Liquid metals represent an aggressive environment where selective degradation can attack structural alloys. Pre-oxidizing structural alloys, particularly those able to form alumina scales, have shown promise for Sn, Pb and Pb–Li concepts for fusion and fission applications. For Pb at 700 °C, a dramatic reduction in mass loss was observed for an alumina-forming austenitic (AFA) steel after pre-oxidation. Likewise, a ferritic FeCrAlMo alloy showed better compatibility in static Sn at 400–500 °C and flowing PbLi when pre-oxidized at 1000 °C to form α-Al2O3. Recent experiments with flowing PbLi at 675–700 °C has shown significant degradation suggesting that alumina-forming alloys are limited to ~ 650 °C in this environment. While the concept is promising, most experiments have been relatively short-term and long-term degradation mechanisms need to be evaluated.
This is a preview of subscription content, access via your institution.
Buy single article
Instant access to the full article PDF.
Tax calculation will be finalised during checkout.
Subscribe to journal
Immediate online access to all issues from 2019. Subscription will auto renew annually.
Tax calculation will be finalised during checkout.
S. Malang and R. Mattas, Fusion Engineering & Design. 27, 399 (1995).
R. G. Ballinger and J. Lim, Nuclear Technology. 147, 418 (2004).
D. Frazer, E. Stergar, C. Cionea, P. Hosemann, Energy Procedia. 49, 627 (2014).
D. C. Vreeland, E. E. Hoffman and W. D. Manly, Nucleonics 11 (11), 36 (1953).
J. H. DeVan, Journal of Nuclear Materials. 85-86, 249 (1979).
P. F. Tortorelli, Journal of Nuclear Materials. 191-194, 965 (1992).
J. Konys, W. Krauss, Z. Voss and O. Wedemeyer, Journal of Nuclear Materials. 367-370, 1144 (2007).
B. A. Pint, L. R. Walker and K. A. Unocic, Materials at High Temperature. 29, 129 (2012).
J. Ejenstam, P. Szakalos, Journal of Nuclear Materials. 461, 164 (2015).
K. A. Unocic and B. A. Pint, Journal of Nuclear Materials. 455, 330 (2014).
S. J. Pawel, Fusion Science and Technology. 61:1T, 369 (2012).
S. J. Pawel and K. A. Unocic, Journal of Nuclear Materials. 492, 41 (2017).
J. Jun, K. A. Unocic, M. J. Lance, H. M. Meyer and B. A. Pint, Journal of Nuclear Materials. 528, 151847 (2020).
J. R. Weeks, Nuclear Engineering Design. 15, 363 (1971).
Y. Yamamoto, M. P. Brady, Z. P. Lu, P. J. Maziasz, C. T. Liu, B. A. Pint, K. L. More, H. M. Meyer and E. A. Payzant, Science. 316, 433-436 (2007).
Y. Yamamoto, M. L. Santella, C. T. Liu, N. D. Evans, P. J. Maziasz and M. P. Brady, Materials Science and Engineering A, 524, 176 (2009).
M. P. Brady, J. Magee, Y. Yamamoto, D. Helmick, L. Wang, Materials Science and Engineering A. 590, 101 (2014).
Y. Yamamoto, B. A. Pint, K. A. Terrani, K. G. Field, Y. Yang and L.L. Snead, Journal of Nuclear Materials. 467, 703 (2015).
A. Weisenburger, A. Jianu, S. Doyle, M. Bruns, R. Fetzer, A. Heinzel, M. DelGiacco, W. An, G. Müller, Journal of Nuclear Materials. 437, 282 (2013).
B. A. Pint, Y.-F. Su, J. Jun, M. P. Brady, Y. Yamamoto and M. R. Ickes, ORNL report TM-2021/2025, Oak Ridge, TN (2021).
O. K. Chopra, P. F. Tortorelli, Journal of Nuclear Materials. 123, 1201 (1984).
M. Kondo, M. Ishii and T. Muroga, Fusion Engineering and Design. 98–99, 2003 (2015).
S. J. Zinkle and N. M. Ghoniem, Fusion Engineering and Design. 51-52, 55 (2000).
H. Sakasegawa, H. Tanigawa, S. Kano, H. Abe, Fusion Engineering and Design. 98-99, 2068 (2015).
B. A. Pint and K. L. More, Journal of Nuclear Materials. 376, 108 (2008).
M. Kondo, B. A. Pint, J. Jun, N. Russell, J. McDuffee, M. Akiyoshi, T. Tanaka, N. Oono, J. Miyazawa, J. W. Geringer, Y. Kato, Y. Hatano, Plasma and Fusion Research, 16 2405040 (2021).
R. J. Lauf and J. H. DeVan, Journal of the Electrochemical Society. 139, 2087 (1992).
B. A. Pint, P. F. Tortorelli, A. Jankowski, J. Hayes, T. Muroga, A. Suzuki, O. I. Yeliseyeva and V. M. Chernov, Journal of Nuclear Materials. 329-333, 119 (2004).
P. Hubberstey, Journal of Nuclear Materials. 247, 208 (1997).
M. Abdou, D. Sze, C. Wong, M. Sawan, A. Ying, N. B. Morley and S. Malang, Fusion Science & Technology. 47, 475 (2005).
P. Hubberstey, T. Sample and A. Terlain, Fusion Technology. 28, 1194 (1995).
B. A. Pint, S. Dryepondt, K. A. Unocic and D. T. Hoelzer, JOM. 66, 2458 (2014).
W. Krauss, J. Konys, S.-E. Wulf, Journal of Nuclear Materials. 455, 522 (2014).
S.-E. Wulf, W. Krauss, J. Konys, Nuclear Materials and Energy. 16, 158 (2018).
B. A. Pint, J. Jun and M. Romedenne, Fusion Engineering and Design. 166, 112389 (2021).
B. A. Pint, J. Jun, E. Cakmak, D. J. Sprouster, N. Olynik and L. L. Snead, “Compatibility of FeCrAlMo in Flowing Pb-Li at 600°-700°C,” Fusion Science and Technology. in press (2021).
S. A. Briggs, P. D. Edmondson, K. C. Littrell, Y. Yamamoto, R. H. Howard, C. R. Daily, K. A. Terrani, K. Sridharan, K. G. Field, Acta Materialia. 129, 217 (2017).
This research was funded by the U.S. Department of Energy, Office of Fusion Energy Sciences and Office of Nuclear Energy, GAIN program. The experimental work at ORNL was assisted by A. Willoughby, M. Stephens, T. Lowe and V. Cox. This manuscript has been authored by UT-Battelle, LLC under Contract No. DE-AC05-00OR22725 with the U.S. Department of Energy. The United States Government retains and the publisher, by accepting the article for publication, acknowledges that the United States Government retains a non-exclusive, paid-up, irrevocable, world-wide license to publish or reproduce the published form of this manuscript, or allow others to do so, for United States Government purposes. The Department of Energy will provide public access to these results of federally sponsored research in accordance with the DOE Public Access Plan (http://energy.gov/downloads/doe-public-access-plan).
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Pint, B.A., Jun, J. Pre-Oxidation to Improve Liquid Metal Compatibility. Oxid Met 96, 231–240 (2021). https://doi.org/10.1007/s11085-021-10057-4
- Fusion energy
- Nuclear energy
- Liquid metal compatibility