang, Y. T. Qian, J. Mater. Chem. A, 2015, 3, 23194.

    Article  CAS  Google Scholar 

  83. 83.

    L. Zhang, H. B. Wu, B. Liu, X. W. D. Lou, Energy Environ. Sci., 2014, 7, 1013.

    Article  Google Scholar 

  84. 84.

    A. Jahel, C. M. Ghimbeu, L. Monconduit, C. Vix-Guterl, Adv. Energy Mater., 2014, 4, 1400025.

    Article  CAS  Google Scholar 

  85. 85.

    L. Zhang, G. Zhang, H. B. Wu, L. Yu, X. W. D. Lou, Adv. Mater., 2013, 25, 2589.

    Article  CAS  PubMed  Google Scholar 

  86. 86.

    G. Zhou, D.-W. Wang, L. Li, N. Li, F. Li, H.-M. Cheng, Nanoscale, 2013, 5, 1576.

    Article  CAS  PubMed  Google Scholar 

  87. 87.

    J. Fan, T. Wang, C. Yu, B. Tu, Z. Jiang, D. Zhao, Adv. Mater., 2004, 16, 1432.

    Article  CAS  Google Scholar 

  88. 88.

    Z. Lu, H. Wang, CrystEngComm, 2014, 16,550.

    Article  Google Scholar 

  89. 89.

    A. Mehdinia, E. Ziaei, A. Jabbari, Electrochim. Acta, 2014, 130,512.

    Article  CAS  Google Scholar 

  90. 90.

    D. Banerjee, D. Nawn, K. Chattopadhyay, J. Alloys Compd., 2013, 572,49.

    Article  CAS  Google Scholar 

  91. 91.

    X. Liu, M. Wu, M. Li, X. Pan, J. Chen, X. Bao, J. Mater. Chem. A, 2013, 1 9527.

    Article  CAS  Google Scholar 

  92. 92.

    J. Yao, X. Shen, B. Wang, H. Liu, G. Wang, Electrochem. Commun., 2009, 11, 1849.

    Article  CAS  Google Scholar 

  93. 93.

    S.-M. Paek, E. Yoo, I. Honma, Nano Lett., 2008, 9,72.

    Article  CAS  Google Scholar 

  94. 94.

    C. Zhong, J. Wang, Z. Chen, H. Liu, J. Phys. Chem. C, 2011, 115, 25115.

    Article  CAS  Google Scholar 

  95. 95.

    J. Liang, W. Wei, D. Zhong, Q. Yang, L. Li, L. Guo, ACS Appl. Mater. Interfaces, 2012, 4,454.

    Article  CAS  PubMed  Google Scholar 

  96. 96.

    Y. Li, X. Lv, J. Lu, J. Li, J. Phys. Chem. C, 2010, 114, 21770.

    Article  CAS  Google Scholar 

  97. 97.

    S. Prabakar, Y. H. Hwang, E. G. Bae, S. Shim, D. Kim, M. S. Lah, K. S. Sohn, M. Pyo, Adv. Mater., 2013, 25, 3307.

    Article  CAS  PubMed  Google Scholar 

  98. 98.

    C. Xu, J. Sun, L. Gao, J. Mater. Chem., 2012, 22,975.

    Article  CAS  Google Scholar 

  99. 99.

    Y. Zhao, L. P. Wang, M. T. Sougrati, Z. Feng, Y. Leconte, A. Fisher, M. Srinivasan, Z. Xu, Adv. Energy Mater., 2017, 7, 1601424

    Article  CAS  Google Scholar 

  100. 100.

    R. Raccichini, A. Varzi, S. Passerini, B. Scrosati, Nat. Mater., 2015, 14,271.

    Article  CAS  PubMed  Google Scholar 

  101. 101.

    F. Ye, B. Zhao, R. Ran, Z. Shao, Chem. Eur. J., 2014, 20, 4055.

    Article  CAS  PubMed  Google Scholar 

  102. 102.

    S. Li, Y. Wang, J. Qiu, M. Ling, H. Wang, W. Martensc, S. Zhang, RSC Adv., 2014, 4, 50148.

    Article  CAS  Google Scholar 

  103. 103.

    M. Xie, X. Sun, S. M. George, C. Zhou, J. Lian, Y. Zhou, ACS Appl. Mater. Interfaces, 2015, 7, 27735.

    Article  CAS  PubMed  Google Scholar 

  104. 104.

    X. Li, X. Meng, J. Liu, D. Geng, Y. Zhang, M. N. Banis, Y. Li, J. Yang, R. Li, X. Sun, M. Cai, M. W. Verbrugge, Adv. Funct. Mater., 2012, 22, 1647.

    Article  CAS  Google Scholar 

  105. 105.

    R. Thomas, G. M. Rao, J. Mater. Chem. A, 2015, 3,274.

    Article  CAS  Google Scholar 

  106. 106.

    X. Zhou, Y. Yin, L. Wan, Y. Guo, J. Mater. Chem., 2012, 22, 17456.

    Article  CAS  Google Scholar 

  107. 107.

    S. Jiang, W. Yue, Z. Gao, Y. Ren, H. Ma, X. Zhao, Y. Liu, X. Yang, J. Mater. Sci., 2013, 48, 3870.

    Article  CAS  Google Scholar 

  108. 108.

    B. P. Vinayan, S. Ramaprabhu, J. Mater. Chem. A, 2013, 1, 3865.

    Article  CAS  Google Scholar 

  109. 109.

    X. Lu, G. Wu, Q. Xiong, H. Qin, Z. Ji, H. Pan, Appl. Surf. Sci., 2017, 422,645.

    Article  CAS  Google Scholar 

  110. 110.

    C. Botas, D. Carriazo, G. Singh, T. Rojo, J. Mater. Chem. A, 2015, 3, 13402.

    Article  CAS  Google Scholar 

  111. 111.

    G. Wu, M. Wu, D. Wang, L. Yin, J. Ye, S. Deng, Z. Zhu, W. Ye, Z. Li, Appl. Surf. Sci., 2014, 315,400.

    Article  CAS  Google Scholar 

  112. 112.

    X. J. Zhu, Y. W. Zhu, S. Murali, M. D. Stoller, R. S. Ruoff, J. Power Sources, 2011, 196, 6473.

    Article  CAS  Google Scholar 

  113. 113.

    B. Zhao, G. Zhang, J. Song, Y. Jiang, H. Zhuang, P. Liu, T. Fang, Electrochim. Acta, 2011, 56, 7340.

    Article  CAS  Google Scholar 

  114. 114.

    X. Wang, X. Cao, L. Bourgeois, H. Guan, S. Chen, Y. Zhong, D.-M. Tang, H. Li, T. Zhai, L. Li, Y. Bando, D. Golberg, Adv. Funct. Mater., 2012, 22, 2682.

    Article  CAS  Google Scholar 

  115. 115.

    L. S. Zhang, L. S. L.-Y. Jiang, H.-J. Yan, W. D. Wang, W. Wang, W.-G. Song, Y.-G. Guo, L.-J. Wan, J. Mater. Chem., 2010, 20, 5462.

    Article  CAS  Google Scholar 

  116. 116.

    X. Wang, X. Zhou, K. Yao, J. Zhang, Z. Liu, Carbon, 2011, 49,133.

    Article  CAS  Google Scholar 

  117. 117.

    W. Chen, K. Song, L. Mi, X. Feng, J. Zhang, S. Cuic, C. Liu, J. Mater. Chem. A, 2017, 5, 10027.

    Article  CAS  Google Scholar 

  118. 118.

    D. Liu, Z. Kong, X. Liu, A. Fu, Y. Wang, Y.-G. Guo, P. Guo, H. Li, X. S. Zhao, ACS Appl. Mater. Interfaces, 2018, 10, 2515.

    Article  CAS  PubMed  Google Scholar 

  119. 119.

    H.-G. Wang, C. Jiang, C. Yuan, Q. Wu, Q. Li, Q. Duan, Chem. Eng. J., 2018, 332,237.

    Article  CAS  Google Scholar 

  120. 120.

    J. Lin, Z. W. Peng, C. S. Xiang, G. D. Ruan, Z. Yan, D. Natelson, J. M. Tour, ACS Nano, 2013, 7, 6001.

    Article  CAS  PubMed  Google Scholar 

  121. 121.

    J. Yao, X. Shen, B. Wang, H. Liu, G. Wang, Electrochem. Commun., 2009, 11, 1849.

    Article  CAS  Google Scholar 

  122. 122.

    Z. Du, X. Yin, M. Zhang, Q. Hao, Y. Wang, T. Wang, Mater. Lett., 2010, 64, 2076.

    Article  CAS  Google Scholar 

  123. 123.

    J. Guo, B. Jiang, X. Zhang, H. Liu, J. Power Sources, 2014, 262,15.

    Article  CAS  Google Scholar 

  124. 124.

    M. Zhang, D. Lei, Z. Du, X. Yin, L. Chen, Q. Li, Y. Wang, T. Wang, J. Mater. Chem., 2011, 21, 1673.

    Article  CAS  Google Scholar 

  125. 125.

    D. Wang, X. Li, J. Wang, J. Yang, D. Geng, R. Li, M. Cai, T.-K. Sham, X. Sun, J. Phys. Chem. C, 2012, 116, 22149.

    Article  CAS  Google Scholar 

  126. 126.

    N. Li, H. Song, H. Cui, C. Wang, Electrochim. Acta, 2014, 130,670.

    Article  CAS  Google Scholar 

  127. 127.

    W. Zhang, M. Li, X. Z. Xiao, X. Huang, Y. Q. Jiang, X. L. Fan, L. X. Chen, J. Alloys Compd., 2017, 727,1.

    Article  CAS  Google Scholar 

  128. 128.

    C. H. Tan, J. Cao, A. M. Khattak, F. P. Cai, B. Jiang, G. Yang, S. Q. Hu, J. Power Sources, 2014, 270,28.

    Article  CAS  Google Scholar 

  129. 129.

    Y. Huang, D. Wu, S. Han, S. Li, L. Xiao, F. Zhang, X. Feng, ChemSusChem, 2013, 6, 1510.

    Article  CAS  PubMed  Google Scholar 

  130. 130.

    R. Wang, C. Xu, J. Sun, L. Gao, H. Yao, ACS Appl. Mater. Interfaces, 2014, 6, 3427.

    Article  CAS  PubMed  Google Scholar 

  131. 131.

    C. Zhang, X. Peng, Z. Guo, C. Cai, Z. Chen, D. Wexler, S. Li, H. Liu, Carbon, 2012, 50, 1897.

    Article  CAS  Google Scholar 

  132. 132.

    D. W. Su, H. J. Ahn, G. X. Wang, Chem. Commun., 2013, 49, 3131.

    Article  CAS  Google Scholar 

  133. 133.

    Y. X. Wang, Y. G. Lim, M. S. Park, S. L. Chou, J. H. Kim, H. K. Liu, S. X. Dou, Y. J. Kim, J. Mater. Chem. A, 2014, 2,529.

    Article  CAS  Google Scholar 

  134. 134.

    B. Dursun, E. Topac, R. Alibeyli, A. Ata, O. Ozturk, R. Demir-Cakan, J. Alloys Compd., 2017, 728, 1305.

    Article  CAS  Google Scholar 

  135. 135.

    J. Zhu, D. Deng, Chem. Eng. Sci., 2016, 154,54.

    Article  CAS  Google Scholar 

  136. 136.

    Y. D. Zhang, J. Xie, S. C. Zhang, P. Y. Zhu, G. S. Cao, X. B. Zhao, Electrochim. Acta, 2014, 151,8.

    Article  CAS  Google Scholar 

  137. 137.

    C.-H. Jo, J.-H. Jo, S.-T. Myung, J. Alloys Compd., 2018, 731,339.

    Article  CAS  Google Scholar 

  138. 138.

    J.-I. Lee, J. Song, Y. Cha, S. Fu, C. Zhu, X. Li, Y. Lin, M.-K. Song, Nano Res., 2017, 10, 4398.

    Article  CAS  Google Scholar 

  139. 139.

    J. Patra, H.-C. Chen, C.-H. Yang, C.-T. Hsieh, C.-Y. Su, J.-K. Chang, Nano Energy, 2016, 28,124.

    Article  CAS  Google Scholar 

  140. 140.

    J.-Y. Piquemal, E. Briot, J.-M. Bregeault, Dalton Trans., 2013, 42,29.

    Article  CAS  PubMed  Google Scholar 

  141. 141.

    M. Hibino, H. Nakajima, T. Kudo, N. Mizuno, Solid State Ionics, 1997, 100,211.

    Article  CAS  Google Scholar 

  142. 142.

    B. Pecquenard, H. Lecacheux, S. Castro-Garcia, J. Livage, J. Sol-Gel Sci. Technol., 1998, 13,923.

    Article  CAS  Google Scholar 

  143. 143.

    P. K. Biswas, N. C. Pramanik, M. K. Mahapatra, D. Ganguli, J. Livage, Mater. Lett., 2003, 57, 4429.

    Article  CAS  Google Scholar 

  144. 144.

    K. Hinokuma, K. Ogasawara, A. Kishimoto, S. Takano, T. Kudo, Solid State Ionics, 1992, 507,53.

    Google Scholar 

  145. 145.

    M. Hibino, M. Ugaji, A. Kishimoto, T. Kudo, Solid State Ionics, 1995, 79,239.

    Article  CAS  Google Scholar 

  146. 146.

    K. Lee, Y. Wang, G. Cao, J. Phys. Chem. B, 2005, 109, 16700.

    Article  CAS  PubMed  Google Scholar 

  147. 147.

    S. Takano, A. Kishimoto, K. Hinokuma, T. Kudo, Solid State Ionics, 1994, 70–71,636.

    Article  Google Scholar 

  148. 148.

    T. Ivanova, A. Harizanova, Mater. Res. Bull., 2005, 40,411.

    Article  CAS  Google Scholar 

  149. 149.

    A. A. Mikhaylov, A. G. Medvedev, D. A. Grishanov, S. Sladkevich, J. Gun, P. V. Prikhodchenko, Z. J. Xu, A. Nagasubramanian, M. Srinivasan, O. Lev, Langmuir, 2018, 34, 2741.

    Article  CAS  PubMed  Google Scholar 

  150. 150.

    A. G. DiPasquale, J. M. Mayer, J. Am. Chem. Soc., 2008, 130, 1812.

    Article  CAS  PubMed  Google Scholar 

  151. 151.

    E. G. Ippolitov, T. A. Tripol´skaya, P. V. Prikhodchenko, D. A. Pankratov, Russ. J. Inorg. Chem., 2001, 46,851.

    Google Scholar 

  152. 152.

    A. V. Churakov, P. V. Prikhodchenko, E. G. Ippolitov, M. Y. Antipin, Russ. J. Inorg. Chem., 2002, 47,68.

    Google Scholar 

  153. 153.

    P. V. Prikhodchenko, A. V. Churakov, B. N. Novgorodov, D. I. Kochubei, Yu. B. Muravlev, E. G. Ippolitov, Russ. J. Inorg. Chem., 2003, 48,16.

    Google Scholar 

  154. 154.

    A. V. Churakov, S. Sladkevich, O. Lev, T. A. Tripol´skaya, P. V. Prikhodchenko, Inorg. Chem., 2010, 49, 4762.

    Article  CAS  PubMed  Google Scholar 

  155. 155.

    S. Sladkevich, V. Gutkin, O. Lev, E. A. Legurova, D. F. Khabibulin, M. A. Fedotov, V. Uvarov, T. A. Tripol´skaya, P. V. Prikhodchenko, J. Sol-Gel Sci. Technol., 2009, 50,229.

    Article  CAS  Google Scholar 

  156. 156.

    E. A. Legurova, S. Sladkevich, O. Lev, M. A. Fedotov, D. F. Khabibulin, T. A. Tripol´skaya, P. V. Prikhodchenko, Russ. J. Inorg. Chem., 2009, 54,824.

    Article  Google Scholar 

  157. 157.

    P. V. Prikhodchenko, V. I. Privalov, T. A. Tripol´skaya, E. G. Ippolitov, Russ. J. Inorg. Chem., 2001, 46, 1881.

    Google Scholar 

  158. 158.

    P. V. Prikhodchenko, E. A. Ustinova, M. A. Fedotov, E. G. Ippolitov, Russ. J. Inorg. Chem., 2004, 49, 1562.

    Google Scholar 

  159. 159.

    A. A. Mikhaylov, A. G. Mevdedev, T. A. Tripol´skaya, V. S. Popov, A. S. Mokrushin, D. P. Krut´ko, P. V. Prikhodchenko, O. Lev, Dalton Trans., 2017, 46, 16171.

    Article  CAS  PubMed  Google Scholar 

  160. 160.

    A. G. Medvedev, A. A. Mikhaylov, A. V. Churakov, M. V. Vener, T. A. Tripol´skaya, S. Cohen, O. Lev, P. V. Prikhodchenko, Inorg. Chem., 2015, 54, 8058.

    Article  CAS  PubMed  Google Scholar 

  161. 161.

    A. A. Mikhaylov, A. G. Medvedev, A. V. Churakov, D. A. Grishanov, P. V. Prikhodchenko, O. Lev, Chem. Eur. J., 2016, 22, 2980.

    Article  CAS  PubMed  Google Scholar 

  162. 162.

    S. Sladkevich, A. A. Mikhaylov, P. V. Prikhodchenko, T. A. Tripol´skaya, O. Lev, Inorg. Chem., 2010, 49, 9110.

    Article  CAS  PubMed  Google Scholar 

  163. 163.

    M. V. Vener, A. G. Medvedev, A. V. Churakov, P. V. Prikhodchenko, T. A. Tripol´skaya, O. Lev, J. Phys. Chem. A, 2011, 115, 13657.

    Article  CAS  PubMed  Google Scholar 

  164. 164.

    I. Yu. Chernyshov, M. V. Vener, P. V. Prikhodchenko, A. G. Medvedev, O. Lev, A. V. Churakov, Crystal Growth Des., 2017, 17,214.

    Article  CAS  Google Scholar 

  165. 165.

    A. G. Medvedev, A. V. Shishkina, O. Lev, P. V. Prikhodchenko, M. V. Vener, RSC Adv., 2015, 5, 29601.

    Article  CAS  Google Scholar 

  166. 166.

    S. Sladkevich, J. Gun, P. V. Prikhodchenko, V. Gutkin, A. A. Mikhaylov, V. M. Novotortsev, J. X. Zhu, D. Yang, Q. Y. Yan, H. H. Hng, Y. Y. Tay, Z. Tsakadze, O. Lev, Nanotechnology, 2012, 23, 485601.

    Article  PubMed  Google Scholar 

  167. 167.

    A. A. Mikhaylov, A. G. Medvedev, C. W. Mason, A. Nagasubramanian, S. Madhavi, S. K. Batabyal, Q. Zhang, J. Gun, P. V. Prikhodchenko, O. Lev, J. Mater. Chem. A, 2015, 3, 20681.

    Article  CAS  Google Scholar 

  168. 168.

    A. A. Mikhaylov, A. G. Medvedev, T. A. Tripol´skaya, E. A. Mel´nik, I. V. Shabalova, P. V. Prikhodchenko, O. Lev, Russ. J. Inorg. Chem., 2016, 61, 1430.

    Article  CAS  Google Scholar 

  169. 169.

    P. V. Prikhodchenko, D. Y. W. Yu, S. K. Batabyal, V. Uvarov, J. Gun, S. Sladkevich, A. A. Mikhaylov, A. G. Medvedev, O. Lev, J. Mater. Chem. A, 2014, 2, 8431.

    Article  CAS  Google Scholar 

  170. 170.

    V. Lakshmi, Y. Chen, A. A. Mikhaylov, A. G. Medvedev, I. Sultana, M. M. Rahman, O. Lev, P. V. Prikhodchenko, A. M. Glushenkov, Chem. Commun., 2017, 53, 8272.

    Article  CAS  Google Scholar 

  171. 171.

    A. G. Medvedev, A. A. Mikhaylov, D. A. Grishanov, D. Y. W. Yu, J. Gun, S. Sladkevich, O. Lev, P. V. Prikhodchenko, ACS Appl. Mater. Interfaces, 2017, 9, 9152.

    Article  CAS  PubMed  Google Scholar 

  172. 172.

    A. A. Mikhaylov, A. G. Medvedev, D. A. Grishanov, T. A. Tripol´skaya, E. A. Mel´nik, P. V. Prikhodchenko, O. Lev, Russ. J. Inorg. Chem., 2017, 62, 1624.

    Article  CAS  Google Scholar 

  173. 173.

    D. Y. W. Yu, S. K. Batabyal, J. Gun, S. Sladkevich, A. A. Mikhaylov, A. G. Medvedev, V. M. Novotortsev, O. Lev, P. V. Prikhodchenko, Main Group Met. Chem., 2015, 38,43.

    Article  CAS  Google Scholar 

  174. 174.

    S. Sladkevich, J. Gun, P. V. Prikhodchenko, V. Gutkin, A. A. Mikhaylov, A. G. Medvedev, T. A. Tripol´skaya, O. Lev, Carbon, 2012, 50, 5463.

    Article  CAS  Google Scholar 

  175. 175.

    P. V. Prikhodchenko, J. Gun, S. Sladkevich, A. A. Mikhaylov, O. Lev, Y. Y. Tay, S. K. Batabyal, D. Y. W. Yu, Chem. Mater., 2012, 24, 4750.

    Article  CAS  Google Scholar 

  176. 176.

    D. Y. W. Yu, P. V. Prikhodchenko, C. W. Mason, S. K. Batabyal, J. Gun, S. Sladkevich, A. G. Medvedev, O. Lev, Nat. Commun., 2013, 4, 2922.

    Article  CAS  PubMed  Google Scholar 

  177. 177.

    D. A. Grishanov, A. A. Mikhaylov, A. G. Medvedev, J. Gun, P. V. Prikhodchenko, A. Nagasubramanian, S. Madhavi, O. Lev, Energy Technol., 2017, 6,127.

    Article  CAS  Google Scholar 

  178. 178.

    D. A. Grishanov, A. A. Mikhaylov, A. G. Medvedev, J. Gun, A. Nagasubramanian, S. Madhavi, O. Lev, P. V. Prikhodchenko, J. Colloid Interface Sci., 2018, 512, 165.

    Article  CAS  PubMed  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to P. V. Prikhodchenko.

Additional information

Based on the materials of the XXVII International Chugaev Conference on Coordination Chemistry (October 2–6, 2017; Nizhny Novgorod, Russia).

Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 7, pp. 1131–1141, July, 2018.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Medvedev, A.G., Mikhaylov, A.A., Tripol´skaya, T.A. et al. Graphene oxide supported tin dioxide: synthetic approaches and electrochemical characterization as anodes for lithium- and sodium-ion batteries. Russ Chem Bull 67, 1131–1141 (2018). https://doi.org/10.1007/s11172-018-2194-4

Download citation

Key words

  • tin dioxide
  • anode material
  • composite material
  • lithium-ion battery
  • sodium-ion battery
  • hydrothermal method
  • peroxide method