Phase equilibria during solidification of alloys in the Al2O3–HfO2–Er2O3 system are studied, and liquidus and solidus surfaces of the Al2O3–HfO2–Er2O3 phase diagram are constructed for the first time. It is established that interaction in the system is eutectic. No ternary compounds or appreciable regions of solid solutions based on components or binary compounds are found in the ternary system.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
S. M. Lakiza, Ya. S. Tishchenko, V. P. Red’ko, and L. M. Lopato, “Isothermal sections of the Al2O3–HfO2–Er2O3 phase diagram at 1250 and 1600°C,” Powder Metall. Met. Ceram., 51, No. 9–10, 594–601 (2012).
Yu. A. Kocherzhinskii, E. A. Shishkin, and V. I. Vasilenko, “DTA apparatus with a temperature sensor to 2200°C,” in: Phase Diagrams of Metal Systems [in Russian], Nauka, Moscow (1971), pp. 245–249.
P. Wu and A. D. Pelton, “Coupled thermodynamic―phase diagram assessment of the rare earth oxide―aluminum oxide binary systems,” J. Alloys Compd., 179, 259–287 (1992).
A. V. Shevchenko, L. M. Lopaton, and E. I. Kiryakova, “Interaction of HfO2 with Y2O3, Ho2O3, Er2O3, Tm2O3, Yb2O3, and Lu2O3 at high temperatures,” Izv. Akad. Nauk SSSR. Neorg. Mater., 20, No. 12, 1991–1996 (1984).
Acknowledgements
The authors thank Z. O. Zaitseva and V. P. Red’ko for participation in petrographic analysis and X-ray diffraction, respectively.
Author information
Authors and Affiliations
Corresponding author
Additional information
L. M. Lopato (Deceased.)
Translated from Poroshkovaya Metallurgiya, Vol. 52, No. 1–2 (489), pp. 115–128, 2013.
Rights and permissions
About this article
Cite this article
Tishchenko, Y.S., Lakiza, S.M., Lopato, L.M. et al. Solidus and liquidus surfaces of the Al2O3–HfO2–Er2O3 phase diagram. Powder Metall Met Ceram 52, 90–101 (2013). https://doi.org/10.1007/s11106-013-9499-5
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11106-013-9499-5