Corrosion Behavior of Cr-Containing Alloys under Cyclic Reaction in Wet CO2 Gas at 650°C

Abstract

The corrosion behavior of seven commercial alloys (602CA, 310SS, 253MA, 800H, F321, F316L, 304SS) was investigated in a wet CO2 gas under cyclic reactions up to 150 cycles at 650°C. Water vapor accelerated the oxidation of all alloys. Alloy 602CA was alumina-forming in dry CO2 but changed to chromia-forming in the wet gas. In wet gas, the 310SS and 253MA underwent breakaway oxidation which was enhanced by the cyclic reaction. Spallation and buckling of the outer iron oxide scale were considerable for the less-protective alloys, 800H, F321, F316L and 304SS, with the formation of reddish iron oxide whiskers on the scale surface. The carburisation of F321, F316L and 304SS was identified and found to be reduced significantly by the presence of water vapor. The effect of water vapor on oxidation, carburisation, oxide buckling and whisker formation is discussed in comparison with that in dry gas.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10

References

  1. 1.

    Buhre, B.J.P., et al., Progress in Energy and Combustion Science, 2005. 31: p. 283.

  2. 2.

    Powell, C.A. and B.D. Morreale, MRS Bulletin, 2008. 33: p. 309.

  3. 3.

    Viswanathan, R., J. Sarver, and J.M. Tanzosh, Journal of Materials Engineering and Performance, 2006. 15: p. 255.

  4. 4.

    Xi, X., C. Kong, and J. Zhang, Oxidation of Metals, 2019.

  5. 5.

    Wagner, C., Zeitschrift für Elektrochemie, 1959. 63: p. 772.

  6. 6.

    Airiskallio, E., et al., Corrosion Science, 2010. 52: p. 3394.

  7. 7.

    Prillieux, A., et al., Oxidation of Metals, 2017. 87: p. 273.

  8. 8.

    Xie, Y., J. Zhang, and D.J. Young, Corrosion Science, 2018. 136: p. 311.

  9. 9.

    Wagner, C., Journal of the Electrochemical Society, 1952. 99: p. 369.

  10. 10.

    Olszewski, T., Vol. 159. 2012: Forschungszentrum Jülich.

  11. 11.

    Yuan, J., et al., Corrosion Science, 2016. 109: p. 36.

  12. 12.

    Ehlers, J., et al., Corrosion science, 2006. 48: p. 3428.

  13. 13.

    Hänsel, M., W.J. Quadakkers, and D.J. Young, Oxidation of Metals, 2003. 59: p. 285.

  14. 14.

    Nguyen, T.D., J. Zhang, and D. Young, Corrosion Science, 2015. 83.

  15. 15.

    Tollman, R.L. and E.A. Gulbransen, Journal of The Electrochemical Society, 1968. 115: p. 770.

  16. 16.

    Raynaud, G.M. and R.A. Rapp, Oxidation of Metals, 1984. 21: p. 89.

  17. 17.

    Yuan, L., et al., Acta Materialia, 2011. 59: p. 2491.

  18. 18.

    Anghel, C., et al., Applied Surface Science, 2004. 233: p. 392.

Download references

Acknowledgements

The authors would like to thank Australian Research Council for financial support of this project under the Discovery project scheme.

Author information

Affiliations

Authors

Corresponding author

Correspondence to Jianqiang Zhang.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Xi, X., Zhang, J. & Young, D.J. Corrosion Behavior of Cr-Containing Alloys under Cyclic Reaction in Wet CO2 Gas at 650°C. Oxid Met 96, 105–116 (2021). https://doi.org/10.1007/s11085-021-10054-7

Download citation

Keywords

  • Austenitic alloys
  • Cyclic reaction
  • Wet CO2
  • High-temperature corrosion