The heat capacity and enthalpy of lutetium monosiliсide are measured for the first time in the temperature ranges 68.56–298.21 and 465–2191 K, respectively. The standard values and temperature dependences of the heat capacity, entropy, Gibbs energy, and enthalpy of the silicide are calculated in a wide temperature range. The temperature, enthalpy, and entropy of melting are determined.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
G. V. Samsonov, L. A. Dvorina, and B. M. Rud’, Silicides [in Russian], Metallurgiya, Moscow (1979), p. 272.
Silicides: Fundamentals and Applications, Proc. 16th Course Int. School Solid State Physics (June 5–16, 1999, Erice, Italy), World Scientific, Singapore (2000), p. 377.
Yu. I. Buyanov, T. Ya. Velikanova, S. P. Luzan, et al., Interaction of Rare-Earth Metals with Silicon [in Russian], Preprint No. 97-5, Inst. Probl. Materialoved., NAN Ukrainy, Kiev (1997), p. 95.
S. V. Meeshel and O. J. Kleppa, “Standard enthalpies of formation of some lutetium alloys by high-temperature direct synthesis calorimetry,” J. All. Compd., 224, No. 2, 343–350 (1995).
S. V. Meeshel, O. J. Kleppa, “Redetermination of the standard enthalpy of formation of Lu5Ge3 by high temperature direct synthesis calorimetry,” J. All. Compd., 245, L28–L29 (1996).
A. K. Niessen, F. R. de Boer, R. Boom, et al., “Model predictions for the enthalpy of formation of transition metal alloys. II,” Calphad, 7, No. 1, 51 (1983).
E. I. Gladyshevskii, Crystal Chemistry of Silicides and Germanides [in Russian], Metallurgiya, Moscow (1971), p. 296.
A. S. Bolgar, A. I. Kriklya, A. P. Suodis, and A. V. Blinder, “Low-temperature heat capacity of praseodymium, neodymium, and samarium sesquicarbides,” Zh. Fiz. Khim., 72, No. 4, 439–443 (1998).
A. S. Bolgar, N. P. Gorbachuk, and A. V. Blinder, “Enthalpies of Gd5Si3, Gd5Si4, GdSi, and GdSi1.88 in the temperature range 298.15–2200 K. Melting enthalpies,” Teplofiz. Vys. Temp., 34, No. 4, 541–545 (1996).
N. P. Gorbachuk and A. S. Bolgar, “The enthalpies of DySi2 and HoSi1.67 at 298.15–2007 K. Phase transformation enthalpies,” Powder Metall. Met. Ceram., 41, No. 3–4, 173–176 (2002).
V. F. Litvinenko, A. S. Bolgar, V. B. Muratov, et al., Processing of Experimental Data on Enthalpy Considering Additional Conditions [in Russian], Dep. VINITI No. 6300-V, September 19, 1984, Inst. Probl. Materialoved. AN USSR, Kiev (1984), p. 15.
N. P. Gorbachuk, A. S. Bolgar, and A. V. Blinder, Thermodynamic Properties of Silicides [in Russian], Preprint No. 95-10, Inst. Probl. Materialoved., Kiev (1995), p. 40.
N. P. Gorbachuk, S. N. Kirienko, V. R. Sidorko, and I. M. Obushenko, “Thermodynamic properties of erbium mono- and disilicide at low temperatures,” Powder Metall. Met. Ceram., 46, No. 1–2, 72–76 (2007).
N. P. Gorbachuk, S. N. Kirienko, V. R. Sidorko, and I. M. Obushenko, “Enthalpy of ErSi and ErSi1.67 in the temperature range 400–2300 K,” Teplofiz. Vys. Temp., 45, No. 2, 203–207 (2007).
V. R. Sidorko, R. V. Antonchenko, and I. M. Obushenko, “Thermodynamic properties of erbium silicides,” in: Proc. Int. Conf. Modern Materials Science: Advances and Challenges [in Russian], (September 26–30, 2005), Kiev (2005), pp. 117–118.
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Poroshkovaya Metallurgiya, Vol. 51, No. 3–4 (484), pp. 125–130, 2012.
Rights and permissions
About this article
Cite this article
Gorbachuk, N.P., Kirienko, S.N., Sidorko, V.R. et al. Low-temperature heat capacity and high-temperature enthalpy of LuSi. Powder Metall Met Ceram 51, 229–233 (2012). https://doi.org/10.1007/s11106-012-9422-5
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11106-012-9422-5