Physicochemical analysis results for alloys in the Al–Ti–Pt system at 0–50 at.% Pt that were cast and annealed at subsolidus temperatures are used to construct for the first time vertical sections at 7, 25, and 35 ± 1 at. Pt of this system taking into account the constitution of its melting diagram. The congruent crystallization of τ3, τ 4, and τ8 compounds and incongruent crystallization of τ2 and τ5 compounds are confirmed. Changes from incongruent to congruent crystallization of the solid solutions based on binary Al3Pt2, Al2Pt, and TiAl phases in transition to the ternary system are shown.
Similar content being viewed by others
References
O.V. Zaikina, V.G. Khorujaya, D.V. Pavlyuchkov, B. Grushko, and T. Ya. Velikanova, “Investigation of the Al–Ti–Pt alloy system at 1100°C,” J. Alloys Compd., 509, No. 28, 7565–7571 (2011), doi: https://doi.org/10.1016/j.jallcom.2011.04.115.
O.V. Zaikina, V.G. Khoruzha, K.E. Kornienko, and T. Ya. Velikanova “Phase equilibria in the aluminum corner of the Al–Ti–Pt system,” Powder Metall. Met. Ceram., 57, No. 1–2, 114–126 (2018).
O.V. Zaikina, V.G. Khoruzhaya, K. Ye. Korniyenko, K. A. Meleshevich, D.V. Pavlyuchkov, and T. Ya. Velikanova, “Phase equilibria in the ternary Al–Ti–Pt system. I. Solidus surface of the Al–Ti–Pt system in the range 0–50 at.% Pt,” Powder Metall. Met. Ceram., 57, No. 9–10, 587–595 (2018).
O.V. Zaikina, V.G. Khoruzhaya, K. Ye. Korniyenko, D.V. Pavlyuchkov, K.A. Meleshevich, and T. Ya. Velikanova, “Phase equilibria in the ternary Al–Ti–Pt system. II. Liquidus surface of the Al–Ti–Pt system in the composition range 0–50 at.% Pt,” Powder Metall. Met. Ceram., 57, No. 11–12, 709–715 (2018).
O.V. Zaikina, V.G. Khoruzhaya, K. Ye. Kornienko, and T. Ya. Velikanova, “Phase equilibria in the ternary Al–Ti–Pt system. III. The Al–Ti–Pt melting diagram in the composition range 0–50 at.% Pt,” Powder Metall. Met. Ceram., 58, No. 1–2, 81–88 (2019).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Poroshkova Metallurgiya, Vol. 58, Nos. 5–6 (527), pp. 98–104, 2019.
Rights and permissions
About this article
Cite this article
Khoruzhaya, V.G., Korniyenko, K.Y. Phase Equilibria in the Ternary Al–Ti–Pt System. IV. Vertical Sections in the Ternary Al–Ti–Pt System in the Composition Range 0–50 at.% Pt. Powder Metall Met Ceram 58, 323–328 (2019). https://doi.org/10.1007/s11106-019-00081-0
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11106-019-00081-0